Preparation method of ni/nio/c composite material, and supercapacitor

A technology of composite materials and mixtures, which is applied in the manufacture of hybrid capacitor electrodes, hybrid/electric double layer capacitors, etc., can solve the problems of material deformation and weak conductivity of transition metal oxide materials, so as to improve conductivity and not require high equipment , the effect of improving the diffusion efficiency

Active Publication Date: 2021-08-31
HUBEI UNIV OF ARTS & SCI
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main purpose of the present invention is to propose a preparation method of Ni / NiO / C composite material and supercapacitor, aiming to solve the problem of weak conductivity of transition metal oxide material and material deformation during charging and discharging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ni/nio/c composite material, and supercapacitor
  • Preparation method of ni/nio/c composite material, and supercapacitor
  • Preparation method of ni/nio/c composite material, and supercapacitor

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] In view of this, the present invention proposes a method for preparing a Ni / NiO / C composite material, which can prepare a Ni / NiO / C composite material with good electrical conductivity and ease the volume change during charging and discharging. combine figure 1 The schematic flow sheet of an embodiment of the preparation method of proposed Ni / NiO / C composite material, the preparation method of described Ni / NiO / C composite material comprises the following steps:

[0039] Step S10, making the biomass raw material into biomass powder.

[0040] Specifically, the biomass is washed, dried, pulverized, and sieved to obtain biomass powder. Wherein, the drying temperature is 80-100° C., and the drying time is 10-12 hours; the sieving is 200-300 mesh sieves. In this embodiment, the biomass raw material is any one of waste biomass materials such as corncobs, peanut shells, straws, leaves, lotus pod shells, etc. The nutrient channels of these biomass raw materials are beneficial t...

Embodiment 1

[0057] Wash the corn cobs, dry them, crush them, and pass through a 300-mesh sieve to obtain corn cob powders; take 1 g of corn cob powders and immerse them in 8 mL of nickel chloride aqueous solution (molar concentration is 0.1 mol / L), soak for 72 hours, and then soak them at 120 Dry at ℃ for 4 hours; mix the dried corn cob powder with LiCl-KCl mixed salt (the molar fraction of LiCl is 0.58) (the mass ratio of corn cob powder and LiCl-KCl is 1:4) to obtain a mixture; Then put the mixture into N 2 In a tube furnace under the atmosphere, heat to 400°C, hold for 2 hours, heat to 650°C, hold for 5 minutes, cool to room temperature to obtain product A; wash product A with water at 60°C, pickle, wash with water, and dry to obtain The specific surface area is 1182m 2 / g and resistivity 3.1×10 -4 Ω.m Ni / NiO / C composite material.

Embodiment 2

[0059] Wash the rice straw, dry it, crush it, and pass it through a 200-mesh sieve to obtain the rice straw powder; take 1g of the rice straw powder and immerse it in 7mL of nickel chloride aqueous solution (molar concentration is 0.26mol / L), soak it for 24h, and then put it in 100 Dry at ℃ for 5 hours; mix the dried rice straw powder with LiCl-KCl mixed salt (the molar fraction of LiCl is 0.65) (the mass ratio of rice straw powder to LiCl-KCl is 1:3) to obtain a mixture; Then put the mixture into N 2 In a tube furnace under atmosphere, heat to 450°C, keep it warm for 1h, then heat to 510°C, keep it for 25min, cool to room temperature, and get product A; wash product A with water at 80°C, pickle, wash with water, and dry to get The specific surface area is 652m 2 / g and resistivity 2.4×10 -3 Ω.m Ni / NiO / C composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a Ni / NiO / C composite material and a supercapacitor. The method for preparing the Ni / NiO / C composite material includes the following steps: making biomass raw materials into biomass powder; The body is immersed in the nickel ion solution, so that the biomass powder absorbs nickel ions, and then the biomass powder adsorbed with nickel ions is dried; the dried biomass powder is uniformly mixed with an inorganic salt to obtain a mixture; the mixture is placed in N 2 Heating to T1 under the atmosphere to melt the inorganic salt in the mixture, keeping it warm for 1-2 hours, then heating to 500-650°C, keeping it warm for 5-30 minutes, cooling to room temperature to obtain product A; washing product A with water at 60-100°C, and then Pickling, washing and drying to obtain Ni / NiO / C composite material. The Ni / NiO / C composite material prepared by the present invention has good electrical conductivity, and using it as an electrode material for a supercapacitor alleviates the stability problem caused by the volume change in the charging and discharging process of NiO, and improves the electrochemical performance of the supercapacitor. performance, good cycle stability and long cycle life.

Description

technical field [0001] The invention relates to the technical field of supercapacitor electrode materials, in particular to a method for preparing a Ni / NiO / C composite material and a supercapacitor. Background technique [0002] Along with a large amount of portable equipments, as portable computer, mobile phone, walkman etc., popularize in daily life. The performance requirements of portable batteries are getting higher and higher. As an energy storage device that can store or release energy, supercapacitors are more and more popular because of their high energy density and power, good reversibility, no pollution to the environment, fast charge and discharge speed, and long cycle life. focus on. For supercapacitors, the quality of electrode materials is a key factor in determining the performance of supercapacitors. [0003] At present, the common supercapacitor electrode material is a transition metal oxide material, and the transition metal oxide is a pseudocapacitive ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/42H01G11/44H01G11/46H01G11/86
CPCH01G11/42H01G11/44H01G11/46H01G11/86Y02E60/13
Inventor 肖作安袁晓庆余洪洋高星圆朱雨晴占丹蔡爽戴高鹏刘素芹胡学步
Owner HUBEI UNIV OF ARTS & SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap