Glass suitable for UV curing process and preparation method thereof

A curing process and glass technology, applied in glass manufacturing equipment, glass furnace equipment, glass production, etc., can solve the problems of glass yellowing and transmittance, etc.

Active Publication Date: 2020-09-22
深圳南玻科技有限公司 +3
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a glass suitable for UV curing process and its preparation method, aiming to solve the problems of yellowing and lower transmittance of existing glass after UV curing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass suitable for UV curing process and preparation method thereof
  • Glass suitable for UV curing process and preparation method thereof
  • Glass suitable for UV curing process and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment

[0060] In Table 1, Table 2, and Table 3, commonly used glass raw materials such as oxides and carbonates, etc. are appropriately selected to have the composition shown in the table, and weighed to obtain 150 g of the batch mixture; then, the Put the batch mixture into a platinum crucible, put the platinum crucible into a silicon-molybdenum furnace, raise the temperature to 1650°C, and melt it for 3 hours, homogenize it and cast it into a mold, keep it at 620°C for 1 hour and anneal, then follow Cool the furnace to obtain block glass; process the block glass to obtain several pieces of thin glass with a size of 50mm×50mm×0.7mm and polished upper and lower surfaces.

[0061] like figure 2 and image 3 As shown, metal halide lamps are used to irradiate the glass sample 20 twice, each time for 5 s, half of the glass sample 20 is covered with an optical filter 10 during irradiation, and the energy in the direct area of ​​each irradiation is 2800mj / cm 2 , the total energy of two...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses glass suitable for a UV curing process and a preparation method thereof. The glass comprises the following components in percentage by mass: 58%-66% of SiO2, 15%-20% of Al2O3,3%-8% of Li2O, 7%-12% of Na2O, 0%-2% of K2O, 0%-3% of MgO, 0%-3% of B2O3, 1%-5% of ZrO2, 0.01%-0.05% of CeO2 and 0.01%-2% of SnO2. The glass provided by the invention has strong anti-irradiation capability, is not easy to discolor even if the single irradiation energy is improved in the UV curing process of the glass, and the transmittance is not reduced basically, so that the irradiation frequency can be reduced, and the production efficiency is improved; and a light filtering device is additionally arranged on the glass in the UV curing process, so that the influence on the color differenceof the glass after multiple times of irradiation is small.

Description

technical field [0001] The invention relates to the technical field of glass manufacturing, in particular to a glass suitable for UV curing technology and a preparation method thereof. Background technique [0002] At present, most of the glass covers on the market are fully laminated. Compared with the traditional frame lamination process, the full lamination process has the advantages of better display effect, thinner body and simpler assembly process. Therefore, the full lamination process has become a screen paste process. The mainstream of bonding, and a very important process in the full bonding process is UV curing, which requires 3000-5000mj / cm 2 The energy irradiates the glass cover; however, the general glass cover will turn yellow after UV curing, and the transmittance will also decrease, which will seriously affect the appearance and display effect, and the higher the UV energy, the more the irradiation times. The yellowing performance of the glass is more serio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C3/095C03C4/00C03B5/16C03B25/00
CPCC03C3/095C03C4/00C03B5/16C03B25/00Y02P40/57
Inventor 戴斌陈志鸿何进刘建党肖子凡刘攀邓臻禄刘红刚王明忠
Owner 深圳南玻科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap