Self-repairing anticorrosive coating for waste gas recovery pipeline

A technology of waste gas recovery and anti-corrosion coating, applied in anti-corrosion coatings, coatings, epoxy resin coatings, etc., can solve the problems of reducing maintenance costs and the lack of anti-corrosion durability of anti-corrosion coatings, so as to reduce maintenance costs and avoid the waste of repair agents. , good support effect

Active Publication Date: 2020-10-02
福建通海镍业科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the problem of lack of anticorrosion durability in the prior art anticorrosion coatings, the present invention discloses a self-repairing anticorrosion coating for waste gas recovery pipelines. The present invention introduces self-repairing slow-release balls to self-repair under trigger conditions The self-repairing agent is released in time in the slow-release ball to improve the repair of the base material of the anti-corrosion coating, greatly improving the service life and anti-corrosion effect of the anti-corrosion coating, and significantly reducing the maintenance cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The preparation method of the self-healing slow-release ball comprises the following steps:

[0036] (1) Synthesis of hollow mesoporous SiO 2 : Add tetraethyl orthosilicate, hexadecyltrimethylammonium bromide, absolute ethanol and ultrapure water into the container, and place it in a constant temperature water bath with magnetic stirring at 35-38°C. After stirring evenly, add Ammonia water with a mass fraction of 25-28%, react at constant temperature for 22-24h; after the reaction, centrifuge to obtain SiO 2 , and then washed with ethanol, the SiO 2 Put it into the mixture of hydrochloric acid and absolute ethanol, stir at 80-85°C for 20-24h, and finally use pure water to dissolve the SiO 2 Wash, dry and set aside, take SiO 2 Disperse in absolute ethanol, add aminopropyltriethoxysilane of equimolar mass, stir and react for 1-1.2h, and prepare hollow mesoporous SiO with amino groups on the surface 2 ; The initial addition ratio of tetraethyl orthosilicate, cetyltrime...

Embodiment 1

[0041] A self-repairing anti-corrosion coating for exhaust gas recovery pipelines, the self-repairing anti-corrosion coating comprises the following raw materials in parts by weight: 58 parts of methylsiloxane modified epoxy resin latex solution, 8 parts of self-repairing slow-release balls parts, 5 parts of plasticizer Vaseline and 6 parts of filler high alumina aggregate. The concentration of the methylsiloxane-modified epoxy resin latex solution is 65wt%; the self-healing slow-release ball includes a copolymer-mesoporous SiO 2 Shell and supported on copolymer-mesoporous SiO 2 A self-healing agent in the shell; the self-healing agent is methyl silicone oil.

[0042] The preparation method of the self-healing slow-release ball comprises the following steps:

[0043] (1) Synthesis of hollow mesoporous SiO 2 : Add tetraethyl orthosilicate, cetyltrimethylammonium bromide, absolute ethanol and ultrapure water into the container, and place it in a constant temperature water bat...

Embodiment 2

[0048] A self-repairing anti-corrosion coating for exhaust gas recovery pipelines, the self-repairing anti-corrosion coating comprises the following raw materials in parts by weight: 54 parts of methylsiloxane modified epoxy resin emulsion solution, 6 parts of self-repairing slow-release ball 6 parts, 6 parts of plasticizer chlorinated paraffin and 8 parts of high precision emery as filler. The concentration of the methylsiloxane-modified epoxy resin latex solution is 60wt%; the self-healing slow-release ball includes a copolymer-mesoporous SiO 2 Shell and supported on copolymer-mesoporous SiO 2 A self-healing agent in the shell; the self-healing agent is methyl silicone oil.

[0049] The preparation method of the self-healing slow-release ball comprises the following steps:

[0050] (1) Synthesis of hollow mesoporous SiO 2 : Add tetraethyl orthosilicate, cetyltrimethylammonium bromide, absolute ethanol and ultrapure water into the container, and place it in a constant temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of chemical structure corrosion prevention. The invention aims to solve the problem that anticorrosive paint in the prior art lacks anticorrosive durability. The invention discloses a self-repairing anticorrosive coating for a waste gas recovery pipeline. The self-repairing anticorrosive coating is prepared from the following raw materials in parts by weight: 54to 60 parts of methyl siloxane modified epoxy resin latex solution, 6 to 10 parts of self-repairing slow release balls, 4 to 6 parts of plasticizer and 4 to 8 parts of filler, wherein the concentration of the methyl siloxane modified epoxy resin latex solution is 60-70 wt%; the self-repairing sustained-release sphere comprises a copolymer-mesoporous SiO2 shell and a self-repairing agent loaded inthe copolymer-mesoporous SiO2 shell. By introducing the self-repairing slow-release ball, the self-repairing agent is released from the self-repairing slow-release ball in time under the triggering condition to repair the base layer material of the anti-corrosion coating, so that the service life of the anti-corrosion coating is greatly prolonged, the anti-corrosion effect of the anti-corrosion coating is greatly improved, and the maintenance cost is remarkably reduced.

Description

technical field [0001] The invention relates to the field of anticorrosion of chemical structures, in particular to a self-repairing anticorrosion coating for waste gas recovery pipelines. Background technique [0002] In industry, when processing stainless steel pickling sludge and other raw materials to extract nickel-chromium alloys, a large amount of SO2 is produced. 2 , H + The flue gas with moisture will seriously corrode the pipes and equipment, and the dust removal system. Various methods are used to thicken the steel plate and use stainless steel. These phenomena will not only greatly increase maintenance costs, but also cause exhaust gas leakage, pollute the environment, and pose a threat to biological health. Since the flue gas discharged in the pipeline is the exhaust gas produced just after sintering, it has a high residual temperature, which requires the exhaust pipeline and the inner wall coating of the pipeline to have high corrosion resistance in addition ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/08C09D163/00C09D7/65B01J13/14
CPCC09D5/08C09D163/00C09D7/65C09D7/70B01J13/14C08L2203/18C08L2207/53C08L2205/035C08L77/04C08L83/04C08K7/26C08K5/053C08L91/06C08K5/12
Inventor 陈杰陈波马选坤周鹏张良生
Owner 福建通海镍业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com