A kind of magnesium-doped cobalt disulfide composite carbon nanotube material, preparation method and application

A technology of cobalt disulfide and carbon nanotubes, applied in chemical instruments and methods, catalyst activation/preparation, chemical/physical processes, etc., to achieve uniform particle size and element distribution, high stability and cycle performance, and low cost Effect

Active Publication Date: 2021-08-17
DONGHUA UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Given the extensive research on transition metal oxide catalysts, few studies have been reported to design their intrinsic properties and enhance electrocatalytic performance by co-engineering the anion chemistry and cation chemistry of oxides.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnesium-doped cobalt disulfide composite carbon nanotube material, preparation method and application
  • A kind of magnesium-doped cobalt disulfide composite carbon nanotube material, preparation method and application
  • A kind of magnesium-doped cobalt disulfide composite carbon nanotube material, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] This embodiment provides a magnesium-doped cobalt disulfide composite carbon nanotube material ((Co, Mg)S with bifunctional activity 2 @CNTs) preparation methods such as figure 1 As shown, the specific preparation steps are as follows:

[0044] Step 1: 0.498g Co(Ac) 2 4H 2 O and 0.256g Mg(NO 3 ) 2 ·6H 2 O was added to 35 mL of deionized water, stirred until the crystals disappeared, and then transferred to an ultrasonic machine for sonication to ensure complete dissolution.

[0045] Step 2: Add 50mg of carbon nanotubes (particle size: 20-30nm, purity>98wt%, Zhongke Times Nano Center) into the above solution, and stir ultrasonically for 30 minutes to obtain a mixed solution.

[0046] Step 3: Transfer the mixed solution to a stirrer, add 0.64g of sulfur powder and 5mL of ethanol (as a dispersant) under magnetic stirring.

[0047] Step 4: After ultrasonically oscillating the mixture for 45 minutes, transfer it to a polytetrafluoroethylene lining, add it to the react...

Embodiment 2

[0051] This embodiment provides a magnesium-doped cobalt disulfide composite carbon nanotube material ((Co, Mg)S with bifunctional activity 2 @CNTs) preparation methods such as figure 1 As shown, the specific preparation steps are as follows:

[0052] Step 1: 0.498g Co(Ac) 2 4H 2 O and 0.256g Mg(NO 3 ) 2 ·6H 2 O was added to 35 mL of deionized water, stirred until the crystals disappeared, and then transferred to an ultrasonic machine for sonication to ensure complete dissolution.

[0053] Step 2: Add 50mg of carbon nanotubes (particle size: 20-30nm, purity>98wt%, Zhongke Times Nano Center) into the above solution, and stir ultrasonically for 30 minutes to obtain a mixed solution.

[0054] Step 3: Transfer the mixed solution to a stirrer, add 0.64g of sulfur powder and 5mL of ethanol (as a dispersant) under magnetic stirring.

[0055] Step 4: After ultrasonically oscillating the mixture for 45 minutes, transfer it to a polytetrafluoroethylene lining, add it to the react...

Embodiment 3

[0059] This embodiment provides a magnesium-doped cobalt disulfide composite carbon nanotube material ((Co, Mg)S with bifunctional activity 2 @CNTs) preparation methods such as figure 1 As shown, the specific preparation steps are as follows:

[0060] Step 1: 0.498g Co(Ac) 2 4H 2 O and 0.256g Mg(NO 3 ) 2 ·6H 2 O was added to 40 mL of deionized water, stirred until the crystals disappeared, and then transferred to an ultrasonic machine for sonication to ensure complete dissolution.

[0061] Step 2: Add 50mg of carbon nanotubes (particle size: 20-30nm, purity>98wt%, Zhongke Times Nano Center) into the above solution, and stir ultrasonically for 30 minutes to obtain a mixed solution.

[0062] Step 3: Transfer the mixed solution to a stirrer, add 0.64g of sulfur powder and 5mL of ethanol (as a dispersant) under magnetic stirring.

[0063] Step 4: After ultrasonically oscillating the mixture for 45 minutes, transfer it to a polytetrafluoroethylene lining, add it to the react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a magnesium-doped cobalt disulfide composite carbon nanotube material, a preparation method and its application in preparing a zinc-air battery cathode catalyst. The preparation method is to use a hydrothermal method to prepare a zinc-air battery cathode catalyst with oxygen reduction and oxygen evolution reactions, that is, magnesium nitrate is used as a dopant, cobalt acetate is used as a cobalt-based metal sulfide raw material, and sulfur powder is used as a vulcanizing agent. Sulfides and carbon nanotubes are recombined at high temperature under an inert atmosphere. Under the combination of metal and carbon materials, this method can effectively inhibit the agglomeration of cobalt on the one hand, and on the other hand simultaneously generate oxygen holes with efficient catalytic oxygen reduction and cobalt disulfide with oxygen evolution activity on the carbon nanotubes. Microparticles, the final catalyst material can be used in zinc-air batteries to achieve long-term, high-stability charge-discharge cycles.

Description

technical field [0001] The invention relates to a regulated and synthesized magnesium-doped cobalt disulfide composite carbon nanotube material, a preparation method and application, and belongs to the technical field of oxygen electrochemical reduction / precipitation dual-function catalysts. Background technique [0002] Today, the depletion of fossil energy and environmental pollution are increasing day by day, and the ensuing environmental problems such as energy shortage and greenhouse effect make it urgent for people to develop new sustainable energy storage devices. Batteries represent a promising and feasible energy conversion technology from the perspective of application prospects in numerous energy systems. Among them, the electrochemical energy source represented by rechargeable zinc-air batteries (ZABs) has attracted widespread attention due to its low cost, environmental friendliness, high safety, and high energy density. The theoretical energy density of the zi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/049B01J35/00B01J37/08B01J37/10H01M4/90
CPCB01J27/049B01J35/0033B01J35/006B01J37/08B01J37/10H01M4/9083Y02E60/50
Inventor 乔锦丽郭佳宁徐能能王旭王永霞娄文双李君
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com