Method for improving impact strength of large high-strength high-toughness nodular cast iron diesel engine body

A technology of impact strength and diesel engine, which is applied in the field of cast iron casting and heat treatment, can solve the problems of insufficient impact strength of large high-strength ductile cast iron body, failure to reach the impact strength range of the body body in the cast state, and failure to reach the impact strength range of the body, etc.

Inactive Publication Date: 2020-11-03
SHANNXI DIESEL ENGINE HEAVY IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, through the control of melting process parameters, the as-cast state cannot meet the requirements of the impact strength range of the machine body, resulting in insufficient impact strength of the large-scale high-strength ductile iron body body
[0003] Through the above analysis, the existing problems and defects of the existing technology are: the prior art cannot meet the requirements of the impact strength range of the machine body in the as-cast state through the control of the melting process parameters, resulting in insufficient impact strength of the large high-strength ductile iron body body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving impact strength of large high-strength high-toughness nodular cast iron diesel engine body
  • Method for improving impact strength of large high-strength high-toughness nodular cast iron diesel engine body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] In order to make the object, technical solution and advantages of the present invention more clear, the present invention will be further described in detail below in conjunction with the examples. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0035] Aiming at the problems existing in the prior art, the present invention provides a method for improving the impact strength of a large high-strength ductile iron diesel engine body. The present invention will be described in detail below in conjunction with the accompanying drawings.

[0036] Such as figure 1 As shown, the method for improving the impact strength of a large-scale high-strength ductile iron diesel engine body provided by the embodiments of the present invention includes:

[0037] S101: According to the principles of high carbon equivalent, high carbon and low silicon, controlling Mn and S, limiting P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of cast iron casting and heat treatment, and discloses a method for improving the impact strength of a large high-strength high-toughness nodular cast irondiesel engine body. The method comprises the following steps of determining stokehole chemical components according to the principles of high carbon equivalent, high carbon, low silicon, Mn and S control, P and Ti limitation, and addition of an additive Sb to eliminate distorted graphite; and conducting spheroidizing and inoculating again, primarily measuring the impact strength, performing low-temperature graphitization heat treatment, and measuring the impact strength again.ai According to the method, in the casting process, the principles of the high carbon equivalent, high carbon, low silicon, Mn and S control, P and Ti limitation, multi-stage inoculation and addition of the additive Sb to eliminate the distorted graphite is selected, generation of supercooled graphite and free cementite is reduced, and solidification of molten iron according to stable system eutectic is promoted; and meanwhile, pearlite is eliminated through low-temperature graphitization annealing, the ferrite content of the engine body structure is increased to 90% or above, and therefore the purpose of improving the impact strength of the engine body is achieved.

Description

technical field [0001] The invention belongs to the technical field of cast iron casting and heat treatment, in particular to a method for improving the impact strength of a large high-strength ductile iron diesel engine body. Background technique [0002] At present, a certain type of large-scale high-strength ductile iron diesel engine body is made of QT400-18A, the mechanical properties (attached casting sample) tensile strength ≥ 390 (MPa), yield strength ≥ 250 (MPa), elongation > 15%, cloth Hardness = 140-180 (HBS), impact strength: Kv average ≥ 14 joules, Kv individual ≥ 11 joules. Graphite form: Ⅴ~Ⅵ, size: 4~5. Substrate: ferrite ≥ 90%. In the prior art, through the control of melting process parameters, the as-cast state cannot meet the requirements of the impact strength range of the machine body, resulting in insufficient impact strength of the large high-strength ductile iron body body. [0003] Through the above analysis, the existing problems and defects o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C33/08C22C37/04C22C37/10C21D5/14C21D1/32C21C1/10
CPCC21C1/10C21D1/32C21D5/14C22C33/08C22C37/04C22C37/10Y02P10/20
Inventor 晁革新
Owner SHANNXI DIESEL ENGINE HEAVY IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products