Proton conducting membrane and preparation method thereof

A technology of proton conduction and diaphragm, which is applied in the direction of final product manufacturing, sustainable manufacturing/processing, climate sustainability, etc. It can solve the problems of poor toughness, short service life and inability to meet application requirements of proton conduction diaphragms, so as to promote Exercise, increase longitudinal tensile strength, effect of increasing longitudinal tensile strength

Active Publication Date: 2020-12-08
河南银金达新材料股份有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a proton conduction diaphragm and a preparation method thereof, in order to solve the problems that existing proton conduction diaphragms have poor toughness, cannot meet application requirements, and have a short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Proton conducting membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] In an embodiment, the preparation method of the proton-conducting membrane comprises the following steps:

[0026] (1) Mix 230-280 parts by mass of boehmite ceramic powder, 8-17 parts of polymethyl methacrylate, 0.6-1.3 parts of ammonium polyacrylate, 0.5-0.8 parts of lauryl polyoxyethylene ether, 0.4 -0.7 parts of carboxyethyl cellulose, 1.3-2.2 parts of sodium bis(2-ethylhexyl) hydroxysuccinate sulfonate, 0.4-0.9 parts of disodium octadecyl succinic acid monoamide sulfonate, 2-3 parts After mixing 1 part of polyethyl methacrylate, 0.1-0.2 part of graphene, and 500-800 parts of water, stir for 15-20 minutes at a microwave power of 80-150W, a temperature of 40-50°C, and a speed of 200-300r / min , to obtain slurry;

[0027] (2) Coating the slurry prepared in step (1) on the surface of a polyolefin film with a thickness of 12-13 μm by micro gravure coating to prepare a semi-finished separator with a coating thickness of 0.8-2 μm;

[0028] (3) Take 60-75 parts by mass of ...

Embodiment 1

[0032] A method for preparing a proton-conducting membrane, comprising the steps of:

[0033] (1) 236 parts by mass of boehmite ceramic powder, 9 parts of polymethyl methacrylate, 0.7 parts of ammonium polyacrylate, 0.5 parts of lauryl polyoxyethylene ether, 0.4 parts of carboxyethyl cellulose, 1.5 parts Parts of sodium di(2-ethylhexyl) hydroxysuccinate sulfonate, 0.4 parts of disodium octadecyl succinic acid monoamide sulfonate, 2.1 parts of polyethyl methacrylate, 0.1 parts of graphene, 520 parts of water After mixing, stir for 19 minutes at a microwave power of 100W, a temperature of 42°C, and a rotation speed of 200r / min to obtain a slurry;

[0034] (2) Coating the slurry prepared in step (1) on the surface of a polyolefin film with a thickness of 12 μm by micro gravure coating to prepare a semi-finished separator with a coating thickness of 1 μm;

[0035] (3) Take 62 parts by mass of silane coupling agent kh550, add it to water, and add acetic acid to adjust the pH value...

Embodiment 2

[0038] A method for preparing a proton-conducting membrane, comprising the steps of:

[0039] (1) 275 parts by mass of boehmite ceramic powder, 16 parts of polymethyl methacrylate, 1.2 parts of ammonium polyacrylate, 0.7 parts of lauryl polyoxyethylene ether, 0.6 parts of carboxyethyl cellulose, 2 Parts of sodium bis(2-ethylhexyl) hydroxysuccinate sulfonate, 0.9 parts of disodium octadecyl succinic acid monoamide sulfonate, 3 parts of polyethyl methacrylate, 0.2 parts of graphene, 786 parts of water After mixing, stir for 16 minutes at a microwave power of 140W, a temperature of 48°C, and a rotation speed of 300r / min to obtain a slurry;

[0040] (2) Coating the slurry prepared in step (1) on the surface of a polyolefin film with a thickness of 12.8 μm by micro gravure coating to prepare a semi-finished separator with a coating thickness of 1.6 μm;

[0041](3) Take 72 parts by mass of silane coupling agent kh550, add it to water, and add acetic acid to adjust the pH value to 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
coating thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a proton-conducting diaphragm, which comprises the following steps: (1) preparing boehmite ceramic powder, polymethyl methacrylate, ammonium polyacrylate, lauryl polyoxyethylene ether, carboxyethyl Base cellulose, sodium bis(2-ethylhexyl) hydroxysuccinate sulfonate, disodium octadecyl succinic acid monoamide sulfonate, polyethyl methacrylate, graphene, and water were mixed, and then microwave (2) Apply the slurry on the surface of the polyolefin film by micro-gravure roller coating to prepare a semi-finished separator; (3) Take the coupling agent and add it to water, and add acid to adjust pH value, to make a coupling agent solution; (4) Coupling agent solution is sprayed on the surface of the semi-finished diaphragm, and then the diaphragm is dried to prepare a proton-conducting diaphragm. The proton conduction membrane prepared by the invention has high efficiency when applied to the proton conduction membrane of a fuel cell, is not prone to fuel permeation, and has a long service life.

Description

technical field [0001] The invention belongs to the technical field of diaphragm preparation, and in particular relates to a proton-conducting diaphragm and a preparation method thereof. Background technique [0002] Proton-conducting membranes are used in many electrochemical applications, including fuel cells, electrolyzers, supercapacitors, sensors, and batteries. Nafion is the most commonly used membrane in fuel cells operating near room temperature (up to 100°C). Nafion, being a solid polymer electrolyte, has two major disadvantages, being very expensive and drying out during fuel cell operation due to water being dragged by protons. [0003] Proton-conducting membranes are the core technology of modern fuel cells. However, the efficiency of proton-conducting membranes currently used in fuel cells is relatively low, and they are prone to fuel permeation, leading to pollution. In addition, there are also the problems of poor toughness, which cannot meet application req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M8/1069H01M8/1041
CPCH01M8/1041H01M8/1069Y02E60/50Y02P70/50
Inventor 李国庆吕志国李航樊鹏鹏夏国华
Owner 河南银金达新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com