Self-repairing capsule, self-repairing anticorrosive coating material and preparation method and application thereof

An epoxy anti-corrosion coating and self-repair technology, applied in the field of materials, can solve the problems of self-repair reliability that needs to be improved, and does not take into account the fluidity of the capsule core, so as to avoid the sharp attenuation of self-repair function, high corrosion resistance, The effect of simple production process

Active Publication Date: 2020-11-10
NINGBO DADA CHEM CO LTD +1
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For example, CN101541416B discloses the principle and preparation method of a self-healing capsule, but the problem of fluidity of the capsule core at low temperature is not considered, and the actual user’s self-healing reliability needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-repairing capsule, self-repairing anticorrosive coating material and preparation method and application thereof
  • Self-repairing capsule, self-repairing anticorrosive coating material and preparation method and application thereof
  • Self-repairing capsule, self-repairing anticorrosive coating material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The embodiment of the present invention also provides a preparation method of the self-healing capsule, which includes:

[0043] At least mix liquid hydrocarbons, oil-soluble corrosion inhibitors, and polyamine compounds uniformly to form a capsule core mixture;

[0044] uniformly dispersing the capsule core mixture in the liquid epoxy resin in the form of an emulsion dispersion to obtain a capsule core dispersion;

[0045] At least polyisocyanate compound is added to the capsule core dispersion, so that the polyisocyanate compound reacts with part of the polyamine compound in the capsule core mixture at the interface of the capsule to form a polyurea film as the capsule wall.

[0046] Further, the preparation method includes: reacting the polyisocyanate compound and part of the polyamine compound in the capsule core mixture at the interface of the capsule at 0-100° C. under normal pressure to form a polyurea film as the capsule wall.

[0047] Further, the preparation ...

manufacture example 1

[0090] Manufacturing example 1, the preparation of capsule compound A-1 (the consumption of each component raw material as follows is in parts by mass, the same below):

[0091] Put 95 parts of naphthenic oil (KN4010, Karamay Chemical), 4 parts of dodecyl phosphonate, 1 part of D230 polyether amine (amine equivalent of 122, Huntsman Chemical) into the mixing tank and stir evenly to form a capsule core The mixture is filtered and packaged for subsequent use;

[0092] Put 50 parts of E51 epoxy resin into the dispersion kettle, add 50 parts of the above-mentioned capsule core mixture while dispersing, after feeding, disperse at a high speed for 0.5h at 45°C to obtain the capsule core dispersion;

[0093] Add 1.3 parts of TDI curing agent (W6875A, Wanhua Chemical, TDI prepolymer, NCO content 14.2%) to the dispersion kettle under stirring conditions, and make the TDI curing agent and capsule core dispersion uniformly disperse to obtain capsule compound A-1, packed for spare.

manufacture example 2

[0094] Manufacturing example 2, preparation of capsule complex A-2:

[0095] Put 78 parts of polyisobutylene (molecular weight 1300, Korea Daelim Chemical), 20 parts of barium petroleum sulfonate, and 2 parts of 140 polyamide (amine equivalent 200, Shanghai Jiangqiao Chemical Factory) into the mixing tank and stir evenly to form a capsule core mixture, filter , packing spare;

[0096] Put 70 parts of E51 epoxy resin into the dispersion kettle, add 30 parts of the above-mentioned capsule core mixture while dispersing, after feeding, disperse at 60°C for 5 hours at a high speed to obtain the capsule core dispersion;

[0097] Add 0.7 parts of HDI trimer (HT-100, HDI trimer, NCO content 21.8%, Wanhua Chemical Industry) to the dispersion kettle under stirring conditions, and make the HDI trimer and capsule core dispersion uniformly dispersed Obtain Capsule Complex A-2 and pack it for later use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a self-repairing capsule, a self-repairing anticorrosive coating material, a preparation method and application thereof. The self-repairing capsule comprises a capsule core anda capsule wall, wherein the capsule core comprises a liquid hydrocarbon, an oil-soluble corrosion inhibitor and a polyamine compound, and the capsule wall comprises a polyurea film. The self-repairing high-solid epoxy anticorrosive coating material provided by the invention has the advantages that the raw materials are easy to obtain, the production process flow is simple, and the preparation iseasy. The self-repairing capsule in a self-repairing epoxy anti-corrosion coating film (coating layer) formed by the self-repairing high-solid epoxy anti-corrosion coating material provided by the embodiment of the invention has thermal stability, hydrolytic stability and low-temperature fluidity.

Description

technical field [0001] The invention relates to an anti-corrosion coating, in particular to a self-repairing capsule, a self-repairing anti-corrosion coating and a preparation method and application thereof, belonging to the field of material technology. Background technique [0002] For a long time, metal corrosion, as a safety and economic problem, has attracted the attention of various countries. Metal corrosion will not only cause serious economic losses, but also affect human health. According to the statistics of corrosion protection organizations, the annual economic loss caused by metal corrosion in my country accounts for about 4% of the gross national product, and the corrosion loss in my country exceeds 2 trillion, which is 4 times the loss of natural disasters; It is necessary to bear the corrosion loss of more than 1,000 yuan. In order to avoid the serious consequences of metal corrosion, people often use the most economical and effective anti-corrosion coatings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/08C09D163/00B01J13/02
CPCC09D5/08C09D163/00C09D7/70B01J13/02
Inventor 刘栓孙立三郭小平李群陈旭杰辛亮陈志宇
Owner NINGBO DADA CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com