Preparation method of one-dimensional photonic crystal structure polymer film
A technology of one-dimensional photonic crystals and structural polymers, which is applied in the measurement of color/spectral properties, material analysis by optical means, and material analysis by observing the effect on chemical indicators, etc. Large, polymer damage and other problems, to achieve the effect of short detection time, reduced detection cost, and fast detection speed
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] Example 1 Preparation of Methamphetamine Molecularly Imprinted Polymer Precursor
[0027] (1) The template molecule methamphetamine (1.00mmol), the functional monomer methacrylic acid (7.29mmol) and acrylamide (30.96mmol) and the cross-linking agent N,N'-methylenebisacrylamide (0.55mmol) , added to a round-bottomed flask containing 2.4 mL of methanol and mixed, stirred overnight at 25°C for 12 hours;
[0028] (2) Add photoinitiator 2959 (0.059mmol) into the solution, stir evenly for 30min, deoxygenate with nitrogen for 5min, then obtain polymer precursor solution, set aside.
Embodiment 2 1
[0029] Embodiment 2 Preparation of one-dimensional photonic crystal structure polymer film
[0030] (1) Take a clean glass slide, drop 250 μL of the prepared precursor solution on the glass slide, and then take a 20mm×20mm one-dimensional photonic crystal template with a span of 761nm, a height of 75nm, and a width of 350nm along one side of the precursor solution. The side is slowly covered on the solution, and no air bubbles can appear. The photonic crystal template such as figure 1 shown;
[0031] (2) Place the glass sheet under an ultraviolet lamp to initiate polymerization for 2 hours, and remove it after polymerization to obtain a one-dimensional photonic crystal polymer film.
Embodiment 3
[0032] Example 3 Elution of the one-dimensional photonic crystal structure polymer film prepared in Example 2
[0033] Prepare 10mL of methanol:acetic acid=9:1 solution, place the polymerized one-dimensional photonic crystal polymer film in the solution, and perform ultrasonic cleaning;
[0034] (1) Change the eluent once every 15 minutes of ultrasonication, and change it 4 times, for a total of 1 hour of ultrasonic elution;
[0035] (2) After ultrasonic elution, rinse the surface of the molecularly imprinted membrane with methanol solution to wash off excess acetic acid solution to obtain a methamphetamine molecularly imprinted membrane, see figure 2 shown.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction