A kind of black glaze for insulator and preparation method thereof

A black glaze and insulator technology, applied in the production of ceramic materials, etc., can solve the problems of unrequired indicators such as glaze strength, porcelain bending strength, and insulator breakdown rate, and poor combination of colored glaze and electric porcelain body.

Active Publication Date: 2022-05-17
CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
View PDF18 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention intends to provide a black glaze for insulators and its preparation method, in order to solve the poor combination of the existing colored glaze and the electric porcelain body, which fails in the indicators such as glazing strength, porcelain bending strength, and insulator breakdown rate. asked questions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of black glaze for insulator and preparation method thereof
  • A kind of black glaze for insulator and preparation method thereof
  • A kind of black glaze for insulator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0115] This embodiment discloses a black glaze for insulators, including the following raw materials in parts by mass: 30 parts of Hunan high-potassium and low-sodium feldspar, 5 parts of Hunan high-sodium and low-potassium feldspar, 6 parts of ball clay, and 20 parts of hard kaolin 11 parts of calcined talc, 7 parts of limestone, 22 parts of quartz powder, 2 parts of barium carbonate, and 7 parts of black color base.

[0116] The black glaze in this example includes the following chemical composition:

[0117] SiO 2

AI 2 o 3

Fe 2 o 3

CaO MgO K 2 o

Na 2 o

BaO LL 64.8％ 15.2％ 0.5％ 3.3％ 3.6％ 2.9％ 1.3％ 1.5％ 6.9％

[0118] In this embodiment, a method for preparing a black glaze for insulators comprises the following steps:

[0119] (1) Prepare the following raw materials in parts by mass: 30 parts of Hunan high-potassium and low-sodium feldspar, 5 parts of Hunan high-sodium and low-potassium feldspar, 6 parts of bal...

Embodiment 2

[0135] This embodiment discloses a black glaze for insulators, which includes the following raw materials in parts by mass: 28 parts of Hunan high-potassium and low-sodium feldspar, 4 parts of Hunan high-sodium and low-potassium feldspar, 4 parts of ball clay, and 18 parts of hard kaolin 10 parts of calcined talc, 5 parts of limestone, 21.8 parts of quartz powder, 1.5 parts of barium carbonate, and 6.5 parts of black color base.

[0136] The black glaze in this example includes the following chemical composition:

[0137] SiO 2

AI 2 o 3

Fe 2 o 3

CaO MgO K 2 o

Na 2 o

BaO LL 65.1％ 15.1％ 0.6％ 3.1％ 3.6％ 2.8％ 1.28％ 1.47％ 6.95％

[0138] In this embodiment, a method for preparing a black glaze for insulators comprises the following steps:

[0139] (1) Prepare the following raw materials in parts by mass: 28 parts of Hunan high-potassium and low-sodium feldspar, 4 parts of Hunan high-sodium and low-potassium feldspar, ...

Embodiment 3

[0144] This embodiment discloses a black glaze for insulators, including the following raw materials in parts by mass: 31 parts of Hunan high-potassium and low-sodium feldspar, 7 parts of Hunan high-sodium and low-potassium feldspar, 7 parts of ball clay, and 21 parts of hard kaolin 12 parts of calcined talc, 8 parts of limestone, 24 parts of quartz powder, 3 parts of barium carbonate, and 9 parts of black color base.

[0145] The black glaze in this example includes the following chemical composition:

[0146] SiO 2

AI 2 o 3

Fe 2 o 3

CaO MgO K 2 o

Na 2 o

BaO LL 65.9％ 14.5％ 0.4％ 3.7％ 3.6％ 2.6％ 1.1％ 2.1％ 6.1％

[0147] In this embodiment, a method for preparing a black glaze for insulators comprises the following steps:

[0148] (1) Prepare the following raw materials in parts by mass: 27-31 parts of Hunan high-potassium and low-sodium feldspar, 4-8 parts of Hunan high-sodium and low-potassium feldspar, 3-7 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fluidityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of electroceramic glazes, and in particular relates to a black glaze for insulators and a preparation method thereof. A black glaze for insulators comprises the following raw materials in parts by mass: 27-31 parts of Hunan high-potassium and low-sodium feldspar, Hunan high-sodium low-potassium feldspar 4-8 parts, ball clay 3-7 parts, hard kaolin 18-22 parts, calcined talc 9-13 parts, limestone 5-9 parts, quartz powder 21-25 parts, barium carbonate 1 ‑3 parts, black color base 6‑10 parts. After the insulator is made into porcelain with black glaze, the surface of the porcelain body is bright black, smooth and bright, delicate and moist, which can well meet the needs of customers for black electric porcelain. Moreover, the black glaze of this scheme can be well combined with the body. After the porcelain is formed, an excellent intermediate layer can be produced between the glaze and the body, which can greatly improve the performance of the porcelain (increase the strength of the porcelain by more than 22%). The development of black glaze achieves the design purpose and meets the company's technology and industry standards.

Description

technical field [0001] The invention belongs to the technical field of electric porcelain glazes, and in particular relates to a black glaze for insulators and a preparation method thereof. Background technique [0002] Electric porcelain refers to a type of porcelain insulator used in power industry systems, which is made of natural minerals such as bauxite, kaolin, and feldspar as the main raw materials and fired at high temperature, including various line insulators and insulators for power station appliances, as well as other charged bodies. Insulating part for isolation or support. Electric porcelain is an important basic device of the electric power industry. The electric porcelain manufacturing industry belongs to the field of equipment manufacturing industry supported by the country during the "Eleventh Five-Year Plan" period, and is the basic industry of the national economy. [0003] The surface of electric porcelain is usually coated with electric enamel. Electri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/86C04B41/5022Y02P40/60
Inventor 姚绍明
Owner CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com