Manufacturing process for multilayer all-black walnut solid wood composite floor

A solid wood composite floor and a production process technology, applied in the field of flooring, can solve the problems of black walnut floor bending under force, waste of resources, low output, etc., and achieve the effects of increasing stability, avoiding waste of resources and firm structure

Active Publication Date: 2021-01-22
浙江精步木业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the price of black walnut is high and the output is low. At the same time, when the logs are sawed, some surplus materials will be generated, resulting in a waste of resources. Moreover, the compressive and weighing capabilities of black walnut floors are average. Electric appliances, the black walnut floor will bend under the force after a period of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process for multilayer all-black walnut solid wood composite floor
  • Manufacturing process for multilayer all-black walnut solid wood composite floor
  • Manufacturing process for multilayer all-black walnut solid wood composite floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] Specific embodiments of the present invention will be further described in detail below. It should be understood that the description of the embodiments of the present invention here is not intended to limit the protection scope of the present invention.

[0027] Such as figure 1 As shown, it is a flow chart of the manufacturing process of the multi-layer all-black walnut solid wood composite floor provided by the present invention. The multi-layer all-black walnut solid wood composite flooring includes a surface board 10 , a bottom board 20 , and a core board 30 arranged between the front board 10 and the bottom board 20 . It is conceivable that, as a floor, it must also include other functional structures, such as groove structure, mortise joint structure, etc., which are known to those skilled in the art and will not be repeated here.

[0028] The surface board 10 can be a whole solid wood board of grade A black walnut, and its thickness can be 2-4mm. In this embo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process for a multilayer all-black walnut solid wood composite floor, comprising the following steps: after a whole piece of solid wood is subjected to frame cutting, selecting out a surface plate and a bottom plate; sawing and trimming excess materials, splicing for multiple times, gluing and cold-pressing to form the core veneer, and finally hot-pressing and combining the surface veneer, the bottom veneer and the core veneer to form the multilayer all-black walnut solid wood composite floor. The core veneer is formed by splicing the excess materials for multiple times, so that the stress of the wood is almost zero, the excess materials are reasonably utilized, the resource waste is avoided, and meanwhile, the stability is greatly improved; in addition, the multilayer all-black walnut solid wood composite floor is of a multilayer combined structure; the defect that a black walnut floor is prone to deformation is overcome; and the multiple layersare all made of the same kind of black walnut wood, the physical properties are the same, the structure is firmer, and the overall quality is greatly improved.

Description

technical field [0001] The invention relates to the technical field of floors, in particular to a manufacturing process of a multi-layer all-black walnut solid wood composite floor. Background technique [0002] Solid wood composite flooring is made of cross-laminated multi-layer solid wood boards, which overcomes the shortcomings of solid wood flooring's wet expansion and shrinkage to a certain extent, and the dry shrinkage and wet expansion rate of solid wood composite flooring is small, and has good dimensional stability. , and retain the natural wood grain and comfortable foot feeling of the solid wood floor. At the same time, solid wood composite flooring also has the stability of laminate flooring and the aesthetics of solid wood flooring, and has environmental protection advantages. Black walnut solid wood composite flooring is widely acclaimed for its beautiful texture, long service life, and stable wood properties, so it is becoming more and more popular among cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27M3/04E04F15/04
CPCB27M3/04E04F15/046
Inventor 赵利均
Owner 浙江精步木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products