Preparation method of high-voltage and ultrahigh-voltage cable insulating material

A cable insulation and ultra-high voltage technology, applied in the direction of organic insulators, plastic/resin/wax insulators, etc., can solve the problems of time-consuming and labor-intensive cleaning equipment and environmental systems, high production and maintenance costs, and affect the quality of insulating materials, etc., to achieve equipment investment less, low cost, and improved cleanliness and stability

Pending Publication Date: 2021-01-29
南京地中缆科技有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this method are: 1. The screw structure of the reciprocating single-screw extruder is complicated, the process is complicated, and the equipment cost is high. The secondary melting process of the resin has a certain influence on the quality and performance of the resin; 2. The process of the twin-screw extruder is simple, Due to low-temperature strong shearing, high local temperature, and material retention, the low-density polyethylene molecules are destroyed, thermally aged, and crystal points, color particles, etc. appear, which seriously affect the quality of insulating materials; 3. In order to reduce resin aging, double Screw extruders and reciprocating single-screw extruders generally have a continuous production time of no more than 7 days, and the production efficiency is low, and cleaning equipment and environmental systems is time-consuming and laborious, resulting in high production and maintenance costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-voltage and ultrahigh-voltage cable insulating material
  • Preparation method of high-voltage and ultrahigh-voltage cable insulating material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention will be further described below in conjunction with the accompanying drawings.

[0016] A preparation method for high-voltage and ultra-high-voltage cable insulation materials, the specific process is as follows:

[0017] (1) After the ethylene monomer is compressed by the compressor 1, it is polymerized into low-density polyethylene at high pressure in the reactor 2. After being separated by the high-pressure and low-pressure separator 3, the low-density polyethylene directly enters the single-screw extruder 6 after being cooled. , add the liquid antioxidant 5 directly through the metering pump 4, and disperse the liquid antioxidant 5 evenly in the low-density polyethylene through the diversion device and the single-screw extruder 6, and then filter through the high-mesh filter 7 Granulate and store in the storage tank 8 to obtain antioxidant-containing low-density polyethylene. The liquid antioxidant used in this example is 2,4-bis(n-octylthiome...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a high-voltage and ultrahigh-voltage cable insulating material. The preparation method comprises the following steps: (1) compressing an ethylene monomer, carrying out high-pressure polymerization in a reactor to obtain low-density polyethylene, separating by a high-pressure separator and a low-pressure separator, cooling the low-density polyethylene, directly feeding into a single-screw extruder, adding a liquid antioxidant, uniformly dispersing the liquid antioxidant into low-density polyethylene, filtering through a high-mesh filter screen, and granulating to obtain low-density polyethylene containing the antioxidant; and (2) dedusting and grading the antioxidant-containing low-density polyethylene, adding a cross-linking agent by adoptinga post-permeation method, fully stirring, putting into an absorption bin, keeping the temperature, cooling, dedusting, removing impurities, and carrying out metal filtration to obtain the high-voltage and ultrahigh-voltage cable insulating material. According to the method provided by the invention, secondary melting processing of low-density polyethylene is avoided, thermal aging of resin is reduced, the cleanliness and the stability of the insulating material are improved, and the method is high in production efficiency, low in cost and convenient to popularize and apply.

Description

technical field [0001] The invention relates to a method for preparing high-voltage and ultra-high-voltage cable insulation materials, and belongs to the technical field of insulation material processing. Background technique [0002] At present, the high-voltage cable insulation materials at home and abroad are mainly cross-linked polyethylene materials. The preparation process is to mix low-density polyethylene with an appropriate amount of solid antioxidant through a twin-screw or reciprocating single-screw extruder to ensure that the antioxidant is uniform. The resin is dispersed in the low-density polyethylene resin. After the resin is filtered through a high-mesh filter, pelletized by an underwater pelletizer, and dried, it is combined with a cross-linking agent to infiltrate the process to achieve ultra-clean and low-scorch production of high-voltage cable insulation materials. . The disadvantages of this method are: 1. The screw structure of the reciprocating single...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08K5/375C08J3/20C08J3/24H01B3/44
CPCC08J3/203C08J3/24H01B3/44C08J2323/06C08K5/375
Inventor 高凯
Owner 南京地中缆科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products