Lightweight concrete and preparation method thereof
A lightweight concrete, mixing and mixing technology, applied in the field of concrete, can solve the problems of poor mechanical properties and short service life of lightweight concrete, and achieve the effects of reducing shrinkage and cracking, improving mechanical properties, and fast speed
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0056] A preparation method of lightweight concrete, comprising the following steps:
[0057] S1. under the rotating speed of 300r / min, the water of 5.5kg sodium dodecylbenzene sulfonate and 43.75kg is mixed and stirred for 10min to obtain foaming solution;
[0058] S2. Under the rotating speed of 130r / min, mix 210kg of cement, 900kg of stones, 350kg of river sand, 1.5kg of polycarboxylate water reducing agent, 2.2kg of basalt fiber (10mm in length), 2.5kg of glass fiber, 0.6kg of straw fiber, 0.3kg sodium alginate, 6.5kg calcium carbonate whisker (particle size is 30nm), 1.2kg D-mannitol, 0.65kg calcium stearate and 81.25kg water mix and stir 5min, then add the foaming of step S1 The solution was continuously stirred for 20 min to obtain lightweight concrete.
Embodiment 2
[0060] A preparation method of lightweight concrete, comprising the following steps:
[0061] S1. under the rotating speed of 325r / min, the water of 5kg sodium dodecylbenzene sulfonate and 43.125kg is mixed and stirred for 12.5min to obtain foaming solution;
[0062] S2. Under the rotating speed of 140r / min, mix 240kg of cement, 875kg of stones, 370kg of river sand, 2.5kg of polycarboxylate water reducer, 2kg of basalt fiber (12.5mm in length), 3kg of glass fiber, 0.45kg of straw fiber, 0.6 kg sodium alginate, 6kg calcium carbonate whisker (particle size is 32.5nm), 1.3kg D-mannitol, 0.75kg calcium stearate and 71.875kg water were mixed and stirred for 7.5min, and then the foaming of step S1 was added. The solution was continuously stirred for 25 min to obtain lightweight concrete.
Embodiment 3
[0064] A preparation method of lightweight concrete, comprising the following steps:
[0065] S1. under the rotating speed of 350r / min, 4.5kg whipping agent (sodium dodecylbenzene sulfonate 2.5kg, α-olefin sulfonate sodium 2kg) is mixed and stirred 15min with the water of 42kg, obtains foaming solution;
[0066] S2. Under the rotating speed of 150r / min, mix 270kg of cement, 850kg of stones, 390kg of river sand, 3.5kg of polycarboxylate water reducer, 1.8kg of basalt fiber (15mm in length), 3.5kg of glass fiber, 0.3kg of straw fiber, 0.9kg sodium alginate, 5.5kg calcium carbonate whisker (particle size is 35nm), 1.4kg D-mannitol, 0.85kg foam stabilizer (calcium stearate is 0.5kg, hydroxypropyl methylcellulose is 0.35kg) and 63kg of water for 10 minutes, then add the foaming solution of step S1, and continue to stir for 30 minutes to obtain lightweight concrete.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
length | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap