Mineral fiber enhanced modified expanded perlite insulation board and production method thereof

An expanded perlite and fiber-reinforced technology, which is applied in the field of building materials, can solve problems such as application limitations of expanded perlite insulation boards, and achieve the effects of superior fire resistance, good flexibility, and reasonable folding ratio

Inactive Publication Date: 2016-12-07
XINYANG CITY OF CRYSTAL ENG MATERIALS CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to various reasons, the application of expanded perlite insulation board is still subject to some restrictions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mineral fiber enhanced modified expanded perlite insulation board and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The mineral fiber reinforced modified expanded perlite insulation board of this embodiment includes the following components in parts by weight: 25 parts of cement, 5 parts of fly ash, 2 parts of methyltrimethoxysilane, and 5 parts of polyacrylate emulsion 3 parts of aluminum silicate fiber, 50 parts of modified expanded perlite, 0.7 part of sodium dodecylbenzenesulfonate, 5 parts of additive, 1 part of quicklime, 0.1 part of PP fiber, 1 part of sodium silicate and 10 parts of water .

[0040] The additive includes the following components in parts by weight: 25 parts of calcium sulfate, 2 parts of aluminum oxide, 0.2 part of sodium carboxymethylcellulose, 5 parts of zinc phosphate and 15 parts of iron oxide.

[0041] The specific preparation method of the modified expanded perlite is: heating the perlite to 1000°C for puffing treatment, expanding the volume of the perlite by 7 times to obtain the expanded perlite, and then cooling down, when the temperature drops to 10...

Embodiment 2

[0048] The mineral fiber-reinforced modified expanded perlite insulation board of this embodiment includes the following components in parts by weight: 32 parts of cement, 7 parts of fly ash, 3 parts of methyltrimethoxysilane, and 8 parts of polyacrylate emulsion 2 parts, 2 parts of aluminum silicate fiber, 2 parts of brucite fiber, 60 parts of modified expanded perlite, 1.5 parts of sodium dodecylbenzenesulfonate, 8 parts of additive, 2 parts of quicklime, 0.3 part of PP fiber, silicic acid 2 parts sodium and 15 parts water.

[0049] The additive includes the following components in parts by weight: 30 parts of calcium sulfate, 3 parts of aluminum oxide, 2 parts of sodium carboxymethylcellulose, 8 parts of zinc phosphate and 18 parts of iron oxide.

[0050] The specific preparation method of the modified expanded perlite is as follows: heating the perlite to 1200°C for puffing treatment, expanding the volume of the perlite by 8 times to obtain the expanded perlite, and then c...

Embodiment 3

[0057] The mineral fiber reinforced modified expanded perlite insulation board of this embodiment includes the following components in parts by weight: 40 parts of cement, 8 parts of fly ash, 5 parts of methyltrimethoxysilane, and 10 parts of polyacrylate emulsion 1 part, 1 part of aluminum silicate fiber, 2 parts of brucite fiber, 2 parts of sepiolite fiber, 70 parts of modified expanded perlite, 2.9 parts of sodium dodecylbenzenesulfonate, 10 parts of additive, 3 parts of quicklime, 0.5 parts of PP fiber, 2 parts of sodium silicate and 20 parts of water.

[0058] The additive includes the following components in parts by weight: 35 parts of calcium sulfate, 5 parts of aluminum oxide, 5 parts of sodium carboxymethylcellulose, 10 parts of zinc phosphate and 20 parts of iron oxide.

[0059] The specific preparation method of the modified expanded perlite is: heating the perlite to 1300°C for puffing treatment, expanding the volume of the perlite by 10 times to obtain the expand...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a mineral fiber enhanced modified expanded perlite insulation board and a production method thereof. The mineral fiber enhanced modified expanded perlite insulation board comprises in parts by weight, 25-40 parts of cement, 5-8 parts of coal ash, 2-5 parts of methyltrimethoxysilane, 5-10 parts of polyacrylate emulsion, 3-5 parts of mineral fibers, 50-70 parts of modified expanded perlite, 0.7-2.9 parts of sodium dodecyl benzene sulfonate, 5-10 parts of additives, 1-3 parts of calcined lime, 0.1-0.5 part of PP (polypropylene) fibers, 1-2 parts of sodium silicate and 10-20 parts of water. The mineral fiber enhanced modified expanded perlite insulation board takes the cement, the coal ash, the mineral fibers and other organic and inorganic matters as raw materials, industrial and mining waste materials are effectively used, toxic and harmful substances are not added, and the insulation board is green and environmentally friendly.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a mineral fiber-reinforced modified expanded perlite insulation board and a production method thereof. Background technique: [0002] With the vigorous development of the construction industry and the modernization of buildings, the use of insulation boards in construction projects has increased year by year. External wall insulation can effectively block heat conduction, and the insulation effect is very obvious. It can not only save a lot of heating costs in winter, but also is more environmentally friendly than other heating methods. The thermal insulation materials currently used in my country are mainly organic thermal insulation materials and inorganic thermal insulation materials. However, due to the characteristics of the chemical properties of materials, no matter whether it is inorganic thermal insulation materials or organic thermal insulation ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04B28B1/52B28B3/02
CPCC04B28/04B28B1/525B28B3/02C04B2111/00017C04B2111/28C04B2111/40C04B2201/32C04B2201/50
Inventor 安武梅春河厉励蔡燚
Owner XINYANG CITY OF CRYSTAL ENG MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap