Auxiliary metal machining process for CuCr contact surface treatment machining

A technology to assist metal and processing technology, applied in the field of metal surface processing, can solve the problem of not completely avoiding the risk of cleaning, not being able to ensure product surface cleanliness, increasing the risk of product oxidation, etc., to avoid oxidation risks and to achieve excellent appearance quality. , the effect of high appearance consistency

Active Publication Date: 2021-03-09
SHAANXI SIRUI ADVANCED MATERIALS CO LTD
View PDF29 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Dry polishing cannot completely avoid the risk of cleaning
[0004] In addition, the general wet polishing mostly uses water or water-based medium as cooling and wetting, which greatly increases the risk of product oxidation, and subsequent cleaning cannot ensure that the surface of the product is clean, and there are often water stains. Improper cleaning of ceramic abrasive polishing products will leave a small amount of residual powder residue
According to statistics, as a contact manufacturer with an annual output of 8 million PCS, the annual number of product repairs caused by oxidation and other appearance problems in the manufacturing process accounts for as much as 10%, and the cost for this part of the repair is also very high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Auxiliary metal machining process for CuCr contact surface treatment machining
  • Auxiliary metal machining process for CuCr contact surface treatment machining
  • Auxiliary metal machining process for CuCr contact surface treatment machining

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An auxiliary metal processing technology for CuCr contact surface treatment processing, comprising the following steps:

[0029] Step 1, magnetic grinding: Put the CuCr contacts into the magnetic grinding equipment, add the grinding cooling and wetting medium to the magnetic grinding equipment, the grinding cooling and wetting medium submerges all the CuCr contacts, and control the total amount of the grinding cooling and wetting medium to be added. 50L, the magnetic grinding equipment adopts NF-9808 high-precision magnetic grinding equipment, the volume of the grinding tank is 175L, and the grinding cooling and wetting medium is No. 10 industrial white oil. The rust liquid can effectively reduce the oxidation of the metal surface. The anti-rust liquid is composed of the following components by weight: 15 parts of naphthenic base oil, 7 parts of diethanolamine borate, 10 parts of polyethylene glycol, and 13 parts of acetyl triethyl citrate 9 parts of lanthanum phytate, ...

Embodiment 2

[0035] An auxiliary metal processing technology for CuCr contact surface treatment processing, comprising the following steps:

[0036] Step 1, Magnetic Grinding: Put the CuCr contacts into the magnetic grinding equipment, add grinding cooling and wetting medium to the magnetic grinding equipment, the grinding cooling and wetting medium submerges all CuCr contacts, and control the total amount of grinding cooling and wetting medium added to 45L , the magnetic grinding equipment in step 1 adopts NF-9808 high-precision magnetic grinding equipment, the grinding tank volume is 175L, wherein the grinding cooling and wetting medium adopts No. 10 industrial white oil, while adding the grinding cooling and wetting medium, add antirust liquid, Adding anti-rust liquid can effectively reduce the oxidation of metal surface. The anti-rust liquid is composed of the following components by weight: 10 parts of naphthenic base oil, 3 parts of diethanolamine borate, 8 parts of polyethylene glyco...

Embodiment 3

[0042] An auxiliary metal processing technology for CuCr contact surface treatment processing, comprising the following steps:

[0043] Step 1, magnetic grinding: Put the CuCr contacts into the magnetic grinding equipment, add the grinding cooling and wetting medium to the magnetic grinding equipment, the grinding cooling and wetting medium submerges all the CuCr contacts, and control the total amount of the grinding cooling and wetting medium to be added. 48L, the magnetic grinding equipment adopts NF-9808 high-precision magnetic grinding equipment, the volume of the grinding tank is 175L, and the grinding cooling and wetting medium is No. 10 industrial white oil. The rust liquid can effectively reduce the oxidation of the metal surface. The anti-rust liquid is composed of the following components by weight: 15 parts of naphthenic base oil, 6 parts of diethanolamine borate, 9 parts of polyethylene glycol, and 12 parts of acetyl triethyl citrate 8 parts of lanthanum phytate, 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an auxiliary metal machining process for CuCr contact surface treatment machining. The process comprises the steps of magnetic grinding, abrasive matching, CuCr contact basketing, grinding and vacuum degreasing treatment; and number 10 industrial white oil is adopted as a grinding cooling wetting medium, mixed abrasive adopting a stainless steel needle is adopted as grinding polishing abrasive, a CuCr contact is subjected to magnetic grinding polishing, then vacuum degreasing, vacuum drying and vacuum packaging are conducted, and the technical requirement that "the surface of the CuCr contact is free of scratches, oxidation, stains and other defects" is met. The process is low in consumption, environment friendly and efficient, the oxidation risk of the polishing link is effectively avoided, the CuCr contact produced through the process is excellent in appearance quality, the surface appearance of the product is in inherent metallic luster, and the appearance consistency is high.

Description

technical field [0001] The invention relates to the technical field of metal surface processing, in particular to an auxiliary metal processing technology for CuCr contact surface processing. Background technique [0002] One of the technical requirements for the delivery appearance of CuCr contacts for vacuum interrupters is "no surface defects such as scratches, oxidation and stains", which requires good appearance quality. Defects such as oxidation and scratches on the surface of the contact material will affect the functional characteristics of the vacuum interrupter, so these defects are not allowed. In the process of contact manufacturing, due to the long process and many process links, the product is frequently grasped and moved in sequence, and the total duration of the process is long. It is inevitable that different degrees of scratches, oxidation, etc. will occur on the final cutting surface. Surface appearance defects, it is difficult to achieve a high degree of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B24B1/00B24B31/10B24B31/12B24B31/14C09G1/02
CPCB24B1/00B24B31/003B24B31/102B24B31/12B24B31/14C09G1/02
Inventor 杨斌李鹏王小军刘凯张石松孙广林马瑞妮
Owner SHAANXI SIRUI ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com