Preparation method of anti-felting woolen overcoat
A woolen coat, anti-felt shrinkage technology, applied in the direction of anti-shrinkage fibers, textiles and papermaking, fiber processing, etc. , maintain flexibility and feel, the effect of simple production process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A preparation method of an anti-felting woolen overcoat, said method comprising the following steps:
[0017] Step 1. According to the ratio of parts by weight, 13 parts of adipic acid, 8 parts of ethyl triethoxysilane, 4 parts of o-hydroxybenzoic acid ester, 4 parts of ethyl acrylate, 1 part of dodecyl trimethoxysilane 2 parts, 2 parts of guar gum hydroxypropyltrimethylammonium chloride, 2 parts of hexamethylenediamine sodium laurylsulfonate, 4 parts of methylcyclosiloxane, 1 part of double-terminal carboxypolyethylene glycol, put into reaction In the container, under the protection of nitrogen, the temperature was raised to 170°C, and the temperature was kept for 0.5h. Then, 3 parts of didecyldimethyl ammonium chloride, 12 parts of natural saponin, 3 parts of titanium isopropoxide, and 1 part of phosphorous acid were added, and the temperature was raised to 240°C. , reacted in vacuum at 0.04MPa for 2h, cooled down to 70°C after the reaction, stopped the reaction, and ...
Embodiment 2
[0020] A preparation method of an anti-felting woolen overcoat, said method comprising the following steps:
[0021] Step 1. According to the ratio of parts by weight, 15 parts of adipic acid, 9 parts of ethyl triethoxysilane, 6 parts of o-hydroxybenzoic acid ester, 5 parts of ethyl acrylate, 2 parts of dodecyl trimethoxysilane 4 parts of guar gum hydroxypropyltrimethylammonium chloride, 3 parts of hexamethylenediamine sodium dodecylsulfonate, 6 parts of methylcyclosiloxane, 3 parts of double-terminal carboxypolyethylene glycol into the reaction In the container, under the protection of nitrogen, the temperature was raised to 180 ° C, and the temperature was kept for 1 hour, and then 7 parts of didecyldimethyl ammonium chloride, 16 parts of natural saponin, 4 parts of titanium isopropoxide, and 3 parts of phosphorous acid were added, and the temperature was raised to 250 ° C. Vacuum reaction at 0.06MPa for 2.5h, after the reaction, cool down to 70°C, stop the reaction, and obt...
Embodiment 3
[0024] A preparation method of an anti-felting woolen overcoat, said method comprising the following steps:
[0025] Step 1. According to the ratio of parts by weight, 18 parts of adipic acid, 10 parts of ethyl triethoxysilane, 9 parts of o-hydroxybenzoic acid ester, 7 parts of ethyl acrylate, 3 parts of dodecyl trimethoxysilane 6 parts, 6 parts of guar gum hydroxypropyltrimethylammonium chloride, 4 parts of hexamethylenediamine sodium dodecylsulfonate, 7 parts of methylcyclosiloxane, 5 parts of double-terminal carboxypolyethylene glycol into the reaction In the container, the temperature was raised to 200°C under the protection of nitrogen, and kept for 1 hour, then 7 parts of didecyldimethylammonium chloride, 16 parts of natural saponin, 6 parts of titanium isopropoxide, and 5 parts of phosphorous acid were added, and the temperature was raised to 260°C. Vacuum reaction at 0.08MPa for 3 hours, after the reaction, lower the temperature to 70°C, stop the reaction, and obtain t...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap