Magnetic writing wall and preparation process thereof

A preparation process and magnetic attraction technology, applied in the field of building decoration materials, can solve the problems of poor surface writing and erasing performance, poor construction, easy rusting of iron powder, etc.

Active Publication Date: 2021-04-30
SUZHOU DEODAR SPECIAL BUILDING MATERIALS
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some existing products such as iron powder magnetic paint, iron powder is easy to rust, lose magnetism, and produce rust spots, and it cannot be applied as easily as commonly used paints, which restricts the application of magnetic whiteboards
However, the writing and erasing performance on the surface of the whiteboard wall is not durable, and some necessary tapes are easy to leave residual glue on the surface, which is not easy to clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetic writing wall and preparation process thereof
  • Magnetic writing wall and preparation process thereof
  • Magnetic writing wall and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] The preparation process of the magnetic writing wall of the present embodiment includes the following process steps:

[0069] 1) Leveling of the base layer of the wall surface: plastering with high-strength putty to repair and level the base layer of the wall surface;

[0070] 2) Apply the water-based reinforcing sealant to the leveled wall surface in step 1), penetrate and reinforce and seal the base layer, and after the surface is dry, lightly sand the surface to remove the burrs;

[0071] 3) Apply the water-based magnetic tough glaze paint evenly on the surface of the base layer that has been sealed in step 2) with a roller, and apply 3 coats evenly. Under the temperature condition of 23°C, the time between two coats is 2h;

[0072] 4) Evenly apply the water-based writing tough glaze paint on the surface of the water-based magnetic suction tough glaze coating formed in step 3) with a roller, and apply 2 coats evenly. After 4 hours, a magnetic writing wall is obtaine...

Embodiment 2

[0083] The preparation process of the magnetic writing wall of the present embodiment includes the following process steps:

[0084] 1) Leveling of the base layer of the wall surface: plastering with high-strength putty to repair and level the base layer of the wall surface;

[0085] 2) Apply the water-based reinforcing sealant to the leveled wall surface in step 1), penetrate and reinforce and seal the base layer, and after the surface is dry, lightly sand the surface to remove the burrs;

[0086] 3) Apply the water-based magnetic tough glaze paint evenly on the surface of the base layer that has been sealed in step 2) with a roller, and apply 3 coats evenly. Under the temperature condition of 23°C, the time between two coats is 2h;

[0087] 4) Evenly apply the water-based writing tough glaze paint on the surface of the water-based magnetic suction tough glaze coating formed in step 3) with a roller, and apply 2 coats evenly. After 4 hours, a magnetic writing wall is obtaine...

Embodiment 3

[0098] The difference between this embodiment and embodiment 1 is that, in the water-based magnetically attractive tough glaze paint, the mass ratio of component A to component B is 1:11, and the others are the same as in embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a magnetic writing wall and a preparation process thereof. The magnetic attraction writing wall is prepared from water-based magnetic attraction tough glaze paint and water-based writing tough glaze paint. The magnetic attraction writing wall is easy to coat and construct, firm in adhesion to various base materials, strong in coating ferromagnetism, high in surface drying speed, excellent in writing erasability, high in scratch resistance and hardness, free of damage during solvent wiping, capable of completely meeting various requirements for whiteboard performance in actual use, capable of completely replacing metal whiteboards and glass whiteboards, reduces waste of financial resources and material resources, reduces unnecessary space occupation, and brings good economic benefits and social benefits into play.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, and relates to a magnetic writing wall and a preparation process thereof. Background technique [0002] In teaching and office spaces, the writing whiteboard is an indispensable facility, which can be a hanging writing whiteboard or a made writing whiteboard wall to meet the writing requirements. The whiteboard wall can meet the needs of writing, and the user also needs the wall to have the function of magnet adsorption, and the performance of adhesive tape without leaving any glue residue. Some existing products, such as iron powder magnetic paint, iron powder is easy to rust, loses magnetism, produces rust spots, and cannot be easily applied like commonly used paints, which restricts the application of magnetic whiteboards. However, the surface writing and erasing performance of the whiteboard wall is not durable, and some necessary tapes are easy to leave residual glue o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/23C09D163/00C09D175/04C09D7/61C09D7/63E04F13/02
CPCC09D5/23C09D163/00C09D175/04C09D7/61C09D7/63E04F13/02C08L2205/02C08L2205/035C08K2003/2241C08K2201/01C08L83/12C08L83/04C08K13/02C08K3/08C08K3/346C08K5/5435C08L75/04C08K3/22
Inventor 党文生杨永顾王贤云江浩文
Owner SUZHOU DEODAR SPECIAL BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com