Silver-body light-transmitting enamel and manufacturing process thereof

A technology of making crafts and silver tires, which is applied in decorative arts, special decorative structures, etc., can solve problems such as poor light transmission, and achieve the effect of good light transmission and good transparency

Pending Publication Date: 2021-05-11
河南梦祥纯银制品有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cloisonné enamel silverware made by the above method, the silver body is inside the enamel, and the light transmission is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The manufacturing process of the silver tire translucent enamel of the present embodiment comprises the following steps:

[0022] 1) Design the tire pattern, silk drawing, and blueprint of the blueprint: first, the designer designs the fetal pattern, silk drawing, and blueprint of the silver carcass. The silk drawing is a drawing of the pattern of the silver wire on the carcass. Blueprints are color drafts used by Dotlan.

[0023] 2) Carcass making: Cut the silver sheet into various shapes, and beat it with a hammer to form a silver carcass, and then connect the various parts of it. After welding with good solder, it will become the silver carcass of the vessel.

[0024] 3) Filigree: Use tweezers to pinch and break the flattened thin silver wire into patterns, and then dip bletilla striata on the silver tire to form the pattern shown on the silk drawing.

[0025] 4) Welding: Sieve silver solder powder on the silver tire after filigree, and burn it at 900°C to firmly w...

Embodiment 2

[0032] The manufacturing process of the silver tire translucent enamel of the present embodiment comprises the following steps:

[0033] 1) Design the tire pattern, silk drawing, and blueprint of the blueprint: first, the designer designs the fetal pattern, silk drawing, and blueprint of the silver carcass. The silk drawing is a drawing of the pattern of the silver wire on the carcass. Blueprints are color drafts used by Dotlan.

[0034] 2) Carcass making: Cut the silver sheet into various shapes, and beat it with a hammer to form a silver carcass, then connect all parts of it with welding powder, and after high-temperature welding, it will become the silver carcass of the vessel.

[0035] 3) Filigree: Use tweezers to pinch and break the flattened thin silver wire into patterns, and then dip it in bletilla striata to adhere to the silver tire.

[0036] 4) Welding: Sieve silver solder powder on the silver tire after filigree, and burn it at 900°C to firmly weld the silver wir...

Embodiment 3

[0043] The manufacturing process of the silver tire translucent enamel of the present embodiment comprises the following steps:

[0044] 1) Design the tire pattern, silk drawing, and blueprint of the blueprint: first, the designer designs the fetal pattern, silk drawing, and blueprint of the silver carcass. The silk drawing is a drawing of the pattern of the silver wire on the carcass. Blueprints are color drafts used by Dotlan.

[0045] 2) Carcass making: Cut the silver sheet into various shapes, and beat it with a hammer to form a silver carcass, then connect all parts of it with welding powder, and after high-temperature welding, it will become the silver carcass of the vessel.

[0046] 3) Filigree: Use tweezers to pinch and break the flattened thin silver wire into patterns, and then dip it in bletilla striata to adhere to the silver tire.

[0047] 4) Welding: Sieve silver solder powder on the silver tire after filigree, and burn it at 950°C to firmly weld the silver wir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a silver-body light-transmitting enamel and a manufacturing process thereof. The manufacturing process comprises the following steps of silver body manufacturing, wire inlay, welding, bluing, bluing and body removing. An enamel glaze material used for applying the blue is a transparent glaze material; and the blank removing is to remove the silver blank so as to enable the enamel to be light-transmitting. According to the manufacturing process of the silver-body light-transmitting enamel, the transparent glaze is selected, the body for supporting the whole device shape is removed after bluing, and the silver-body light-transmitting enamel can be manufactured, is good in light transmission and has very good transparency from inside to outside.

Description

technical field [0001] The invention belongs to the technical field of light-transmitting enamel, and in particular relates to a silver-bodied light-transmitting enamel and a manufacturing process thereof. Background technique [0002] Cloisonné enamelware refers to utensils made of gold, silver, copper and other carcasses that are filigree, blued and fired. [0003] In the prior art, the application publication number is the invention patent of CN106240217A, discloses a kind of manufacture method of cloisonné enamel silverware, and this method comprises the following steps: (1) tire making: silver material is made into silver tire; (2) Scrubbing: Polish the silver tire obtained in step (1) with 240-400 mesh sandpaper until the surface is smooth; (3) filigree: make a pattern of silver wire and bond it to the silver tire after rubbing in step (2) (4) Welding: Weld the silver body that has been threaded in step (3) with flux, specifically, spray water on the surface of the th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/00B24B1/00C23D5/00C23D11/00
CPCB44C5/00B24B1/00C23D5/00C23D11/00
Inventor 吕雪峰路英霞
Owner 河南梦祥纯银制品有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com