Waterborne epoxy resin coating, waterborne epoxy resin coating, floor and preparation method thereof

A water-based epoxy resin and water-based epoxy technology, applied in the field of coatings, can solve problems such as harsh construction conditions, achieve good wear resistance, improve curing speed, and meet market demand.

Active Publication Date: 2022-05-24
ASIA PAINT SHANGHAI
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the water-based epoxy resin coatings on the market have harsh construction conditions. The construction can only be carried out under the condition that the ambient temperature is 8°C-35°C, the humidity is <80%, and the surface temperature is 3°C higher than the dew point temperature, so it is severely limited. its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] One embodiment of the present invention provides a method for preparing the above-mentioned water-based epoxy resin coating, comprising the following steps:

[0046] S101: mixing the raw materials of component A, stirring evenly, to prepare component A;

[0047] S102: Mix the raw materials of component B and stir evenly to prepare component B.

[0048] An embodiment of the present invention provides a water-based epoxy resin coating, which is prepared by using the above-mentioned water-based epoxy resin coating.

[0049] An embodiment of the present invention provides a preparation method of a water-based epoxy coating, comprising the following steps:

[0050] S201: Provide the above water-based epoxy resin coating;

[0051] In step S201, the water-based epoxy resin coating is as described above, which will not be repeated here.

[0052] Further, in step S201, the preparation method of the water-based epoxy resin coating includes the following steps:

[0053] S2011:...

Embodiment 1

[0063] Component A: 45% non-ionic waterborne epoxy curing agent, 2% waterborne polyamide curing agent, 3% latex powder, 0.8% dispersant, 0.3% defoamer, 15% titanium dioxide, 15% barium sulfate, Quartz powder 8%, wax powder 1.5%, water balance;

[0064] B component: 128 resin (hydrogenated bisphenol A epoxy resin) 90%, reactive diluent AGE 7.5%, emulsifier 2.5%.

[0065] Preparation:

[0066] (1) Mix all the raw materials of component A, and stir for 30 to 40 minutes under the condition of 1300 to 1500 r / min to obtain component A;

[0067] (2) mixing the raw materials of component B, stirring evenly, to prepare component B;

[0068] (3) Mixing the A component and the B component in a mass ratio of 6:1 to prepare a mixed slurry;

[0069] (4) Construction is carried out in an environment of about 0°, and the mixed slurry is coated on the substrate and dried to obtain the water-based epoxy resin coating of Example 1.

Embodiment 2

[0071] Component A: 50% non-ionic waterborne epoxy curing agent, 2.5% waterborne polyamide curing agent, 3.5% latex powder, 1% dispersant, 0.4% defoamer, 17% titanium dioxide, 15% barium sulfate, Quartz powder 8%, wax powder 1.2%, water balance;

[0072] B component: 128 resin (hydrogenated bisphenol A epoxy resin) 89%, active diluent AGE 8%, emulsifier 3%; A:B=5:1 mixing and stirring.

[0073] Preparation:

[0074] (1) Mix all the raw materials of component A, and stir for 30 to 40 minutes under the condition of 1300 to 1500 r / min to obtain component A;

[0075] (2) mixing the raw materials of component B, stirring evenly, to prepare component B;

[0076] (3) Mixing the A component and the B component in a mass ratio of 5:1 to prepare a mixed slurry;

[0077] (4) The construction is carried out in an environment of about 0°, and the mixed slurry is coated on the substrate and dried to obtain the water-based epoxy resin coating of Example 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tack-free timeaaaaaaaaaa
Login to view more

Abstract

The present invention relates to water-based epoxy resin coating, water-based epoxy resin coating, floor and preparation method thereof, wherein the water-based epoxy resin coating comprises: A component; in parts by weight, said A component comprises: non-ionic 40-60 parts of water-based epoxy curing agent, 2-3 parts of water-based polyamide curing agent, 1.1-2 parts of auxiliary agent and 20-50 parts of powder; the hydrogen equivalent of the non-ionic water-based epoxy curing agent is 120 ‑280; the powder includes latex powder, quartz powder, wax powder, titanium dioxide and barium sulfate; and B component; in parts by weight, the B component includes: hydrogenated bisphenol A type epoxy resin 83‑ 91 parts, 3-10 parts of diluent and 1-3 parts of emulsifier. The water-based epoxy resin coating can be applied in a low temperature environment (such as about 0° C.), and the obtained coating has high wear resistance and hardness.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based epoxy resin coating, a water-based epoxy resin coating, a floor and a preparation method thereof. Background technique [0002] Epoxy resin coatings are widely used in the preparation of epoxy resin floors, especially industrial floors, due to their high hardness, good wear resistance, strong adhesion, good flexibility, and excellent chemical corrosion resistance. At present, epoxy resin floors are mainly divided into solvent-based epoxy resin floors and water-based epoxy resin floors. Among them, solvent-based epoxy resin floors contain a large amount of volatile organic solvents, which have a greater impact on the environment, so they are gradually replaced by water-based epoxy resin floors. At present, the water-based epoxy resin floors on the market are mainly prepared by mixing and proofing of curing agents, various additives and powders, and then compounded ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D7/61C09D7/65C09D7/20C08G59/40C08G59/68E04F15/12
CPCC09D163/00C09D7/61C09D7/65C09D7/20C08G59/40C08G59/686E04F15/12C08K2003/2241C08K2003/3045C08L2205/035C08L2205/025C08L91/06C08L71/02C08L63/00C08K3/36C08K3/22C08K3/30
Inventor 毛美琴李金钟徐志新
Owner ASIA PAINT SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap