A preparation method of anti-cracking-self-healing-root-blocking functional additive for concrete

A concrete and functional technology, applied in the field of building materials, can solve problems such as waste of resources, and achieve the effects of increasing service life, increasing water absorption rate, and increasing osmotic pressure.

Active Publication Date: 2022-02-25
HUBEI UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In my country, the output of copper tailings is extremely large, and most of them are treated as waste, which causes huge pressure on the environment and wastes a lot of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of anti-cracking-self-healing-root-blocking functional additive for concrete
  • A preparation method of anti-cracking-self-healing-root-blocking functional additive for concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1) 100 parts by mass of copper tailings, 500 parts by mass of water and 1 part by mass of grinding aid are mixed and placed in a wet mill at a speed of 400 RPS to wet grind to a median particle size of 100nm to obtain nanometer copper tailings;

[0022] 2) Get 50 parts by mass of 2% (g / mL) chitosan solution and put it into an electromagnetic stirrer with a rotating speed of 300r / min, add 10 parts by mass of 0.25mol / L glutaraldehyde solution during stirring, Stir in a constant temperature water bath for 10 minutes;

[0023] 3) Add 5 parts by mass of the nano-copper tailings in step 1) to the solution in step 2) and continue the constant temperature water bath for 1 hour, freeze-dry for 24 hours to obtain the anti-cracking-self-healing-root-blocking functional additive for concrete.

Embodiment 2

[0025] 1) 100 parts by mass of copper tailings, 480 parts by mass of water and 1.2 parts by mass of grinding aid are mixed and placed in a wet mill at a speed of 420RPS to wet grind to a median particle size of 85nm to obtain nanometer copper tailings;

[0026] 2) Get 50 parts by mass of 2.2% (g / mL) chitosan solution and put it into an electromagnetic stirrer with a rotating speed of 300r / min, add 10 parts by mass of 0.28mol / L glutaraldehyde solution during stirring, Stir in a constant temperature water bath for 10 minutes;

[0027] 3) Add 6 parts by mass of the nano-copper tailings in step 1) to the solution in step 2) and continue the constant temperature water bath for 1 hour, freeze-dry for 24 hours to obtain the anti-cracking-self-healing-root-blocking functional additive for concrete.

Embodiment 3

[0029] 1) 100 parts by mass of copper tailings, 450 parts by mass of water and 1.4 parts by mass of grinding aid are mixed and placed in a wet mill at a speed of 430 RPS to wet grind to a median particle size of 70nm to obtain nano copper tailings;

[0030] 2) Get 50 parts by mass of 2.5% (g / mL) chitosan solution and put it into a 300r / min electromagnetic stirrer, add 10 parts by mass of 0.3mol / L glutaraldehyde solution during stirring, Stir in a constant temperature water bath for 10 minutes;

[0031] 3) Add 8 parts by mass of the nano-copper tailings in step 1) to the solution in step 2) and continue the constant temperature water bath for 1 hour, freeze-dry for 24 hours to obtain the anti-cracking-self-healing-root-blocking functional additive for concrete.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an anti-crack-self-healing-root-blocking functional additive for concrete, comprising the following steps: step 1, mixing copper tailings, water and grinding aids and placing them in a wet mill to obtain Nano-copper tailings; step 2, get chitosan solution and put it into an electromagnetic stirrer, add glutaraldehyde solution during stirring, and stir in a warm water bath for 10min; step 3, take 5 min of nano-copper tailings in step 1 ‑10 parts by mass were added to the solution in step 2 and continued in a constant temperature water bath for 1 hour, and freeze-dried for 24 hours to obtain an anti-crack-self-healing-root-blocking functional additive for concrete. When the concrete structure cracks and produces micro-cracks, the water absorption rate of chitosan superabsorbent resin in a neutral environment is greatly increased, and it quickly absorbs water and swells to seal the pores, so as to achieve the purpose of concrete self-healing.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a preparation method of an anti-cracking-self-healing-root-blocking functional additive for concrete. Background technique [0002] With the acceleration of urbanization and the rapid development of industrialization in our country, government departments in many cities attach great importance to the construction of roof greening to solve the problems of increasing urban construction area and the increasingly serious "urban heat island" effect. Roof greening refers to the greening of the tops, roofs and terraces of various buildings and structures that are not connected to the natural soil layer. The greening of the roof helps to increase the urban green area and improve the urban ecological environment. At present, most of the green roofs in my country use organic flexible component root-blocking materials. The later maintenance costs are high, and it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/38C04B18/12C04B24/00C04B103/30
CPCC04B40/0039C04B2103/0068C04B18/12C04B24/38C04B24/008C04B2103/302Y02W30/91
Inventor 杨进王福龙贺行洋苏英王铁唐袁珍于肖雷
Owner HUBEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com