Synthetic leather article and method for preparing the same

A technology for synthetic leather and products, applied in synthetic resin layered products, chemical instruments and methods, layered products, etc., to achieve the effect of excellent delamination resistance

Pending Publication Date: 2021-06-25
DOW GLOBAL TECH LLC
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, externally emulsified PUD is known so far as a candidate material for the preparation of PU matrix, but there is no report on the use of externally emulsified PUD for surface layer in ecological process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic leather article and method for preparing the same
  • Synthetic leather article and method for preparing the same
  • Synthetic leather article and method for preparing the same

Examples

Experimental program
Comparison scheme
Effect test

example

[0088] Some embodiments of the invention will now be described in the following examples, in which all parts and percentages are by weight unless otherwise indicated.

[0089] Information on the raw materials used in the examples is listed in Table 1 below:

[0090] Table 1. Raw materials

[0091]

[0092] By adding the isocyanate prepolymer shown in Table 1 (Voralast TM GE 143ISO) was combined with the raw materials listed in Table 2 (ie, component (Bii)) to prepare 2K non-solvent PU foam.

[0093] Table 2. Raw materials used in 2K PU composites (component (Bii))

[0094]

example 1

[0096] In this example, a synthetic leather was prepared by directly adhering an externally emulsified aliphatic polyurethane dispersion as a skin layer on a 2k PU foam layer, and a high peel strength was achieved.

[0097] 1) Preparation of isocyanate prepolymer of polyurethane particles in PUD:

[0098] Voranol 9287A (70 g) and MPEG1000 (2 g) were charged into a 250 ml three-necked flask and dehydrated at 110° C. and 76 mmHg vacuum for one hour, and then naturally cooled to about 73° C. IPDI (28 g) was poured into the dehydrated polyol mixture at about 73°C under nitrogen flow and mechanical stirring. Catalyst T120 (0.03 g) was then added to the reactants. The reaction was continued at about 73°C for one hour, and then the temperature was raised to about 83°C to continue the reaction for an additional 2.5 hours. The product (prepolymer) was packaged in a plastic bottle and sealed and stored under nitrogen protection. NCO% was measured to be 7.0 wt%.

[0099] 2) Preparati...

example 2

[0107] In this example, a synthetic leather was prepared by directly adhering an externally emulsified aromatic polyurethane dispersion as a skin layer on a 2k PU foam layer, and a high peel strength was achieved.

[0108] 1) Manufacture of synthetic leather

[0109] With 5g of color masterbatch and 1g of RM825 thickener, 94g of externally emulsified aromatic PUD, Syntegra YS3000 provided by Dow Chemical Company was formulated and mixed at 2500rpm for 4.5 minute. The formulated PUD was coated on release paper to a wet film thickness of 150 μm. The coated release paper was dried in an oven at 120° C. for 5 minutes. The release liner with the dry PU skin was removed from the oven and allowed to cool to ambient temperature.

[0110] The formulated 2k PU composite with the formulation of the polyol formulation and Voralast*GE 143ISO in Table 2 was coated on the dry PU skin opposite the release paper to a wet film thickness of 300 μm. Put the coated release paper in an oven at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to view more

Abstract

A synthetic leather article comprising a top coating derived from externally emulsified PUD and a 2K non-solvent PU foam is provided. The leather article exhibits high delamination resistance while retaining superior mechanical properties and appearance comparable with those derived from the organic solvent-based PU. A method for preparing the synthetic leather article is also provided.

Description

technical field [0001] The present disclosure relates to a synthetic leather article and a method for its preparation, in particular a multilayer synthetic leather article based on the combination of a 2K non-solvent polyurethane matrix and an externally stabilized polyurethane skin disposed thereon. Background technique [0002] Synthetic leather finds a wide variety of applications in people's everyday lives, from clothing, footwear, bags and luggage, home decorations to car seats. Synthetic leather offers similar properties and feel to natural leather at a cost advantage. Synthetic leather is manufactured by coating polymers on or impregnating polymers into fabric substrates, and the most commonly used polymer is polyurethane. The traditional process is performed with solutions of polyurethane resins in volatile organic solvents such as dimethylformamide (DMF), methyl ethyl ketone (MEK) and toluene. The porous structure of PU is produced by introducing the coated or imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/12D06N3/14B32B27/40B32B27/18C08G18/42C08G18/76
CPCD06N3/14C08G18/7671C08G18/10C08G18/485C08G18/283C08G18/755C08G18/242C08J9/365C08G18/3271C08G18/632C08G18/4829C08G18/4072C08G18/3206C08G18/6674C08G18/6564C08G18/2063C08G18/165C08G18/4812C08G2101/00C08G2110/0066C08G2110/0083C08L75/08C08J9/283C08J2201/0504C08J9/30C08J2375/04C08J2475/08D06N3/0086D06N3/145C08G18/63C08G18/48C08G18/40B32B27/18B32B27/40C08G18/42C08G18/76C08J2375/08B32B2255/102B32B5/18B32B2255/26B32B2266/0278
Inventor 邰向阳张朝熊家文R·德鲁姆赖特
Owner DOW GLOBAL TECH LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products