Solar glass panel with honeycomb-shaped colored tempered coating, production method of solar glass panel and colored solar photovoltaic module

A technology of solar glass and a production method, which is applied in the field of solar photovoltaics, can solve problems such as being unable to be used on the outer surface of photovoltaic module glass, low light transmittance of inorganic coatings, and no practical application value, so as to reduce the probability of burning photovoltaic modules, Excellent outdoor weather resistance and the effect of widening the range of color choices

Active Publication Date: 2021-07-09
杭州玻美文化艺术有限公司
View PDF12 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of low-temperature color coating is that the hardness of the coating is low, the weather resistance is poor, and the friction resistance is poor. It cannot be used on the outer surface of the glass of photovoltaic modules. surface decoration
[0010] Traditional high-temperature tempered glass coatings are mainly composed of inorganic pigments and glass fluxes, both of which are inorganic components, with outstanding advantages and obvious disadvantages
The advantages are strong hiding power, good weather resistance, good decoration, the same high hardness as tempered glass, the surface coating cannot be scraped off by a knife, and excellent impact resistance. It is suitable for the outer surface decoration of photovoltaic glass and can withstand wind, sand and The impact of objects such as hail; the disadvantage is that the light transmittance of the inorganic coating is very low, and some tempered coatings are not transparent at all, and the light transmittance is only a few percent at the highest. When used for the decoration of colored solar glass panels, the photoelectricity of photovoltaic modules Conversion efficiency is almost zero, no practical application value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solar glass panel with honeycomb-shaped colored tempered coating, production method of solar glass panel and colored solar photovoltaic module
  • Solar glass panel with honeycomb-shaped colored tempered coating, production method of solar glass panel and colored solar photovoltaic module
  • Solar glass panel with honeycomb-shaped colored tempered coating, production method of solar glass panel and colored solar photovoltaic module

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Golden honeycomb tempered UV coating formula (mass percentage of raw materials):

[0062]

[0063]

[0064] Stir and dissolve the B-3310 and IBOA in the above formula at 60-80°C to form a homogeneous liquid, mix with the other components evenly to obtain a colored UV coating, and print the above UV coating with a 200-mesh screen to obtain a thickness of 20 Micron color coating; UV light curing, irradiation energy 600 mJ / cm2; use a green laser with a wavelength of 532 nm and a power of 10 watts to drill holes at an angle of 45 degrees to the glass, with a diameter of 15 microns, and the area of ​​the hole and the coating The ratio is 10%; the punched glass is directly sent into a tempering furnace for tempering (780-820°C / 220 seconds), and a golden honeycomb tempered glass coating is obtained. Viewed from a distance, it is golden glass with uniform color, but viewed from a close distance, there are many oblique light-transmitting small holes on the surface. The phy...

Embodiment 2

[0066] Blue honeycomb tempered UV coating formula (mass percentage of raw materials):

[0067]

[0068] Stir and dissolve the B-3131 polymer and HDDA in the above formula at 60-80°C to form a homogeneous liquid, mix with the other components evenly to obtain a colored UV coating, and print the above UV coating with a 200-mesh screen to obtain Thickness 18 micron blue coating. The UV light curing energy is 1100 mJ / cm2, and the green laser with a wavelength of 532 nm and a power of 10 watts is used to drill holes at an angle of 45 degrees to the glass. The hole diameter is 15 microns, and the ratio of the hole to the coating area is 20%. The glass is directly sent into the tempering furnace for tempering (780-820°C / 220 seconds), and the blue honeycomb tempered glass coating is obtained. It is uniform blue glass when viewed from a distance, and there are many oblique light transmissions on the surface when viewed closely. For small holes, measure physical and chemical indicat...

Embodiment 3

[0070] White honeycomb tempered UV coating formula (mass percentage of raw materials):

[0071]

[0072] Stir and dissolve the B-3131 polymer and IBOMA in the above formula at 60-80°C to form a homogeneous liquid, and mix with the rest of the components evenly to obtain a colored UV coating; screen the above UV coating with a 200-mesh screen to obtain a thickness of 20 microns Color coating. UV light curing, irradiation energy 1500 mJ / cm2. A green laser with a wavelength of 532 nanometers and a power of 10 watts is used to drill holes at an angle of 45 degrees to the glass. The hole diameter is 15 microns, and the ratio of the hole to the coating area is 25%. The perforated glass is sent directly to the tempering furnace for tempering (780-820°C / 220 seconds), and a white honeycomb color tempered glass panel is obtained. It is white glass with uniform color when viewed from a distance, and there are many inclinations on the surface when viewed from a close distance. Light-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a solar glass panel with a honeycomb-shaped colored tempered coating, a production method of the solar glass panel and a colored solar photovoltaic module. The production method comprises the following steps: coating a photovoltaic glass panel with a UV colored tempered coating, and preheating the photovoltaic glass panel; after preheating, adopting ultraviolet light for irradiating the UV colored tempered coating; obliquely punching or scribing the preliminarily-cured UV colored tempered coating by adopting a laser beam so as to enable the UV colored tempered coating to form a honeycomb structure; performing high-temperature tempering on the perforated UV colored tempered coating to form the solar glass panel with the honeycomb-shaped colored tempered coating. The UV colored tempered coating comprises the following raw materials in percentage by mass: 8-25% of a thermoplastic polymer, 10-25% of a low-viscosity photoactive diluent, 1-3% of a photosensitizer, 50-65% of a transparent glass flux, 0.1-15% of an inorganic pigment and 0.01-3% of a leveling agent. The coating of the solar glass panel provided by the invention is excellent in shock resistance and has relatively high light transmittance.

Description

technical field [0001] The invention relates to the field of solar photovoltaics, in particular to a solar glass panel with a honeycomb colored tempered coating, a production method thereof, and a colored solar photovoltaic module. Background technique [0002] Vigorously developing solar photovoltaic power generation is one of the important paths to reduce carbon emissions and achieve carbon neutrality. [0003] Silicon solar photovoltaic cells occupy the mainstream of the market. The traditional structure of silicon solar photovoltaic cells is composed of photovoltaic glass, photovoltaic adhesive film, monocrystalline silicon or polycrystalline silicon solar cells, photovoltaic adhesive film and photovoltaic backplane from the outside to the inside, and is fixed with an aluminum alloy frame. [0004] Since monocrystalline silicon or polycrystalline silicon solar cells are dark blue or black, silicon solar photovoltaic cells are also dark in color. [0005] Distributed so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D5/36C03C17/00C03C17/32H01L31/0216
CPCC09D4/06C09D5/36C03C17/009C03C17/32H01L31/02168Y02E10/50
Inventor 何平
Owner 杭州玻美文化艺术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap