Flame-retardant brush wire

A technology of flame-retardant brush filaments and flame retardants, which is applied in the manufacture of fire-resistant and flame-retardant filaments, the manufacture of rayon, and the addition of pigments to spinning liquids, etc., which can solve the problems of unfavorable storage, transportation and use, high price, and unfavorable use. And other issues

Pending Publication Date: 2022-01-04
广州明晖新材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional brush filaments are plant fibers or animal hairs, which are not conducive to use because plant fibers or animal hairs are easily damaged, deformed and relatively high in price.
Therefore, plastic products are usually used, but plastic products are flammable and produce a large amount of pollutants when burned, which is not conducive to storage, transportation and use. Therefore, in consideration of environmental protection and safety performance, it is necessary to design a flame-retardant brush filament to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A flame-retardant brush filament, comprising the following raw materials in parts by weight:

[0032] 27-34 parts of polybutylene terephthalate fiber, 7-11 parts of epoxy resin, 1-3 parts of zinc hydroxystannate, 2-3 parts of antimony trioxide, 4-6 parts of nano-zinc oxide, plasticizer 1-2 parts of crosslinking agent, 8-12 parts of aminopropyltriethoxysilane, 6-8 parts of aminopropyltrimethylaminosilane, 1-2 parts of toughening agent and 5 parts of flame retardant -8 servings.

[0033] Polybutylene terephthalate fiber and epoxy resin are the main base materials, which ensure the performance of brush filaments in all aspects. The further addition of oxysilane and aminopropyltrimethylaminosilane can further improve the performance of the brush filament, and with the addition of flame retardants, it can further ensure the flame retardancy and fire suppression performance of the brush filament, and improve the environmental protection and safety of the brush filament. . ...

Embodiment 2

[0040] A flame-retardant brush filament, comprising the following raw materials in parts by weight:

[0041] 28 parts of polybutylene terephthalate fiber, 7 parts of epoxy resin, 1 part of zinc hydroxystannate, 2 parts of antimony trioxide, 4 parts of nano-zinc oxide, 1.2 parts of plasticizer, 1.1 parts of crosslinking agent, 8.4 parts of aminopropyltriethoxysilane, 6.2 parts of aminopropyltrimethylaminosilane, 1.1 parts of toughening agent and 5 parts of flame retardant.

Embodiment 3

[0043] A flame-retardant brush filament, comprising the following raw materials in parts by weight:

[0044] 30 parts of polybutylene terephthalate fiber, 8.8 parts of epoxy resin, 2.3 parts of zinc hydroxystannate, 2.1 parts of antimony trioxide, 5 parts of nano-zinc oxide, 1.5 parts of plasticizer, 1.4 parts of crosslinking agent, 9.5 parts of aminopropyltriethoxysilane, 7.2 parts of aminopropyltrimethylaminosilane, 1.6 parts of toughening agent and 6.8 parts of flame retardant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retardant brush wire. The flame-retardant brush wire comprises the following raw materials in parts by weight of 27-34 parts of polybutylene terephthalate fibers, 7-11 parts of epoxy resin, 1-3 parts of zinc hydroxystannate, 2-3 parts of antimony trioxide, 4-6 parts of nano-zinc oxide, 1-2 parts of a plasticizer, 1-2 parts of a cross-linking agent, 8-12 parts of aminopropyltriethoxysilane, 6-8 parts of aminopropyltrimethylamino silane, 1-2 parts of a toughening agent and 5-8 parts of a flame retardant. According to the invention, the polybutylene terephthalate fiber and the epoxy resin are used as main base materials, so that the performance of the brush wire in all aspects is ensured; meanwhile, the zinc hydroxystannate, the antimony trioxide, the nano-zinc oxide, the aminopropyltriethoxysilane and the aminopropyltrimethylamino silane are further added, so that the performance of the brush wire can be further improved; and the flame retardant is added, so that the flame-retardant and combustion suppression properties of the brush wire are further ensured, and the environmental protection and safety of the brush wire in use are improved.

Description

technical field [0001] The invention relates to the field of brush filaments, in particular to a flame-retardant brush filament. Background technique [0002] A brush is a daily tool for cleaning and cleaning. It mainly consists of a combination of brush filaments, brush discs and brush rods. Since the brush filaments are in direct contact with the object to be cleaned, the material selection and performance of the brush filaments are related to the service life of the brush. cleaning efficiency. [0003] Traditional brush filaments are plant fibers or animal hairs, which are not conducive to use because plant fibers or animal hairs are easily damaged, deformed and relatively expensive. Therefore, plastic products are usually used, but plastic products are flammable and produce a large amount of pollutants when burned, which is not conducive to storage, transportation and use. Therefore, in consideration of environmental protection and safety performance, it is necessary to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/14D01F8/16D01F1/04D01F1/07D01F1/10
CPCD01F8/14D01F8/16D01F1/04D01F1/07D01F1/10D01F1/106
Inventor 黄家屏
Owner 广州明晖新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products