Part powder outlet hole repairing method in powder laying printing

A repair method and powder-spreading technology, applied in welding equipment, laser welding equipment, metal processing equipment, etc., can solve problems such as substandard and inability to weld welding quality

Pending Publication Date: 2022-01-11
TSC LASER TECH DEV BEIJING CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for repairing the powder outlet hole of a part in powder laying and printing, which is used to solve the probl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Part powder outlet hole repairing method in powder laying printing
  • Part powder outlet hole repairing method in powder laying printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In order to make the technical problems, technical solutions and beneficial effects to be solved by the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0025] It should be noted that when an element is referred to as being “fixed” or “disposed on” another element, it may be directly on the other element or be indirectly on the other element. When an element is referred to as being "connected to" another element, it can be directly connected to the other element or indirectly connected to the other element.

[0026] In addition, the terms "first" and "second" are used for descriptive purposes only, and cannot be interpreted as indicating or implying relative importance or implicitly specifying the quantity of indic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a part powder outlet hole repairing method in powder laying printing, and relates to the technical field of 3D printing. The problem that in traditional powder outlet hole repairing, due to the gas reverse phenomenon generated in welding of a last powder outlet hole, welding cannot be conducted or the welding quality does not reach the standard is solved. The part powder outlet hole repairing method in powder laying printing comprises the steps that a powder laying printing sample piece and a blocking piece are included, a powder outlet hole is formed in the sample piece, and the powder outlet hole is matched with the blocking piece in shape and size; and laser welding is conducted on the sample piece and the blocking piece under the vacuum environment, and the blocking piece blocks the powder outlet hole. The part powder outlet hole repairing method in powder laying printing is used for repairing work of the part powder outlet hole in 3D powder laying printing.

Description

technical field [0001] The invention relates to the technical field of powder coating 3D printing, in particular to a method for repairing powder outlet holes of parts in powder coating printing. Background technique [0002] In powder laying 3D printing, according to the design requirements of parts, some parts with structures such as internal cavity flow channels, support ribs or weight-reducing slots need to reserve powder outlet holes during the powder laying printing process to facilitate the processing of the parts. Perform powder cleaning operation, and some parts need to ensure the airtightness of the internal structure in structural design. Under this design requirement, the repair of the powder outlet hole after printing has become a major problem. At present, the main method for repairing the powder outlet hole is argon arc welding. Parts, argon arc welding needs argon protection on the back of the weld, so at least one powder outlet hole must be reserved for arg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K26/22B23K26/70
CPCB23K26/22B23K26/702
Inventor 相泽锋孙雪莹李广生李澄刘斌李宁
Owner TSC LASER TECH DEV BEIJING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products