Electric spark deposition preparation method of self-lubricating coating containing tantalum oxide

A self-lubricating coating and electric spark deposition technology, which is applied in the field of EDM deposition to achieve the effects of excellent anti-friction and wear resistance, improved mechanical properties, and simple preparation process

Active Publication Date: 2022-02-25
SHENYANG LIGONG UNIV
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to provide a method for preparing a self-lubricating coating containing tantalum oxide by electric spark deposition. The obtained self-lubricating coating can solve the problem of friction and wear on the surface of a steel base material in a friction and wear environment, and ensure the safety and security of steel components. Efficient operation reduces production and maintenance costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric spark deposition preparation method of self-lubricating coating containing tantalum oxide
  • Electric spark deposition preparation method of self-lubricating coating containing tantalum oxide
  • Electric spark deposition preparation method of self-lubricating coating containing tantalum oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] In this embodiment, the base material is CrNi3MoVA steel, the electrode is pure tantalum, and the preparation steps of the tantalum self-lubricating coating are as follows:

[0038] (1) Firstly, the substrate material is polished step by step according to 240#, 400#, 600#, and 800# sandpaper to remove the oxide film on the surface of the substrate, and then polish it with an abrasive paste with a particle size of 2.5 μm, and then perform ultrasonic cleaning with acetone for 10 minutes to remove surface oil;

[0039] (2) First process the pure tantalum electrode into a columnar shape of Φ4mm×50mm, and grind it step by step according to 240#, 400#, 600#, 800# sandpaper to remove the oxide film on the surface of the substrate, and then use the abrasive paste with a particle size of 2.5μm Polishing, followed by ultrasonic cleaning with acetone for 10 minutes to remove surface oil;

[0040] (3) EDM deposition was carried out under argon protection. The specific process para...

Embodiment 2

[0050] In this embodiment, No. 45 steel is used as the base material, pure tantalum is used as the electrode, and the preparation steps of the self-lubricating coating are as follows:

[0051] (1) Firstly, the substrate material is polished step by step according to 240#, 400#, 600#, 800# sandpaper to remove the oxide film on the surface of the substrate, then polish it with a grinding paste with a particle size of 2.5 μm, and then perform ultrasonic cleaning with acetone for 8 minutes to remove surface oil;

[0052] (2) First process the pure tantalum electrode into a columnar shape of Φ3mm×50mm, and grind it step by step according to 240#, 400#, 600#, 800# sandpaper to remove the oxide film on the surface of the substrate, and then use the abrasive paste with a particle size of 2.5μm Polishing, followed by ultrasonic cleaning with acetone for 8 minutes to remove surface oil;

[0053] (3) EDM deposition is carried out under the protection of argon gas. The specific process p...

Embodiment 3

[0057] In this embodiment, the base material is Q235 steel, the electrode is pure tantalum, and the self-lubricating coating preparation steps are as follows:

[0058] (1) Firstly, the substrate material is polished step by step according to 240#, 400#, 600#, 800# sandpaper to remove the oxide film on the surface of the substrate, then polish it with an abrasive paste with a particle size of 2.5 μm, and then perform ultrasonic cleaning with acetone for 9 minutes to remove surface oil;

[0059] (2) First process the pure tantalum electrode into a Φ5mm×40mm column, and grind it step by step according to 240#, 400#, 600#, 800# sandpaper to remove the oxide film on the surface of the substrate, and then use the abrasive paste with a particle size of 2.5μm Polishing, followed by ultrasonic cleaning with acetone for 9 minutes to remove surface oil;

[0060] (3) EDM deposition was carried out under argon protection. The specific process parameters were: output power 1200W, output vo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of preparation of an anti-wear coating on the surface of a steel member, and particularly relates to an electric spark deposition preparation method of a self-lubricating coating containing tantalum oxide. Steel is adopted as a base body material, a pure tantalum electrode is adopted as an electric spark deposition electrode, and a self-lubricating coating containing tantalum oxide is deposited on the surface of a steel base body by adopting an electric spark deposition technology. The self-lubricating coating and a steel substrate are metallurgically bonded with a strong bonding force, and tantalum oxide enhances the hardness of the self-lubricating coating so that the self-lubricating coating has better antifriction and wear-resistant effects, and the problem of wear of the surface of a steel member in a frictional wear environment can be solved.

Description

technical field [0001] The invention relates to the field of preparation of wear-resistant coatings on the surface of steel components, in particular to a method for preparing pure tantalum electrodes for self-lubricating coatings containing tantalum oxide strengthening phases by electric spark deposition, which can be applied to the realization of steel parts The surface coating has a significant anti-friction and wear-resisting effect on the surface of the part. Background technique [0002] Surface wear can lead to premature failure of equipment components, thereby affecting the normal operation of the entire equipment. In highly industrialized countries, friction and wear cause a large amount of economic losses, accounting for about 1 to 2% of GDP. Therefore, it is of great significance to improve the friction and wear properties of the surface of key component materials. [0003] Coating technology has been widely used to improve the surface properties of metal compon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C26/02
CPCC23C26/02
Inventor 王子君郭策安张新颖梁振刚柳泉张健
Owner SHENYANG LIGONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap