Large-thickness quenched and tempered Q690E/F high-strength steel and manufacturing method thereof

A technology of Q690E, manufacturing method, applied in the field of metallurgy, to achieve the effect of good application prospects, good strength and toughness, and excellent atmospheric corrosion resistance

Active Publication Date: 2022-03-01
MINMETALS YINGKOU MEDIUM PLATE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] To sum up, in the prior art, large-thickness quenched and tempered Q690E/F high-stren

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Large-thickness quenched and tempered Q690E/F high-strength steel and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1

[0029] A large thickness tension Q690E / F high strength steel plate thickness is 100 mm, and the composition of the chemical composition of the steel sheet and the mass content of the mass: C: 0.1%, Si: 0.4%, Mn: 1.4%, P: 0.009%, S : 0.003%, Al: 0.015%, Nb: 0.035%, Ni: 0.5%, B: 0.0008%, Ti: 0.008%, Cr: 0.4%, MO: 0.5%, Cu: 0.25%, N: 0.002%, H : 0.0015%, the margin is Fe and inevitable impurities, CEV = 0.57%.

[0030] The production steps and process parameters of the steel sheet are:

[0031] 1, smelting: LF refining time is 40min, RH vacuum processing time is 15 min;

[0032] 2, continuous casting: overheating 10 ° C, the thickness of the casting is 328 mm, the puller is 0.7m / min, the center segregation C: None;

[0033] 3, heating: heating section maximum heating temperature 1230 ° C, warm segment temperature 1220 ° C, total heating time of the slab in the heating furnace 280min;

[0034] 4, rolling and cooling: two-stage controlled rolling process in the r...

Example Embodiment

[0037] Example 2

[0038] A large thickness tension Q690E / F high strength steel plate thickness is 110 mm, the chemical composition composition of steel sheets and the percentage of the mass: C: 0.12%, Si: 0.38%, MN: 1.45%, P: 0.010%, S : 0.002%, Al: 0.020%, Nb: 0.025%, Ni: 0.45%, B: 0.0008%, Ti: 0.02%, Cr: 0.45%, MO: 0.4%, Cu: 0.35%, N: 0.001%, H : 0.0014%, the margin is Fe and inevitable impurities, CEV = 0.58.

[0039] The production steps and process parameters of the steel sheet are:

[0040] 1, smelting: LF refining time 45min, RH vacuum processing time is 12 minutes;

[0041] 2, continuous casting: overheating 12 ° C, the thickness of the mold is 328 mm, the puller is 0.7 m / min, the center segregation C: 0.5;

[0042] 3, heating: heating section maximum heating temperature 1240 ° C, warm segment temperature 1210 ° C, the total heating time of the slab in the heating furnace is 300 min;

[0043] 4, rolling and cooling: two-stage controlled rolling process in the recrystall...

Example Embodiment

[0046] Example 3

[0047] A large thickness tension Q690E / F high strength steel plate thickness is 120 mm, and the composition of the chemical composition of steel sheets and the mass content of: C: 0.13%, Si: 0.35%, Mn: 1.5%, P: 0.008%, S 0.002%, Al: 0.025%, Nb: 0.028%, Ni: 0.42%, B: 0.0025%, Ti: 0.01%, Cr: 0.42%, MO: 0.42%, Cu: 0.28%, N: 0.002%, H : 0.0012%, margin is Fe and inevitable impurities, CEV = 0.59.

[0048] The production steps and process parameters of the steel sheet are:

[0049] 1, smelting: LF refining time 48min, RH vacuum processing time is 15 min;

[0050] 2, continuous casting: overheating 18 ° C, the thickness of the mold is 328 mm, the puller is 0.7 m / min, the center segregation C class: 1.0;

[0051] 3, heating: heating section maximum heating temperature 1240 ° C, warm section temperature 1230 ° C, total heating time of the slab in the heating furnace is 310min;

[0052] 4, rolling and cooling: two-stage controlled rolling process by re-crystallizatio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Impact energyaaaaaaaaaa
Login to view more

Abstract

The invention discloses a large-thickness quenched and tempered Q690E/F high-strength steel plate and a manufacturing method thereof. The manufacturing method comprises the steps of smelting, continuous casting, heating, rolling, cooling and heat treatment. The steel plate comprises the following components in percentage by weight: 0.11 to 0.14 percent of C, 0.25 to 0.4 percent of Si, 1.4 to 1.55 percent of Mn, less than or equal to 0.015 percent of P, less than or equal to 0.003 percent of S, 0.015 to 0.035 percent of Al, 0.020 to 0.035 percent of Nb, 0.4 to 0.5 percent of Ni, 0.0008 to 0.0025 percent of B, 0.008 to 0.02 percent of Ti, 0.4 to 0.45 percent of Cr, 0.4 to 0.5 percent of Mo, 0.25 to 0.35 percent of Cu, less than or equal to 0.0030 percent of N, less than or equal to 0.00015 percent of H and the balance of Fe. The steel plate has high strength, good low-temperature toughness and excellent atmospheric corrosion resistance, and can be used in the fields of engineering machinery, mining, ocean platforms and the like.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a large-thickness quenched and tempered Q690E / F high-strength steel and a manufacturing method thereof. Background technique [0002] High-strength steel is a resource-saving product with high technical content and high added value. High-strength steel of Q690 and above grades has been widely used in construction machinery, mining, crane trucks, offshore platforms, etc. , has the characteristics of simple structure, light weight, high safety, large carrying capacity and long service life. Large-thickness high-strength steels are applied to key parts and play a vital role in the structure of large-scale components. Many domestic steel mills are studying the production process of large-thickness Q690 and above high-strength steels, but for adjustments with a thickness ≥100mm The quality of Q690 high-strength steel is less researched, and it is even more rare to meet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/42C22C38/44C22C38/48C22C38/50C22C38/54C22C38/58B22D11/12B22D11/18B22D11/22C21C7/10C21D8/02C22C33/04
CPCC22C38/02C22C38/04C22C38/06C22C38/58C22C38/48C22C38/54C22C38/50C22C38/44C22C38/42C22C38/001C22C33/04C21D8/0205C21D8/0226C21D8/0263C21C7/10B22D11/225B22D11/18B22D11/1206
Inventor 张德勇李新宇李伟许继勇杨志强冯仰峰曲之国马林欧阳宇杨清山宋继强王博马鑫邴纯于涛
Owner MINMETALS YINGKOU MEDIUM PLATE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products