Making process of woven ceramic product of zirconia flexibilized alumina ceramic

A technology of alumina ceramics and a manufacturing method, which is applied in the manufacture of zirconia toughened alumina ceramic textile parts, can solve the problem that the wear resistance cannot meet the requirements of high-speed spinning machines, etc., and achieves improved fracture toughness, good wear resistance and high wear resistance. The effect of shear strength

Inactive Publication Date: 2005-07-20
上海施迈尔精密陶瓷有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]At present, the textile parts of textile machinery, such as spinning guide wires, shearing parts, etc., are mostly made of metal. The wear resistance of this metal spinning Can not meet the requirements of high-speed spinning machine

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Making process of woven ceramic product of zirconia flexibilized alumina ceramic
  • Making process of woven ceramic product of zirconia flexibilized alumina ceramic
  • Making process of woven ceramic product of zirconia flexibilized alumina ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Now take the small-sized wire guide as an example to illustrate the manufacturing method of the present invention.

[0021] The manufacture method of the zirconia toughened alumina ceramic textile porcelain of the present invention comprises the following steps:

[0022] (1), select the raw material and weigh each component raw material according to the weight percentage of the raw material, and grind it into powder through a ball mill, and its particle size is controlled below 2 μm;

[0023] (2), add binder and mix and stir to form compound;

[0024] (3), the mixture is molded into a textile porcelain body by injection molding or isostatic pressing;

[0025] (4) Appropriate finishing and processing after drying, including turning, cutting and drilling;

[0026] (5), high temperature sintering;

[0027] (6) Finally, grinding and polishing are carried out to form textile porcelain pieces.

[0028]

ingredients

Wt%

example 1

Example 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
Login to View More

Abstract

The production process of ceramic product of zirconia flexibilized alumina ceramic for textile use includes: weighing material and grinding into powder in a ball mill; adding adhesive and mixing into mixed material; forming biscuit; trimming; high temperature sintering; and final polishing. The ceramic product for textile use has high wear resistance and shearing strength and long service life and its use can improve the quality of fiber and textile.

Description

Technical field: [0001] The invention relates to textile pieces, in particular to a method for manufacturing a zirconia toughened alumina ceramic textile piece. Background technique: [0002] At present, the textile parts of textile machinery, such as spinning guide wires, shearing parts, etc., are mostly made of metal. The wear resistance of such metal spinning parts cannot meet the requirements of high-speed spinning machines. Invention content: [0003] The technical problem to be solved by the present invention is to overcome the defects of existing metal textiles, and provide a method for manufacturing zirconia toughened alumina ceramic textiles, so as to meet the performance requirements of high-speed spinning machines for textiles. [0004] Technical solution of the present invention is as follows: [0005] A method for manufacturing a zirconia toughened alumina ceramic textile piece, comprising the following steps: [0006] (1), select the raw material and weigh ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/119C04B35/622C04B35/632
Inventor 李广仁张万林杨文生李功正唐源生
Owner 上海施迈尔精密陶瓷有限公司