Anode aluminium foil etching process for electrolytic capacitor

A technology of electrolytic capacitors and anode aluminum foil, which is applied in the manufacture of electrolytic capacitors, capacitors, capacitors, etc., can solve the problems of reduced mechanical strength, insufficient hole density, uneven distribution of corrosion holes, etc., and achieve good mechanical strength, easy uniform pitting, The effect of increasing the corrosion expansion rate

Inactive Publication Date: 2007-08-22
RUYUAN YAO AUTONOMOUS COUNTY DONGYANGGUANG FORMED FOIL CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing pretreatment process is to immerse the aluminum foil directly in an acid or alkali solution for a few minutes at a certain temperature. This treatment removes the oil and oxide film on the surface of the aluminum foil and also dissolves the impurity elements on the surface of the aluminum foil that are conducive to pores, causing corrosion. Uneven distribution of pores, insufficient density of pores and reduced mechanical strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] In Example 1, after immersing the aluminum foil in a pretreatment solution with a temperature of 40°C and a concentration of 5.0wt% NaOH+0.005wt% ZnO for 120 seconds, the usual pre-etch, post-etch and post-treatment are performed.

Embodiment 2

[0011] Example 2 is to heat the aluminum foil at a temperature of 80°C and a concentration of 5.0wt%H 2 SO 4 +0.005wt%PbO pre-treatment solution soaked for 120 seconds, then the usual pre-etch, post-etch and post-treatment.

Embodiment 3

[0012] Embodiment 3 is that the aluminum foil is heated at a temperature of 70°C and a concentration of 5.0wt%H 3 PO 4 +0.005wt% ZnO pre-treatment solution soaked for 120 seconds, and then the usual pre-etch, post-etch and post-treatment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The etching process of anode aluminum foil for electrolytic capacitor includes one pre-treatment step. The pretreating solution is solution of alkali, acid or their mixture with Zn and / or Pb compound in 0.0001-1.0 wt% added. Aluminum foil is soaked in the pretreating solution for 10-300 sec, and owing to the separation of Zn and / or Pb, the aluminum foil surface becomes more easy in producing homogeneous spot etching in the fore etching process, and this results in raised area expanding rate, specific capacitance and tensile strength of the aluminum foil.

Description

technical field [0001] The invention relates to a metal corrosion process, in particular to a pretreatment method for an electrolytic capacitor anode aluminum foil corrosion process. Background technique [0002] Aluminum foil for electrolytic capacitor anode, in order to expand its effective surface area and increase the electrostatic capacity (specific capacity) per unit area, is generally subjected to chemical or electrochemical corrosion treatment to form high-density uniformly distributed corrosion pits with a certain depth on the surface. Thereby increasing the surface area of ​​the aluminum foil. The corrosion process generally includes the following steps: pre-treatment, pre-corrosion, post-corrosion, and post-treatment. Pre-treatment is a variety of physical and chemical treatments before electro-etching the light foil. Its main function is to remove oil, impurities and natural oxide film on the surface of the aluminum foil, adjust the structure of the aluminum foi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/055H01G9/045H01G13/00
Inventor 吕根品罗向平吴志坚
Owner RUYUAN YAO AUTONOMOUS COUNTY DONGYANGGUANG FORMED FOIL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com