A polyorganosiloxane and sealing material technology, applied in chemical instruments and methods, and other chemical processes, can solve the problems of complex synthesis, increased cost of polyorganosiloxane sealing materials, and many steps, and achieve simple preparation process , Strong adhesion and stable performance

Inactive Publication Date: 2005-05-11
ZHEJIANG UNIV
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the synthesis is complicated and there are many steps, whic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polysiloxane sealing material with modified surface and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Introduce 20.6 grams of N-β-aminoethyl-γ-aminopropylmethyldimethoxysilane and 50 milliliters of toluene into a three-necked flask equipped with a stirrer, and the moisture in the mixture gradually dissolves by azeotroping for 30 minutes. Removed, and then 28.8 grams of oleic acid was added dropwise with a dropping funnel. The set temperature is 100°C, and dry nitrogen gas is fed into it. After three hours of reaction, the mixture is sampled and analyzed by infrared absorption spectrum (IR), and it is found that the characteristic absorption peak of the carboxyl group disappears, and a new amido group absorption peak is formed. The reaction is thus complete. The IR spectrum is shown in figure 1 . The brown transparent liquid obtained by heating and distilling low boilers is the viscosity-increasing additive of the present invention.

[0036] Mix 100 parts (viscosity of 20000mPa.s) of hydroxyl-terminated polydimethylsiloxane and 80 parts of nano-active calcium carbonat...

Embodiment 2

[0047] 0.5 g of the thickening additive synthesized in Example 1 was mixed with 10 g of hydroxyl-terminated polydimethylsiloxane with a viscosity of 3000 mPa.s. The appearance of the resulting mixture was visually evaluated: the mixture was white turbid but slightly transparent, and when the mixture was left at room temperature for 3 days, its appearance was almost completely unchanged from the new mixture.

Embodiment 3

[0052] 22.2 grams of N-β-aminoethyl-γ-aminopropyltrimethoxysilane and 50 milliliters of toluene were imported into a three-necked flask equipped with a stirrer, and the moisture in the mixture was gradually removed by azeotropic 30 minutes, and then 27.8 g of oleic acid was added dropwise with a dropping funnel. The temperature is set at 100° C., and dry nitrogen is passed through. After reacting for three hours, the viscosity-increasing additive of the present invention is obtained by heating and distilling low boilers.

[0053] Mix 100 parts (viscosity: 5000mPa.s) of hydroxyl-terminated polydimethylsiloxane and 100 parts of nano-active calcium carbonate treated with stearic acid under vacuum-tight condition of 0.1-1kPa, and then add 3 parts of tackifying additives, 6 parts of methyltrimethoxysilane, 0.2 parts of tetrabutyl titanate. Mix evenly, and vacuum remove air bubbles to obtain the surface-modifiable polyorganosiloxane sealing material of the present invention.

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an organic siloxane polymer sealing material that can make surface finished. The weight percent of the composition is: organic siloxane polymer 100, filler 5-200, the cross linker 0.1-20, the catalytic agent 0.01-10, and tackifier 0.1-10. It is produced by: mixing the above materials in a vacuum condition to get product. The material is non-noxious to environment and human. The process is easy and the product is stable and has great adhesion strength to all kinds of paints.

Description

technical field [0001] The invention relates to a surface modifiable polyorganosiloxane sealing material and a preparation method thereof. Background technique [0002] Silicone material is a new type of polymer synthetic material, which has excellent physical and chemical properties such as UV resistance, ozone resistance, heat resistance, low temperature flexibility, etc., and has good adhesion to the substrate, convenient construction, and fast curing speed. , has been widely used in the field of construction, especially as a building sealing material and caulking material has obvious advantages. However, as building sealing materials and caulking materials, it is often required to be coated with decorative and (or) protective coatings on its surface, while traditional polyorganosiloxane sealing materials have very low surface energy and surface tension. The cohesive force of this kind of paint and latex paint coating is small, and the surface coating is difficult. To i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/14C09K3/10
Inventor 郑强陈永兴胡洪国林薇薇
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap