Composite materials with polyvinyl/anhydrite for producing corrugated piping material with double walls

A double-wall corrugated pipe, polyvinyl chloride technology, applied in the direction of pipes/pipe joints/pipes, pipes, rigid pipes, etc., can solve the problems of unsatisfactory mechanical properties and poor compatibility of materials

Inactive Publication Date: 2006-08-16
安徽恒泰非金属材料科技有限责任公司
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, it is mainly used in the field of building materials, and when used as a filling material for organic resins, due to the lack of chemical modification of the anhydrite surface, the compatibility between the anhydrite and the matrix is ​​poor, and the mechanical properties of the material are not ideal. did not attract widespread attention from researchers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Add two kilograms of 1250 mesh anhydrite into a high-speed mixer, add 31 grams of stearic acid at the same time, heat up to 100°C with high-speed stirring, and take out after 5 minutes at a constant temperature to obtain modified anhydrite; PVC: modified anhydrite : CPE: Tri-salt and di-salt compound stabilizer: Sodium stearate was mixed in a high-speed mixer for 5 minutes at a ratio of 100: 35: 14: 5.7: 5, and then taken out after being mixed on two rollers for 5 minutes, Then, it was molded on a flat vulcanizer with a pressure of 10 MPa to obtain composite material 1#. The test results of its mechanical properties are shown in Table 1.

Embodiment 2

[0017] Add two kilograms of 1250 mesh anhydrite into a high-speed mixer, add 30 grams of aluminate coupling agent, stir at a high speed and heat up to 100 ° C, and take out after 5 minutes of constant temperature to obtain modified anhydrite; PVC: modified Anhydrite:CPE:Tri-salt-disalt composite stabilizer:PE wax in a high-speed mixer at a ratio of 100:45:15:6:4, mixed for 5 minutes, and taken out, mixed on a double roller for 5 minutes, taken off, Then, it was molded on a flat vulcanizer with a pressure of 10 MPa to obtain composite material 2#. The test results of its mechanical properties are shown in Table 1.

Embodiment 3

[0019] Add two kilograms of 1250 mesh anhydrite into the high-speed mixer, add 33 grams of titanate coupling agent at the same time, heat up to 100°C with high-speed stirring, and take out after 5 minutes of constant temperature to obtain the modified anhydrite; PVC: modified The anhydrite: CPE: tri-salt disalt compound stabilizer: calcium stearate was mixed in a high-speed mixer for 5 minutes at a ratio of 100: 37: 16: 6: 4.5 and taken out, and mixed on two rollers for 5 minutes. Take it off, and then shape it on a flat vulcanizer with a pressure of 10MPa to obtain a composite material 3#. The test results of its mechanical properties are shown in Table 1.

[0020] serial number

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A polyvinyl chloride / anhydrite composite material for producing double-wall corrugated piping material can be used for drainage, blow-down of agriculture and industry, telecommunication and agricultural irrigation. It uses medical modified anhydrite as filler, has better compatibility for anhydrite and carrier resin and good high-pressure-resistant and anti-impact performances.

Description

Technical field: [0001] The invention relates to a composite material for preparing double-wall corrugated pipes by filling anhydrite into polyvinyl chloride. Background technique: [0002] As an inorganic mineral material, anhydrite has abundant resources in my country. At present, it is mainly used in the field of building materials, but when it is used as a filling material for organic resins, because there is no chemical modification on the surface of anhydrite, the compatibility between anhydrite and the matrix is ​​poor, and the mechanical properties of the material are not ideal. It has not attracted widespread attention from researchers. Invention content: [0003] The invention provides a kind of polyvinyl chloride / hard gypsum for preparing double-wall corrugated pipes, which widely uses anhydrite whose surface is chemically modified as filler to enhance the compatibility of anhydrite and carrier resin and improve material performance. Gypsum composite. [0004...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K3/30F16L9/133C08L23/04C08L33/04C08L23/08C08L55/02
Inventor 徐卫兵刘敏周正发温德力王道俊李宏武潘静懿卢尚琨
Owner 安徽恒泰非金属材料科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap