Prepn and application of ethyl diisopropyl carboxylate

A technology of ethyl diisopropyl carboxylate and diisopropyl malonate, which is applied in the preparation and application fields of ethyl diisopropyl carboxylate, can solve the problems of environmental pollution, long process, and emission It can achieve the effect of mild reaction conditions, simple post-treatment process and short reaction time.

Inactive Publication Date: 2007-06-06
JINGGANGSHAN UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional synthesis method of citrate plasticizers is to use citric acid and corresponding alcohols in the presence of sulfuric acid as a catalyst. Currently, the raw material citric acid is mainly prepared by microbial fermentation. This method has a long process, especially for producing A large amount of organic pollutants and solid wastes, these pollutants not only pollute the environment, but also discharge a large amount
Therefore, environmental problems have long been the main factor restricting the development of the citric acid industry, which in turn has affected the widespread promotion and application of citric acid ester plasticizers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prepn and application of ethyl diisopropyl carboxylate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1) Add diisopropyl malonate to the ethanol solution of 19.0% sodium ethoxide by mass percentage under stirring, the molar ratio of diisopropyl malonate to sodium ethoxide is 1:1.05, heat up to 85°C and react for 25 minute;

[0028] 2) add catalyst potassium iodide, the mass ratio of potassium iodide and diisopropyl malonate is 1: 130;

[0029] 3) Ethyl bromoacetate was added dropwise, the molar ratio of ethyl bromoacetate to diisopropyl malonate was 1.01:1, the addition time was 25 minutes, reacted at 85°C for 4 hours, and cooled to room temperature;

[0030] 4) adding water to dissolve the separated inorganic salts, separating the oil layer and distilling under reduced pressure to collect products in the boiling point range, while reclaiming unreacted raw materials and solvent ethanol. The yield was 87% based on diisopropyl malonate.

Embodiment 2

[0032] 1) Add the methanol solution of 19.5% sodium methoxide to diisopropyl malonate under stirring, the molar ratio of diisopropyl malonate to sodium methoxide is 1:1.1, heat up to 80°C and react for 20 minute;

[0033] 2) adding catalyst elemental iodine, the mass ratio of elemental iodine to diisopropyl malonate is 1: 180;

[0034] 3) Ethyl chloroacetate was added dropwise, the molar ratio of ethyl chloroacetate to diisopropyl malonate was 1.02:1, the time for the addition was 20 minutes, reacted at 80°C for 9 hours, and cooled to room temperature;

[0035] 4) filter the separated out inorganic salt, distill under reduced pressure, collect the product of boiling point range, reclaim unreacted raw material and solvent methanol simultaneously. The yield was 85% based on diisopropyl malonate.

Embodiment 3

[0037] 1) Add diisopropyl malonate to 20.0% sodium ethoxide ethanol solution with a mass percentage concentration of 20.0% under stirring, the molar ratio of diisopropyl malonate to sodium ethoxide is 1:1.08, heat up to 75°C and react for 20 minute;

[0038] 2) add catalyst elemental iodine, the mass ratio of elemental iodine and diisopropyl malonate is 1: 200;

[0039] 3) Ethyl chloroacetate was added dropwise, the molar ratio of ethyl chloroacetate to diisopropyl malonate was 1.02:1, the time for the addition was 30 minutes, reacted at 80°C for 10 hours, and cooled to room temperature;

[0040] 4) filter the separated out inorganic salt, distill under reduced pressure, collect the product of boiling point range, reclaim unreacted raw material and solvent ethanol simultaneously. The yield was 87% based on diisopropyl malonate.

[0041] Examples of the application of EDETC as a plastic plasticizer are as follows:

[0042] After mixing polyvinyl chloride (PVC) powder, EDETC,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is preparation process and application of ethyl diisopropyl carboxylate. Diisopropyl malonate and ethyl chloroacetate as the initial material are one-step reacted under the action of strong alkali and catalyst to synthesize ethyl diisopropyl carboxylate. After reaction, the reaction product is filtered, water washed to eliminate inorganic salt and decompression distilled to obtain the product. Ethyl diisopropyl carboxylate is colorless or yellowish transparent liquid, and has structure similar to that of tri citrate, plasticizing efficiency and cold resistance similar to that of DOP and compatibility higher than that of DOP. The present invention is used as plasticizer.

Description

technical field [0001] The invention relates to a preparation method and application of ethyl diisopropyl carboxylate. Background technique [0002] With the improvement of environmental protection awareness in various countries in the world, plastic products such as medicine and food packaging, daily necessities, toys, etc. have put forward higher purity and sanitation requirements for the main plasticizer dioctyl phthalate DOP. DOP has a potential carcinogenic risk, and international measures have been taken to limit the scope of use of DOP: the U.S. Environmental Protection Agency has stopped the use of six phthalate plasticizers according to the research results of the National Cancer Institute. Industrial production; the Swiss government has decided to ban the use of DOP in children's toys; Germany has banned the use of DOP in all plastic products related to the human body and hygienic food; in Japan, DOP as a plastic additive is limited to industrial plastic products. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C07C69/34C07C67/00C07C67/333C08K5/11
Inventor 隋岩曾锡瑞李新发方小牛
Owner JINGGANGSHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com