Method for producing cigarette connection paper by transfer method

A production method and technology of tipping paper, which are applied in the field of cigarette production, can solve the problems of rough surface, limitation of the exquisiteness of characters and patterns, unclear display of characters and patterns, etc., achieve fine surface, clear outline of patterns, and improve quality Effect

Inactive Publication Date: 2007-06-27
江苏卫星新材料股份有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, cigarette tipping papers are produced in various forms in the domestic market. In recent years, tipping papers for gilded cigarettes have developed rapidly. Compared with ordinary cigarette tipping papers, gilding cigarette tipping papers have obvious advantages, and are more and more popular. More and more cigarette factories are using it, but the delicacy of the stamped text and patterns on the hot stamping cigarette tipping paper is still limited by technical conditions
Hot stamping cigarette tipping paper may still have a rough surface, especially in the process of hot stamping small text, patterns, and patterns, and the text and patterns cannot be displayed clearly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing cigarette connection paper by transfer method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] As shown in the figure, the production method of tipping paper for cigarettes by transfer method comprises the following steps in turn:

[0014] 1) Coat the release layer on one side of the base film made of BOPP material, the coating material is water wax, and the thickness of the release layer is 0.6g / m 2 ; In practice, the base film thickness can be 12 μm, 16 μm, 17 μm, 21 μm, etc.

[0015] 2) After the release layer is dried, apply a colored layer on its surface. The material to be applied is a mixture of resin and pigment, wherein the resin content is not less than 60% of the total mass of the mixture (that is, the resin content is 60% of the mass of the mixture- 100%), the thickness of the painted layer is 3.5g / m 2 .

[0016] 3) After drying, aluminum-plate the surface of the color layer in a vacuum aluminum-coating machine, and keep the vacuum at 0.5×10 -3 Pa, the aluminum wire with a purity of 99.99% is atomized and sprayed onto the surface of the color layer...

Embodiment 2

[0019] The production method of tipping paper for cigarettes by transfer method comprises the following steps in sequence:

[0020] 1) Coat the release layer on one side of the base film made of BOPP material, the coating material is water wax, and the thickness of the release layer is 0.8g / m 2 ; The thickness of the basement film is 16 μm.

[0021] 2) After the release layer is dried, apply a colored layer on its surface. The material to be applied is a mixture of resin and pigment, wherein the resin content is 80%, and the thickness of the applied color layer is 3g / m 2 .

[0022] 3) After drying, aluminum-plate the surface of the color layer in a vacuum aluminum-coating machine, and keep the vacuum at 1×10 -3 Pa, the aluminum wire with a purity of 99.99% is atomized and sprayed onto the surface of the color layer, so that the aluminum wire and the color layer are bonded to form an aluminum-coated layer, and the thickness of the aluminum-coated layer is 75 μm.

[0023] 4),...

Embodiment 3

[0025] The production method of tipping paper for cigarettes by transfer method comprises the following steps in sequence:

[0026] 1) Coat the release layer on one side of the base film made of BOPP material, the coating material is water wax, and the thickness of the release layer is 0.7g / m 2 ; The thickness of the basement film is 21 μm.

[0027] 2) After the release layer is dried, apply a colored layer on its surface. The material to be applied is a mixture of resin and pigment, wherein the mass content of the resin is 95%, and the thickness of the applied colored layer is 4g / m 2 .

[0028] 3) After drying, aluminum-plate the surface of the color layer in a vacuum aluminum-coating machine, and keep the vacuum at 1.5×10 -3 Pa, the aluminum wire with a purity of 99.99% is atomized and sprayed on the surface of the color layer, so that the aluminum wire and the color layer are bonded to form an aluminum-coated layer, and the thickness of the aluminum-coated layer is 100 μm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A technology for making the packing paper of cigarette by transfer method includes such steps as providing a film substrate, sequentially coating parting layer and color layer, plating aluminum layer, and transferring said plated aluminum layer and color layer onto the raw paper for cigarette.

Description

technical field [0001] The invention relates to the production technology of cigarettes, in particular to a production method of tipping paper for cigarettes. Background technique [0002] At present, cigarette tipping papers are produced in various forms in the domestic market. In recent years, tipping papers for gilded cigarettes have developed rapidly. Compared with ordinary cigarette tipping papers, gilding cigarette tipping papers have obvious advantages, and are more and more popular. More and more cigarette factories are using it, but the delicacy of the printed text and patterns on the hot stamping cigarette tipping paper is still limited by technical conditions. Hot stamping cigarette tipping paper may still have a rough surface, especially during the process of hot stamping small text, patterns, and patterns, the text and patterns cannot be displayed clearly. Contents of the invention [0003] The object of the present invention is to provide a production method...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/08D21H27/18B32B29/00
Inventor 张爱兵
Owner 江苏卫星新材料股份有限公司