Bicomponent strengthening system for paper

a technology of bicomponents and strengthening systems, applied in papermaking, non-fibrous pulp addition, reinforcing agent addition, etc., can solve the problem that wet strength agents should not prevent bath tissue from disintegrating

Inactive Publication Date: 2006-03-30
GARNIER GIL B D +6
View PDF55 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0014] The bicomponent strengthening system of the present invention may be adjusted so as to provide either temporary or permanent wet strength to a paper web. For instance, the bicomponent strengthening system may provide temporary wet strength to a paper web such that the paper web may have less than about 70% of the initial wet tensile index remaining after soaking in water for about one hour. In one embodiment, the paper web may have less than about 60% of the initial wet tensile index remaining after soaking in water for about one hour. For example, in one embodiment, the bicomponent strengthening s

Problems solved by technology

When added to bath tissues, however, the wet strength agents should not prevent the ba

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bicomponent strengthening system for paper

Examples

Experimental program
Comparison scheme
Effect test

example 1

Control—The Effect of Catiofast®, Parez®, and Kymene® on Wet Strength Development

Preparation of Pulp Slurry

[0129] To prepare a pulp slurry, 24 grams (oven-dry basis) of pulp fibers were soaked in 2 liters of deionized water for 5 minutes. The pulp slurry was disintegrated for 5 minutes in a British disintegrator. The slurry was then diluted with water to a volume of 8 liters. The strength agent was then added to the slurry. The slurry was mixed with a standard mechanical mixer at moderate shear for 10 minutes after addition of the strength agent.

Preparation of Handsheets

[0130] Handsheets were made with a basis weight of 60 gsm. During handsheet formation, the appropriate amount of fiber (0.3% consistency) slurry required to make a 60 gsm sheet was measured into a graduated cylinder. The slurry was then poured from the graduated cylinder into an 8.5-inch by 8.5-inch Valley handsheet mold (Valley Laboratory Equipment, Voith, Inc.) that had been pre-filled to the appropriate leve...

example 2

Effect of pH and Order of Addition on PVAm / Cationic Parez Bicomponent

[0133] A slurry of pulp fibers as described in Example 1 was prepared. A bicomponent strength system was formed in the slurry which included the following compounds: [0134] 1% aqueous solution of CParez® 631NC (a cationic glyoxylated polyacrylamide) manufactured by Cytec Industries [0135] 1% aqueous solution of Catiofast® PR 8106 polyvinylamine

[0136] Polyvinylamine and CParez® were added sequentially with add-on levels constant at 10 Kg / T each. The first polymer was added to the furnish and stirred for 10 minutes. The second polymer was then added to the furnish and mixed 2 minutes. Handsheets were prepared as in Example 1 and tested. Results (average of 5 samples) are given in Table 2. No additives were used in the control. The pH of the pulp furnish was adjusted as shown below in Table 2 prior to the addition of the polymers.

TABLE 2Tensile data for handsheets treated with polyvinylamine / cationic Parez.Effect ...

example 3

Polyvinylamine / Cationic Parez® Bicomponent Strength Agents—Effect of Polymer Ratio and Polyvinylamine Charge Density

[0138] A slurry of pulp fibers as described in Example 1 was prepared. A bicomponent strength system was formed in the slurry which included the following compounds: [0139] 1% aqueous solution of CParez® 631NC (a cationic glyoxylated polyacrylamide) manufactured by Cytec Industries [0140] 1% aqueous solution of polyvinylamine

[0141] Polyvinylamine and CParez® were added sequentially with add-on levels constant at 10 Kg / T each. CParez® was added first to the furnish and stirred for 10 minutes. The polyvinylamine was then added to the furnish and mixed 2 minutes. Three types of PVAm were used: Catiofast® PR 8106 (90% amine, 21 m-eq amine / g polymer), Catiofast® PR 8087 (50% amine, 11 me-q / g), and Catiofast® 8104 (10% amine, 2.3 m-eq / g). The total polymer concentration added to the furnish equaled 10 kg / T of dry fiber. The weight ratio of PVAm / CParez® was varied from 0:1,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fractionaaaaaaaaaa
Fractionaaaaaaaaaa
Timeaaaaaaaaaa
Login to view more

Abstract

The present invention is directed to a bicomponent strengthening system and the paper webs produced with the bicomponent strengthening system. Through use of the strengthening system, paper webs may be produced in which the strength characteristics of the web may be specifically tailored. The first component of the system comprises a polymer having at least about 1.5 m-eq primary amine functionality per gram of polymer and a molecular weight of at least about 10,000 Daltons. The second component may be either a polymeric anionic compound or a polymeric aldehyde functional compound. For example, the polyamine polymer component may be a polyvinylamine or polysaccharide having primary amine functionality. In one embodiment, the second component may be a cationic polymeric aldehyde functional compound. For example, the second component may be a cationic glyoxylated polyacrylamide. In another embodiment, the second component may be a polymeric anionic compound comprising carboxy functionality.

Description

BACKGROUND OF THE INVENTION [0001] In the art of tissue making and papermaking in general, many additives have been proposed for specific purposes, such as increasing wet strength, improving softness, or control of wetting properties. For instance, in the past, wet strength agents have been added to paper products in order to increase the strength or otherwise control the properties of the product when contacted with water and / or when used in a wet environment. For example, wet strength agents are added to paper towels so that the paper towel may be used to wipe and scrub surfaces after being wetted without the towel disintegrating. Wet strength agents are also added to facial tissues to prevent the tissues from tearing when contacting fluids. In some applications, wet strength agents are also added to bath tissues to provide strength to the tissues during use. When added to bath tissues, however, the wet strength agents should not prevent the bath tissue from disintegrating when dr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H21/20D21H17/20D21H17/37D21H17/42D21H17/56D21H23/04D21H23/10
CPCD21H17/20D21H17/37D21H23/04D21H17/56D21H17/71D21H17/42D21H21/20
Inventor GARNIER, GIL B. D.LINDSAY, JEFFREY D.SHANNON, THOMAS G.LOSTOCCO, MICHAEL R.HANSEN, LACEYBRANHAM, KELLY D.SIDERIUS, DAN
Owner GARNIER GIL B D
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap