Dental adhesive compositions and methods

a technology of dental adhesives and compositions, applied in dental prosthetics, dental impression caps, dentistry, etc., can solve the problem of not achieving adhesion with confiden

Inactive Publication Date: 2007-12-27
SANG JUNJIE +2
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is apparent that it takes time in many bonding steps to accomplish such handling and that no adhesion with confidence is attained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

1P-SEA Example 1

[0091] A mixture comprising 3.3 parts by weight of 4-methacryloxyethyltrimellitic anhydride (4-META), 13.3 parts by weight of dipentaerythritol pentaacrylate phosphoric acid ester (PENTA), 6.7 parts by weight of 3-(acryloyloxy)-2-hydroxypropyl methacrylate (AHPMA), 3.3 parts by weight of triethyleneglycoldimethacrylate (TEGMA), 10.9 parts by weight of 1,6-Bis(methacryloyloxyethoxycarbonylamino)-2,4,4-trimethylhexane (UDMA), 1.7 parts by weight of trimethylolpropane trimethacrylate (TMPTMA), 1.7 parts by weight of diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide, 0.13 part by weight of butylated hydroxytoluene, 42.3 parts by weight of acetone and 16.7 parts by weight of deionized water were prepared. The dentin and enamel bond strength was measured 22.4 MPa and 33.8 MPa, respectively. The thermal cycled (1800 cycle, between 55 / 5° C.) composite to dentin and enamel bond strength was measured 25.5 MPa and 25.9 MPa, respectively, without separate etching step. The more ex...

example 2

1P-SEA Example 2

[0092] A mixture comprising 25.0 parts by weight of dipentaerythritol pentaacrylate phosphoric acid ester (PENTA), 7.9 parts by weight of 3-(acryloyloxy)-2-hydroxypropyl methacrylate (AHPMA), 5.5 parts by weight of 2-hydroxyethyl methacrylate (HEMA), 10.9 parts by weight of 1,6-Bis(methacryloyloxyethoxycarbonylamino)-2,4,4-trimethylhexane (UDMA), 1.7 parts by weight of trimethylolpropane trimethacrylate (TMPTMA), 1.7 parts by weight of diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide, 0.13 part by weight of butylated hydroxytoluene, 42.3 parts by weight of acetone and 16.7 parts by weight of deionized water were prepared. The dentin and enamel bond strength was measured 21.4 MPa and 26.3 MPa, respectively. The thermal cycled (1800 cycle, between 55 / 5° C.) composite to dentin and enamel bond strength was measured 21.1 MPa and 28.3 MPa, respectively, without separate etching step.

example 3

1P-SEA Example 3

[0093] 50° C. Accelerated Storage Stability Test of Two Representative Formulations

TABLE 1SEA formulations and bond strengthFormulationHL2-5HL2-7Component% wt% wtPENTA25.020.04-META03.3AHPMA7.90HEMA03.3UDMA3.59.9TMPTMA1.71.7L-TPO1.71.7BHT0.130.13Acetone41.743.3Water18.316.7SUM100100Dentin SBS0 week 50° C.21.4 (3.9)22.4 (5.2)(MPa):2 week 50° C.17.8 (5.8)14.2 (4.2)mean (SD)3 week 50° C.17.6 (6.4)21.8 (0.7)4 week 50° C. 8.2 (2.2)14.8 (2.1)Enamel SBS0 week 50° C.26.3 (4.6)33.8 (3.1)(MPa):2 week 50° C. 30.6 (11.1)19.7 (3.1)mean (SD)3 week 50° C. 29.4 (12.0)24.2 (9.0)4 week 50° C.14.4 (4.1)12.8 (7.8)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water-miscibleaaaaaaaaaa
bond strengthaaaaaaaaaa
bond strengthaaaaaaaaaa
Login to view more

Abstract

Two-part and one-part self-etching dental adhesives containing polymerizable acidic monomers. Methods include one-coat application without need for tooth etching.

Description

RELATED APPLICATION [0001] This application is a continuation of U.S. patent application Ser. No. 10 / 844,628 having a filing date of May 13, 2004 which claims the benefit of Provisional Application No. 60 / 469,938 filed on May 13, 2003.TECHNICAL FIELD [0002] The present invention generally relates to dental adhesives. More particularly the invention relates to self-etching adhesives. Specifically the invention relates to adhesives containing polymerizable acidic monomers. BACKGROUND OF THE INVENTION [0003] Table of Abbreviations Used Herein AbbreviationFull term4-META4-methacryloxyethyltrimellitic AnhydrideAHPMA3-(Acryloyloxy)2-hydroxypropyl methacrylateBHTButylated HydroxytolueneBMAPBis(2-methacryloxyethyl) phosphateCAFCetylamine HydrofluorideCQCamphorquinoneDHEPTDihydroxylethyl-p-toluidineDMABADimethylaminobenzoic acidDMABNDimethylaminobenzonitrileEDAB4-ethyldimethylaminbenzoateEGMPEthylene glycol methacrylate phosphateHEMA2-Hydroxyethyl methacrylateL-TPODiphenyl (2,4,6-trimethylb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(United States)
IPC IPC(8): C08K3/00A61K6/00A61K6/083
CPCA61K6/0023A61K6/083C08L33/04C08L75/16A61K6/30A61K6/887
Inventor SANG, JUNJIELIU, HUAIBINGWANG, XIULING
Owner SANG JUNJIE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap