Towels of micro fibers of polyester/polyamide bi-components and the method of making

Inactive Publication Date: 2013-07-25
ZIBO UNION PLUSH PRODS +1
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The invention is a towel made of polyester / polyamide bi-components micro fibers that have a plush-like structure on the top sections of the loop piles on at least one side of the towel. This towel is more comfortable to touch, can keep heat, be skin-friendly, have high absorbency, be soft, and be strong. The method of making this towel is simple and effective, and the fabric can be easily implemented.

Problems solved by technology

In addition, traditional towels may lose fibers quickly and may become stiff after being washed.
Therefore, the normal fabric has high frictional drag during usage.
It is not smooth and easily to scratch one's hands, so it gives people an uncomfortable feeling.
Especially when the skin is dry or coarse, the uncomfortable feeling is more prominent.
All these restrict the further development of fabrics made of micro fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Towels of micro fibers of polyester/polyamide bi-components and the method of making
  • Towels of micro fibers of polyester/polyamide bi-components and the method of making

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0026]As shown in FIG. 1, in one embodiment, a towel of polyester / polyamide bi-components micro fibers may be a wrap knitted fabric that has a double-sided base fabric 2 made of polyester / polyamide bi-components micro fibers that are treated by a chemical splitting process. Both sides of the base fabrics 2 may have loop piles 3. The density of the loop piles 3 may be at least 10 per square centimeter. Every loop pile 3 may contain at least 1 single-thread loop. The bottom sections of loop piles 3 are connected to the base fabric 2. A plush-like structure 1 may be made by fracturing loops from the top of the loop piles 3 inwardly to about ⅓ of the thickness of the loop piles 3 from the top of the loop piles 3. All the loop piles 3 may have loops fractured at about the same position. The fractured fibers may form an outward plush-like structure 1. The sanding paper used for the sanding treatment may be 400 grits. The rotation speed of the sand paper may be 1000 rpm, and the speed of f...

example 2

[0029]As shown in FIG. 1, in one embodiment, a towel of polyester / polyamide bi-components micro fibers may be a wrap knitted fabric that has a double-sided base fabric 2 made of polyester / polyamide bi-components micro fibers that are treated by a chemical splitting process. Both sides of the base fabrics 2 may have loop piles 3. The density of the loop piles 3 may be at least 10 per square centimeter. Every loop pile 3 may contain at least 1 single-thread loop. The bottom sections of loop piles 3 are connected to the base fabric 2. Only the loop piles 2 on one side of the base fabrics 2 are sanded. The sanding process may start at the top of the loop piles 3 and moves inwardly to about 1 / 10 of the thickness of the loop piles 3. The fractured loops of the loop piles 3 may form outward plush-like structures 1. The sanding paper used for the sanding treatment may be 500 grits. The rotation speed of the sand paper may be 1200 rpm, and the speed of fabric advancement may be 10 meters per...

example 3

[0034]As shown in FIG. 1, in one embodiment, the loop piles 3 of the both sides of the base fabric 2 may be sanded. On one side, the sanding process may start at the top of the loop piles 3 and moves inwardly to about 5 / 10 of the thickness of the loop piles 3 from the top. The sanding paper used for the sanding treatment may be 300 grits. The rotation speed of the sand paper may be 800 rpm, and the speed of fabric advancement may be 8 meters per minute, and the sanding angle may be 70 degrees. On the other side, the sanding process is started at the top of the loop piles 3 and moves inwardly to about 1 / 10 of the thickness of the loop piles 3. The sanding paper used for the sanding treatment may be 500 grits. The rotation speed of the sand paper may be 1200 rpm, and the speed of fabric advancement may be 10 meters per minute, and the sanding angle may be 5 degrees.

[0035]The advantages of the towels made from the above mentioned method may be that the loop piles on both sides of the b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A fabric with polyester / polyamide bi-components microfibers may include a warp knitted double-sided base fabric with polyester / polyamide bi-components microfibers that is treated by a chemical splitting process. Both sides of the double-sided base fabric may have at least 10 loop piles per square centimeter. Each loop pile may have at least one single thread loop. The bottom of the loop piles may be connected to the base fabric. The loops may be arranged orderly to form a planar structure that has the feature that the loop piles on one side of the base fabric may have plush-like structures at the top sections. The loops may be fractured by sanding the loops with a sand paper of 200-600 grits at about 1 / 10 to 5 / 10 of a thickness of the loop piles to form the plush-like structures.

Description

TECHNICAL FIELD[0001]This invention is related to towels of polyester / polyamide bi-components micro fibers and is in the field of textile fabrics.BACKGROUND[0002]It is well known that the traditional towels are made of natural fibers: for example cotton fibers. Cotton fibers may facilitate the propagation of bacteria and mildew in a humid environment. In addition, traditional towels may lose fibers quickly and may become stiff after being washed.[0003]Micro fibers have the advantages of extra high absorbency, resistance to tinting, resistance to mildew growth, odorless, softness, resistance to color fading, easy to clean after usage, resistance to chlorine bleaching and oxidizing bleaching, etc. They are widely used and have great performance in automobile maintenance, hotel industry, beauty salons, sports products and products for daily use. Examples of products with micro fibers may include towels, shower towels, hair-drying bath hats, facial cleaning cloths, household cleaning cl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D27/00D06C13/00D06C11/00
CPCD04B21/04D06C11/00Y10T428/2395
Inventor SUN, DE MIN
Owner ZIBO UNION PLUSH PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com