One-sided electrode with reduced twisting for a secondary battery, and method for producing same

a secondary battery and electrode technology, applied in the field of one-sided electrodes, can solve the problems of reducing the speed of pressing process, distorted or curled electrode sheets, and the inability of the electrodes located at the lowermost and uppermost ends to contribute to the performance of the cell, so as to improve the convenience of work, improve the efficiency of pressing process, and improve the effect of distortion or curling

Pending Publication Date: 2021-10-28
LG ENERGY SOLUTION LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The solution significantly reduces electrode curling and distortion, enhancing the convenience and productivity of subsequent processes by matching the tensile strength of the electrode distortion-preventing layer with the electrode mixture, thereby improving the manufacturing efficiency of one-sided electrodes.

Problems solved by technology

In the case of the double-sided electrode formed by coating the electrode mixture on both sides of the current collector, when the single electrodes are stacked upward, the electrodes located at the lowermost and uppermost ends do not contribute to the performance of the cell because there is no counter electrode.
On the other hand, in the production of the one-sided electrode, even when the same pressure is applied to the electrode mixture and the current collector in the rolling process, the electrode sheet is distorted or curled toward the current collector due to the difference in elongation rate after rolling.
Accordingly, technologies such as minimizing the rolling rate, increasing the thickness of the current collector, or reducing the speed of the pressing process have been proposed, but these have problem of limiting the performance of the battery or increasing the cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-sided electrode with reduced twisting for a secondary battery, and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0084]A clad metal containing copper and stainless steel was prepared (8 μm+12 μm). Thereafter, an electrode slurry (prepared by mixing LiNi0.55Mn0.30Co0.15O2, Denka black as a conductive material and polyvinylidene fluoride as a binder in a weight ratio of 96:2:2, followed by addition of NMP) was applied on the clad metal to have a thickness of 200 μm. Thereafter, it was dried and rolled to produce a cross-section electrode sheet.

example 2

[0085]Stainless steel having a thickness of 12 μm was laminated on one side of a copper foil having a thickness of 8 μm as a current collector, followed by applying heat and pressure to form an electrode distortion-preventing layer. Thereafter, an electrode slurry (prepared by mixing LiNi0.55Mn0.30Co0.15O2, Denka black as a conductive material and polyvinylidene fluoride as a binder in a weight ratio of 96:2:2, followed by addition of NMP) was applied on the other side of aluminum foil to have a thickness of 200 μm. Thereafter, it was dried and rolled to produce a one-sided electrode sheet.

example 3

[0086]A polypropylene solution was applied to a copper foil having a thickness of 8 μm as a current collector to have a thickness of 12 μm and dried to form an electrode distortion-preventing layer. Thereafter, the electrode slurry was coated to have a thickness of 40 μm, followed by drying and rolling to produce a one-sided electrode sheet.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a one-sided electrode for a secondary battery comprising a current collector, an electrode mixture layer applied to one surface of the current collector, and an electrode distortion-preventing layer formed on the other surface of the current collector to which no electrode mixture is applied. The one-sided electrode according to the present invention exhibits significantly reduced warping or curling after a rolling process and has the advantages of facilitating subsequent processes and enabling enhanced productivity.

Description

[0001]This application is a divisional of a U.S. application Ser. No. 16 / 491,083, filed Sep. 4, 2019, which is a U.S. national stage application pursuant to 35 U.S.C. § 371 of PCT / KR2018 / 012632, filed Oct. 24, 2018, designating the United States, which claims the benefit of priority based on Korean Patent Application No. 10-2017-0139136, filed Oct. 25, 2017. The entire contents of the aforementioned patent applications are incorporated herein by reference.TECHNICAL FIELD[0002]The present invention relates to a one-sided electrode that improves an occurrence of an electrode being distorted or rolled due to a difference in the current collector and the electrode mixture at the time of rolling process when preparing the one-sided electrode, and a method of preparing the same.BACKGROUND ART[0003]As technologies for mobile devices are developed, and demand for the mobile devices increases, there has been a rapid increase in demand for secondary batteries as energy sources. Among such sec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): H01M4/66H01M4/04H01M4/139H01M10/0525
CPCH01M4/667H01M4/0404H01M4/0435H01M4/139H01M2004/027H01M4/668H01M4/669H01M10/0525H01M4/661H01M4/13H01M10/052H01M4/70Y02E60/10Y02P70/50H01M4/0471
Inventor OH, SEI WOONYOON, YEO KYUNGWOO, SUN HWAKJEONG, YU RA
Owner LG ENERGY SOLUTION LTD