Machining process capable of improving punching performance of magnesium alloy plate and belt

A magnesium alloy plate and processing method technology, applied in metal processing and other directions, can solve problems such as unfavorable grain orientation and poor stamping performance, and achieve the effects of simple equipment, high processing efficiency and improved performance

Inactive Publication Date: 2008-01-09
CHONGQING UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem of poor stamping performance caused by the unfavorable grain orientation of the existing magnesium alloy plate and strip, the present invention proposes a processing method for improving the stamping performance of the magnesium alloy plate and strip, using unidirectional multi-pass bending technology to control the magnesium alloy Cold-rolled sheet texture. To achieve the purpose of improving the stamping performance of magnesium alloy sheet and strip

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Machining process capable of improving punching performance of magnesium alloy plate and belt
  • Machining process capable of improving punching performance of magnesium alloy plate and belt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In conjunction with the accompanying drawings 1, the magnesium alloy plate 6 with a thickness of 1.0mm is placed on the fixed bracket 5, the front end of the plate is connected with the flexible belt 8 by the clamp 7, the rear end of the plate is connected with the flexible belt 3 by the clamp 4, and the flexible belt The other end of 8 is fixed on the reel 10 surface. Driven by the motor, the reel 10 moves at a speed of 10m / min. By adjusting the pressure between the pinch roller 1 and the two rollers, the tension on the magnesium alloy plate is controlled to be 30 MPa. After the magnesium alloy sheet 6 is bent for one pass, the motor drives the pinch roller 1 to reverse, and the reel 10 also reverses at the same time, so as to ensure that the magnesium alloy sheet 6 is not under tension during the movement. Repeat the above steps, the number of bending passes is 5. Then it is straightened on a roller leveler, and finally it is fully softened and annealed at 260°C for...

Embodiment 2

[0020] Referring to Fig. 3, the coiled magnesium alloy strip 13 with a thickness of 0.6mm is placed on the uncoiler 12, the front end of the strip crosses over the top of the fixed bracket 5 and is connected to the coiler 14, and the coiler is driven by the motor to drive The magnesium alloy strip moves at a speed of 20 m / min, and the tension on the magnesium alloy strip 13 is adjusted to 40 MPa through the uncoiler 12 and the coiler 14 . After one pass is finished, the coiled material is taken off from the coiler 14, loaded on the uncoiler 12 and repeats the above steps. After 10 bending passes, stress relief annealing was carried out at 135°C for 120min. The arc radius of the contact part between the fixed bracket 5 and the magnesium alloy strip 14 is 1.0mm, and the bending angle of the magnesium alloy strip 13 is 90° when bending, and lubricated by cold rolling lubricating oil. After bending, the yield strength decreased from 172MPa to 120MPa, the yield strength ratio decr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The processing method of improving punching performance of magnesium alloy plate and belt is to bent the magnesium alloy plate or belt fixed on the arced top of fixture by 45-135 deg with tension of 10-60 MPa applied to one end for 5-20 times, and then to straighten and anneal the bent magnesium alloy plate or belt. The said bending process makes the tensile stress of the crystal grains in the bent deformation part in certain angle to the basal plane, makes the basal plane rotate in the tensile stress direction to form some angle to the surface of the plate or belt, reduces base plane texture, obtains ideal texture component and improves the performance of the plate or belt. Therefore, the method of the present invention can lower the yield strength and yield ratio of the plate and the belt, raise the elongation and punching performance of the plate and the belt.

Description

technical field [0001] The invention belongs to the field of plastic processing of non-ferrous metals and relates to performance improvement of magnesium alloy plates and strips. Background technique [0002] Magnesium alloys with a hexagonal close-packed structure are commonly used. When the temperature is lower than 498K, the slip plane is mainly the basal plane {0001}. The slip direction is That is, there is only one main slip surface and two independent slip systems, and the deformation passes through the cone surface twinning, grain boundary slip, etc. to coordinate. During the rolling deformation process, a strong basal texture will be formed in the magnesium alloy sheet. Especially during cold rolling and warm rolling deformation, the magnesium alloy has less slip system and forms a very strong basal texture, and its (0001) basal plane is parallel to the rolling surface. During the recrystallization annealing process of the plate, due to the directional nucleati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P25/00
Inventor 黄光胜黄光杰潘复生
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com