Composition for chemical Cu plating onto timber surface and the chemical Cu plating process

A wood surface, chemical copper plating technology, applied in liquid chemical plating, metal material coating process, coating and other directions, can solve problems such as damage to aesthetics, film aging and cracking, etc., to achieve the effect of enhanced surface decoration effect

Inactive Publication Date: 2009-01-14
BEIJING FORESTRY UNIVERSITY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Over time, the membrane ages and cracks, destroying its aesthetics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Embodiment 1 Basswood surface copper plating

[0057] (1) Wood surface treatment:

[0058] First use 320-grit sandpaper, and then use 800-grit sandpaper to finely sand and clean the surface of the basswood. The wood was then ultrasonically washed with distilled water at 70°C for 10 minutes in an ultrasonic tank with a power of 100 W, and then dried at 35°C for 20 minutes.

[0059] (2) Wood surface stabilization treatment:

[0060] The wood surface treated in step (1) is put into a stable solution composed of 3 parts by weight polyethylene glycol and 5 parts by weight benzyl alcohol, soaked for 10 minutes, cleaned, then dried at a temperature of 60 ° C for 30 minutes, and then put into Immerse in a 0.1% by weight NaOH solution at a temperature of 60°C for 10 minutes, and finally dry at a temperature of 60°C for 30 minutes.

[0061] (3) Wood surface sensitization and activation treatment:

[0062] Put the wood stabilized in step (2) into an ultrasonic water tank, ultr...

Embodiment 2

[0066] Embodiment 2 Copper plating on the surface of elm wood

[0067] (1) Wood surface treatment:

[0068] First use 320-grit sandpaper, and then use 800-grit sandpaper to finely sand and clean the surface of the elm. Then the wood was ultrasonically washed with distilled water at 70°C for 10 minutes in an ultrasonic tank with a power of 150W, and then dried at 35°C for 20 minutes.

[0069] (2) Wood surface stabilization treatment:

[0070] After the surface treatment of step (1), put the wood in a stable solution consisting of 4 parts by weight of polyether and 8 parts by weight of acetone for 10 minutes, then wash it, then dry it for 30 minutes at a temperature of 60 ° C, and then put it in a temperature of 60 ° C. 0.5 wt% NaOH solution for 10 min, and finally dried at 60°C for 30 min.

[0071] (3) Wood surface sensitization and activation treatment:

[0072] Put the wood stabilized in step (2) into an ultrasonic water tank and ultrasonically wash it at room temperature...

Embodiment 3

[0076] Embodiment 3 Catalpa wood surface is copper-plated

[0077] (1) Wood surface treatment:

[0078] First use 320 mesh sandpaper, and then use 800 mesh sandpaper to fine sand the surface of the catalpa wood and clean the surface. Then the wood was ultrasonically washed with distilled water at 65°C for 20 minutes in an ultrasonic tank with a power of 150W, and then dried at 35°C for 30 minutes.

[0079] (2) Wood surface stabilization treatment:

[0080] After the surface treatment of step (1), put the wood in a stable solution consisting of 5 parts by weight of polyketone and 6 parts by weight of ethanol for 15 minutes, then wash it, then dry it for 35 minutes at a temperature of 55 ° C, and then put it in a temperature of 60 ° C. 0.8 wt% NaOH solution for 12 min, and finally dried at 60°C for 30 min.

[0081] (3) Wood surface sensitization and activation treatment:

[0082] Put the wood stabilized in step (2) into an ultrasonic water tank and ultrasonically wash it for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind of composition for chemical copper plating onto timber surface and the chemical copper plating process. The composition contains copper compound, complexing agent and reductant. The chemical copper plating process is to set the timber in the composition solution, so that copper ion is reduced through chemical reaction and deposited homogeneously onto the surface of the timber and the timber surface possesses metal decoration effect and conducting performance. The present invention can reach copper coating thickness over 3.5 microns and square resistivity as low as 0.06 ohm, being comparable with copper foil.

Description

【Technical field】 [0001] The invention relates to an electroless copper plating composition and an electroless copper plating method using the composition. More specifically, the present invention relates to a composition for electroless copper plating on wood surfaces, and a method for electroless copper plating on wood surfaces using the composition. 【Background technique】 [0002] Wood is widely used in every link of national economic development, from people's daily living utensils, furniture, interior decoration and furnishing components to packaging supplies, transportation tools, sports equipment to large buildings, wood plays an important role. The use of wood has witnessed the development of human civilization. [0003] Wooden products for interior furnishings have changed from traditional full functionality to a combination of function and art, so the surface decoration of wood is particularly important. Traditional wood surface decoration is mainly covered by un...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C18/38C23C18/20
Inventor 赵广杰周杲黄金田薛振华薛凤莲符韵林马晓军
Owner BEIJING FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com