Dicyclopentadiene modified unsaturated polyester resin preparation method

A technology of dicyclopentadiene and polyester resin is applied in the field of preparation of dicyclopentadiene-modified unsaturated polyester resin, which can solve the problems of reduced mechanical properties of UPR products, influence of heat resistance of UPR products, etc.

Active Publication Date: 2009-04-29
SINOPEC SHANGHAI PETROCHEMICAL CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the average molecular weight of UPR obtained by this method is too low, and when the molecular weight is too low, many mechanical properties of UPR products will be reduced, especially the heat resistance of UPR products will be greatly affected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dicyclopentadiene modified unsaturated polyester resin preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～8

[0021] Under the protection of nitrogen, 196g of maleic anhydride and the required amount of DCPD were added to a 0.5-liter reactor, and the required amount of catalyst composition phosphoric acid and p-toluenesulfonic acid were added. Stir and heat up, when the temperature rises above 100°C, add 36g of water, control the reaction temperature to 150-170°C, and react for 2 hours. Add the required amount of propylene glycol and glycerin, gradually raise the temperature, and continuously fractionate the water in the system. When the acid value of the reactant is 90-100mgKOH / g, a polymerization inhibitor p-tert-butylcatechol is added, and the amount of the polymerization inhibitor added is 0.01-0.2wt% based on the total amount of the reactant. Continue the reaction, keep it for about half an hour when the reaction temperature rises to 200-205° C., and stop the reaction until the acid value of the reactant is less than 50 mg KOH / g. Cool the reactant to 100-110°C, add the required ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

This invention relates to a method for producing dicyclopentadiene modified unsaturated polyester resin, comprising: 1) unsaturated diacid anhydride, water and dicyclopentadiene perform addition reaction with presence of catalyst to produce dicyclopentadiene ester of unsaturated diacid. The catalyst is a mixture of phosphoric acid and methyl benzene sulfonic acid, wherein the weight ratio of phosphoric acid and methyl benzene sulfonic acid is (2-6):1; 2) add in a mixture of diatomic alcohol and tribasic alcohol to the reaction system to perform polycondensation reaction, finish the reaction till the acidity of the reactants becomes less than 50mgKOH / g, and remove the produced water during the reaction process; 3) cool the reactants to 100-110Deg C, add and homogenously mix the ethenyl crosslinking monomer diluted reactant and polymerization inhibitor to obtain the dicyclopentadiene modified unsaturated polyester resin product. This invention is characterized in that: the obtained UPR product has a superior heat-durability, with heat distortion temperature more than 100Deg C, which is better than the level of current technology.

Description

technical field [0001] The invention relates to a preparation method of dicyclopentadiene modified unsaturated polyester resin. Background technique [0002] Unsaturated polyester resin (UPR) is a thermosetting resin mainly used in the manufacture of FRP. It is generally polycondensed from unsaturated dibasic acid or anhydride and diol to form a polymer, and then the polymer is diluted in vinyl crosslinking monomer Made in. Under the action of curing agent, UPR can manufacture FRP products through various processing methods. UPR has excellent mechanical properties, electrical properties and chemical corrosion resistance, but its disadvantages are high brittleness, low impact resistance, and poor heat resistance. UPR modified with dicyclopentadiene (DCPD) can significantly improve toughness and heat resistance. When DCPD is used to modify unsaturated polyester resin, it is mainly that DCPD is depolymerized into cyclopentadiene (CPD), and then CPD undergoes a diene addition...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/52
Inventor 马洪玺谢家明陈丽华陈洪军
Owner SINOPEC SHANGHAI PETROCHEMICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com