Filling particle for producing foam ferrous metals and production method thereof

A technology of filler particles and ferrous metals, which is applied in the field of filler particles and its production, can solve the problems of difficulty in controlling the uniformity and porosity of the internal pore structure of foamed ferrous metals, and the quality is difficult to meet the ideal requirements, so as to achieve high porosity and uniformity Better, more homogeneous results

Inactive Publication Date: 2009-04-29
TAIYUAN UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the production of foamed stainless steel and other materials at home and abroad is completed by powder foaming process, but the uniformity and porosity of the internal pore structure of foamed ferrous metal produced by powder foaming process is difficult to control, and the quality is difficult to meet the ideal requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] ①, material selection and preparation

[0009] Purchase 1 kg of 75-mesh quartz sand;

[0010] Purchase 1 kg of water glass with a modulus of 2.2;

[0011] Configure 1 kg of 10% solution in water glass and add water to dilute.

[0012] ②. Spray the diluted water glass evenly on the quartz sand, and do directional shaking, so that the quartz sand is bonded together under the action of water glass to form a particle shape of a certain size similar to a sphere.

[0013] ③. Aging at 25°C for 24 hours to harden the spherical particles and have a certain strength, or blow carbon dioxide to the particles to solidify them to have a certain strength.

[0014] ④. Sieve and store particles of different sizes separately for later use.

Embodiment 2

[0016] ①, material selection and preparation

[0017] Purchase 1 kg of 200-mesh quartz sand;

[0018] Purchase 1 kg of water glass with a modulus of 2.9;

[0019] Configure 1 kg of 30% solution in water glass and add water to dilute.

[0020] ②. Spray the diluted water glass evenly on the quartz sand, and do directional shaking, so that the quartz sand is bonded together under the action of water glass to form a particle shape of a certain size similar to a sphere.

[0021] ③. Aging at 25°C for 24 hours to harden the spherical particles to have a certain strength, or to blow carbon dioxide to solidify the spherical particles to have a certain strength.

[0022] ④. Sieve and store particles of different sizes separately for later use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a filling particle of black foam metal and making method in the black foam metal technical domain, which comprises the following steps: blending sodium silicate and quartz sand to form filling particle; spraying sodium silicate solution with water on the quartz sand evenly; swaying directionally; solidifying under certain temperature or through carbon dioxide to possess certain strength; sieving; preparing the particle with fire resistance and easy dissolution; improving void rate of pore structure of black foam metal evenly.

Description

technical field [0001] The invention belongs to the technical field of producing foamed ferrous metal. In particular, it relates to filler particles used for producing foamed ferrous metals by extrusion infiltration technology and a production method thereof. Background technique [0002] At present, the production of foamed stainless steel and other materials at home and abroad is completed by powder foaming process, but the uniformity and porosity of the internal pore structure of foamed ferrous metal produced by powder foaming process is difficult to control, and the quality is difficult to meet the ideal requirements. Contents of the invention [0003] The purpose of the present invention is: to provide a new technical scheme, to provide a new filler particle for the production of foamed ferrous metal by the extrusion seepage process, which can greatly improve the quality of the produced foamed ferrous metal. [0004] The present invention is realized in the following...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/00B22D25/00B22D23/04
Inventor 任建富
Owner TAIYUAN UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com