Nano lubricating oil additive

A lubricating oil additive and lubricating oil technology, applied in the direction of additives, lubricating compositions, petroleum industry, etc., can solve the problems of increased user cost, large usage, affecting use function and industrial application, etc., and can repair wear and scratches Surface, extended service life, excellent anti-friction and anti-wear effects

Inactive Publication Date: 2009-12-09
BEIJING SIBNANO TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has good dispersibility, extreme pressure performance and anti-wear performance, but its disadvantage is that the lubricating oil additive contains 0.1-50% dispersant and 0.1-30% synergist, based on the same reason as above , the existence of the dispersant and synergist of the additive has seriously affected its use function and industrial application; in addition, the usage amount of the lubricating oil additive is also very large, being 1-10% of the total amount of lubricating oil, resulting in increase in user costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano lubricating oil additive
  • Nano lubricating oil additive
  • Nano lubricating oil additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] The mechanism of action of the nano lubricating oil additive of the present invention:

[0045] Firstly, the repair and anti-wear performance and mechanism of oil-soluble nano-copper (or nano-copper alloy) and reactive nano-silica were analyzed respectively, and then the oil-soluble nano-copper (or nano-copper alloy) and reactive nano-silica were analyzed. The action mechanism of the nano lubricating oil additive composed of silicon of the present invention is analyzed.

[0046] (1) Repair and anti-wear performance and mechanism analysis of oil-soluble nano-copper (sports car experiment):

[0047]Add 30ml of oil-soluble nano-copper to 3L of SP series gasoline engine lubricating oil produced by Beijing Sunshine Lubricating Oil Co., Ltd., a Sino-US joint venture, and mix evenly. After the gasoline engine has been working normally for about half a month, take out the connecting rod bush for analysis , and compared with the connecting rod bearing of the SP series lubricati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a nano lubricating oil additive. The lubricating oil additive mainly consists of oil-soluble nano-copper or oil-soluble nano-copper alloy and oil-soluble nano-silicon dioxide. Using the lubricating oil additive of the present invention can realize the self-repair of the worn part, and has the functions of fuel saving, anti-wear, noise reduction, carbon deposition reduction, power improvement and the like. The lubricating oil additive of the present invention can be well dispersed in various lubricating oil base oils, has good oxidation stability, can exist stably for a long time, and is suitable for solving the friction, wear and maintenance of various mechanical equipment under various working conditions question.

Description

technical field [0001] The invention relates to a nano lubricating oil additive, in particular to a novel lubricating oil additive containing oil-soluble nano copper or nano copper alloy and reactive nano silicon dioxide. Background technique [0002] Lubricants are an integral part of machinery operation and maintenance. With the increasing load, speed, temperature and other working parameters of modern mechanical equipment, the original friction reducer and antiwear agent in lubricating oil can no longer fully meet the requirements of its antifriction and antiwear performance. Since the 1990s, with the in-depth research on nanomaterials and technologies, it has been found that nanoparticles have shown many excellent tribological properties in the field of lubrication. The friction and anti-wear performance has been greatly improved, and a new solution has been opened up for the long-term unsolved problems in the field of lubricating oil. [0003] There are many researche...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M125/26C10M125/04C10N20/06
Inventor 许伟李小红
Owner BEIJING SIBNANO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products