Low-odour acrylonitrile-butadiene-styrene copolymer complex

A technology of styrene copolymer and acrylonitrile, which is applied in the field of preparation of the composite material, can solve the problems that the impact performance of the material is greatly affected and has no practical value, and achieve low cost, low odor characteristics, and excellent physical and chemical properties. Effect

Active Publication Date: 2010-01-13
CHONGQNG PRET NEW MATERIAL +2
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, through practice, we found that the addition of this mixture has a great influence on the basic physical and mechanical properties of ABS materials, especially the impact properties of the material, so it does not have great practical value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Dry blend ABS100, molecular sieve material 3, antioxidant 168 0.25, and antioxidant 245 0.25 in a high-speed mixer for 3-5 minutes, and then melt-extrude in a twin-screw extruder and granulate. It is: 200-210°C in the first zone, 210-220°C in the second zone, 210-220°C in the third zone, 205-215°C in the fourth zone; the residence time is 1-2 minutes, and the pressure is 12-18Mpa.

Embodiment 2

[0044] Dry mix ABS100, molecular sieve material 2, antioxidant 168 0.25, and antioxidant 245 0.25 in a high-speed mixer for 3-5 minutes, and then melt-extrude in a twin-screw extruder and granulate. It is: 200-210°C in the first zone, 210-220°C in the second zone, 210-220°C in the third zone, 205-215°C in the fourth zone; the residence time is 1-2 minutes, and the pressure is 12-18Mpa.

Embodiment 3

[0046] Dry mix ABS100, molecular sieve material 1, antioxidant 168 0.25, and antioxidant 245 0.25 in a high-speed mixer for 3-5 minutes, and then melt-extrude in a twin-screw extruder and granulate. It is: 200-210°C in the first zone, 210-220°C in the second zone, 210-220°C in the third zone, 205-215°C in the fourth zone; the residence time is 1-2 minutes, and the pressure is 12-18Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed is a low-odour acrylonitrile-butadiene-styrene copolymer complex comprising the raw materials (by weight ratio) of ABS 100 and molecular sieve material 0.001-0.01, toughening agent 0-5, anti-oxidant 0.2-2.0, ultraviolet light absorbent 0-2.0, free radical quenching agent 0-2.0, pigment and lubricating agent 0-5.0, wherein the molecular sieve material being a alkali metal aluminosilicate powder of sodium type crystal structure with the chemical formula of Na86[(AlO2)86(SiO2)106]*XH2O, the toughening agent being a high colloid AB comprising rubber 50-70 wt%, acrylic nitrile 5-20 wt%, phenylethene 25-30 wt%.

Description

technical field [0001] The invention relates to a low-odor styrene-acrylonitrile copolymer, and more particularly relates to preparing a low-odor styrene-acrylonitrile copolymer by adding an odor inhibitor that can effectively suppress the unpleasant smell in polypropylene composite materials. Acrylonitrile copolymer. The invention also relates to a method for preparing the composite material. Background technique [0002] Styrene acrylonitrile copolymer, namely ABS (acrylnitrole-butadiene-styrene copolymer), is a copolymer of acrylonitrile-butadiene-styrene, which is the most developed and changed variety among styrene series resins. Due to the advanced performance Compared with other resins, ABS has undoubted advantages and competitiveness due to its relatively low price. Therefore, ABS with various characteristics has been continuously developed and applied, which makes ABS the most widely used variety in engineering plastics. It is used in the automobile industry, hous...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08K5/524B29B9/12B29C47/40
Inventor 翁永华张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
PatSnap Eureka logo

PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.

X (Twitter)LinkedInYouTubeSubstack

© 2026 PatSnap. All rights reserved. 

Terms of Service

 | 

Privacy policy

 | 

Modern Slavery Act Transparency Statement