Problems solved by technology

[0002] At present, the statues such as bronze Buddha sold on the market are all made of copper casting, but the amount of copper is relatively large, the cost is high, and a large amount of non-ferrous metal copper is wasted, and the cast copper Buddha statues are easy to rust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Copper 79Kg

[0015] Aluminum 25Kg

[0016] Lead 7Kg

[0017] Nickel 1.8Kg

[0018] Manganese 0.8Kg.

Embodiment 2

[0020] Copper 82Kg

[0021] Aluminum 27Kg

[0022] Lead 8Kg

[0023] Nickel 2.0Kg

[0024] Manganese 1.0Kg.

Embodiment 3

[0026] Copper 85Kg

[0027] Aluminum 29Kg

[0028] Lead 9Kg

[0029] Nickel 2.2Kg

[0030] Manganese 1.2Kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A bronzy formulation is disclosed. The invention relates to an alloy comprising copper of 79-85 Kg, aluminium of 25-22 Kg, lead 7-9 Kg, nickel 1.8-2.2 Kg and manganese 0.8-1.2 Kg. The formulation of the invention is reasonable, buddha statue csated by the invention has low content of copper and few expenditure, a great deal of nonferrous metal copper materials are saved. All kinds of buddha statue can not rust for a long time, the formulation of the invention also can cast a plurality of ornaments in the room with attractive appearance.

Description

technical field [0001] The invention relates to an alloy, in particular to a formula for imitating bronze. Background technique [0002] At present, statues such as copper Buddhas sold on the market are all cast from copper, but the consumption of copper is relatively large, the cost is high, a large amount of non-ferrous metal copper is wasted, and the copper Buddha statues of casting are easy to get rusty. Contents of the invention [0003] The object of the present invention is to overcome the weak point that exists in the above-mentioned technology, and a kind of imitation bronze formula with low copper content is provided. [0004] In order to achieve the above object, the technical scheme adopted in the present invention is: [0005] Copper 79-85Kg [0006] Aluminum 25-29Kg [0007] Lead 7-9Kg [0008] Nickel 1.8-2.2Kg [0009] Manganese 0.8-1.2Kg. [0010] The advantages of the present invention are: [0011] The formula of the invention is reasonable, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/01
Inventor 徐桂芬
Owner 徐桂芬