Modified formulation for high surface hardness PC-ABS resin

A PC-ABS, high-surface technology, applied in the field of thermoplastic resin compositions, can solve the problems of increasing processing technology, adverse effects on the environment and human body, and increasing production costs, so as to improve surface hardness, reduce processing technology costs, and expand application fields Effect

Inactive Publication Date: 2007-11-28
MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the previous process, the method of surface spraying was used to improve the surface hardness of PC-ABS resin, but the surface spraying process brought adverse effects on the environment and human body on the one hand, and on the other hand increased the processing technology and increased the production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Take PC-ABS resin raw material, PMMA, CPE, graft copolymer, toughening agent and other components, and blend all the raw materials according to the following composition formula:

[0034] (a) 63 parts of PC-ABS resin raw material

[0035] (b) PMMA 24 parts

[0036] (c) 4 copies of CPE

[0037] (d) ABS-g-MAH 3 parts

[0038] (e) MBS 6 copies

[0039] Then the blended material is mixed and granulated in the extruder, and the obtained mixed and granulated product is made into a finished product through injection molding. Finally, the mechanical properties and surface hardness of the finished product are tested according to the national standard GB13525 / T-92. The results are shown in the table 1.

[0040] project

Embodiment 2

[0042] Take PC-ABS resin raw material, PMMA, CPE, graft copolymer, toughening agent and other components, and blend all the raw materials according to the following composition formula:

[0043] (a) PC-ABS resin raw material 73.6 parts

[0044] (b) PMMA 18.4 parts

[0045] (c) 1 copy of CPE

[0046] (d) 2 parts of ABS-g-MAH

[0047] (e) MBS 5 copies

[0048] Then the blended material is mixed and granulated in the extruder, and the obtained mixed and granulated product is made into a finished product through injection molding. Finally, the mechanical properties and surface hardness of the finished product are tested according to the national standard GB13525 / T-92. The results are shown in the table 1.

[0049] project

Embodiment 3

[0051] Take PC-ABS resin raw material, PMMA, CPE, graft copolymer, toughening agent and other components, and blend all the raw materials according to the following composition formula:

[0052] (a) PC-ABS resin raw material 73.6 parts

[0053] (b) PMMA 18.4 parts

[0054] (c) 1 copy of CPE

[0055] (d) 2 parts of ABS-g-MAH

[0056] (e) MBS 5 copies

[0057] Then the blended material is mixed and granulated in the extruder, and the obtained mixed and granulated product is made into a finished product through injection molding. Finally, the mechanical properties and surface hardness of the finished product are tested according to the national standard GB13525 / T-92. The results are shown in the table 1.

[0058] project

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to one kind of modified PC-ABS resin with high surface hardness. The recipe of the modified PC-ABS resin consists of PC-ABS resin 60-85 weight portions, PMMA 12-25 weight portions, CPE 1-5 weight portions, graft copolymer 1-5 weight portions, and toughener 1-7 weight portions. The modified PC-ABS resin has high surface hardness, mechanical performance basically the same as that of PC-ABS resin, lowered processing cost, and expanded application fields.

Description

technical field [0001] The invention relates to the field of thermoplastic resin compositions in polymer material technology, in particular to a modified formula of PC (Polycarbonate, polycarbonate)-ABS resin with high surface hardness. Background technique [0002] PC-ABS resin is an engineering plastic with superior comprehensive performance developed in the 1960s. It not only has the heat resistance, mechanical strength and dimensional stability of PC, but also has the advantages of easy processability and low price of ABS resin. Good performance, reasonable cost performance, widely used in the automotive industry, household appliances, daily necessities and other fields. Since PC-ABS resin is widely used in the panel production of electronic and electrical products, in order to maintain the long-term shape and aesthetic appearance of the panel, it has a higher surface hardness requirement. In the previous process, the method of surface spraying was used to improve the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08L33/12C08L51/00
Inventor 汪克风岳瑟杨得志刘济林
Owner MITAC PRECISION TECH CO LTD SHUNDE DISTRICT FOSHAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com