High impact polyphenylene sulfide alloy material and method of producing the same

A technology of polyphenylene sulfide and alloy materials, applied in the field of polymer materials, can solve the problems of damaging PPS, reducing the thermal deformation temperature, rigidity, and strength of PPS materials, and achieving improved impact resistance, low cost, and high impact resistance Effect

Inactive Publication Date: 2008-02-27
SHENZHEN KEJU NEW MATERIAL
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, it is feasible to improve the impact resistance of PPS through elastomers, but it will damage other superior propert

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1:

[0029] The weight ratio of PPS is 54% (the following are weight ratios), 1010 / 168 is 0.2 / 0.3%, glass fiber is 40%, compatibilizer is 5%, and other additives are 0.5%. The mixed materials are added to the hopper of the twin-screw extruder, melted and blended, extruded and granulated into composite materials. Among them, the temperature settings of each heating zone of the screw are: temperature in zone one: 265°C; zone two: 270°C; zone three: 270°C; zone four: 275°C; temperature zone five: 275°C; zone six: 275°C; Seven zone: 280℃; eight zone: 280℃; machine head: 265℃; residence time 3~4min, pressure 15MPa.

Example Embodiment

[0030] Example 2:

[0031] The weight ratio of PPS is 49% (the following are weight ratios), PA6 is 5%, 1010 / 168 is 0.2 / 0.3%, glass fiber is 40%, compatibilizer is 5%, and other additives are 0.5%. The mixed materials are added to the hopper of the twin-screw extruder, melted and blended, extruded and granulated into composite materials. Among them, the temperature settings of each heating zone of the screw are: temperature in zone one: 265°C; zone two: 270°C; zone three: 270°C; zone four: 275°C; temperature zone five: 275°C; zone six: 275°C; Seven zone: 280℃; eight zone: 280℃; machine head: 265℃; residence time 3~4min, pressure 15MPa.

Example Embodiment

[0032] Example 3:

[0033] The weight ratio of PPS is 44% (the following are weight ratios), PA6 is 10%, 1010 / 168 is 0.2 / 0.3%, glass fiber is 40%, compatibilizer is 5%, and other additives are 0.5%. The mixed materials are added to the hopper of the twin-screw extruder, melted and blended, extruded and granulated into composite materials. Among them, the temperature settings of each heating zone of the screw are: temperature in zone one: 265°C; zone two: 270°C; zone three: 270°C; zone four: 275°C; temperature zone five: 275°C; zone six: 275°C; Seven zone: 280℃; eight zone: 280℃; machine head: 265℃; residence time 3~4min, pressure 15MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high impact polyphenylene sulfide alloy material and preparing method, which comprises the following steps: allocating with mass ratio as 30-55% polyphenylene sulfide, 5-20% polycaproamide, 30-50% glass fiber, 2-8% inclusive agent, 0. 2-0. 5% anti-oxidant and 0. 1-2% other auxiliary agent; mixing; adding into twin-screw extruder; controlling the temperature at 250-280 deg. c; controlling the rotary speed of the bolt at 400-500rpm; pelleting; getting the product. This invention possesses high impact strength, high modulus and high-intensity, which can modify the defects of the material.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a high-impact-strength polyphenylene sulfide alloy material and a preparation method thereof. Background technique [0002] Polyphenylene sulfide (PPS), also known as polyphenylene sulfide and polyphenylene sulfide, is a thermoplastic special engineering plastic with excellent comprehensive properties. The outstanding features of PPS materials are heat resistance, excellent chemical corrosion resistance, inherent flame retardancy, excellent mechanical properties and electrical properties, excellent dimensional stability, good molding performance and relatively low cost price, available A variety of processing molding methods for molding processing, and precision molding. It is mainly used in automobiles, electronics and electrical appliances, machinery, petroleum, chemical industry and medicine, light industry, and made into long fiber composite materials for special f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08K7/14B29C47/40B29C47/92B29B9/12C08L77/02C08L63/00C08K5/524C08K5/13B29C48/92B29C48/40
CPCB29C2947/9259B29C48/92B29C2948/9259B29C48/40
Inventor 徐东黄义宏
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap