Special plastic/acrylonitrile butadiene styrene (PC/ABS) alloy for notebook computer shell

A notebook computer and alloy technology, applied in the field of polymer alloys, can solve the problems of poor electroplatability, increased product weight, and insufficient surface scratch resistance, and achieve excellent impact resistance, improved hardness and scratch resistance performance effect

Active Publication Date: 2011-02-16
大河宝利材料科技(苏州)有限公司
View PDF16 Cites 83 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these products all have shortcomings such as insufficient surface scratch resistance, increased product weight, and poor electroplatability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be described in further detail below in conjunction with specific embodiments, but not limited to these embodiments.

[0021] The halogen-free flame retardant PC / ABS alloy material prepared by the present invention adopts the following methods or standards for performance testing. All test specimens need to be stored for not less than 16 hours under the conditions of temperature of 23℃±2 and humidity of 50%±5% :

[0022] Tensile strength: tested according to standard ASTM D638;

[0023] Flexural modulus: tested according to standard ASTM D790;

[0024] Notched impact strength: tested according to standard ASTM D256;

[0025] Heat distortion temperature: Tested according to standard ASTM D648, test condition 1.82MPa, 3.2mm / min.

[0026] Flame Retardancy: Tested according to standard UL 94, with a strip thickness of 1.2mm.

[0027] Pencil Hardness: Tested according to standard ASTM D785, test condition 500g.

[0028] Each embodiment adopts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a special plastic / acrylonitrile butadiene styrene (PC / ABS) alloy for a notebook computer shell. The formula comprises the following materials in parts by weight: 30-80 parts of polycarbonate, 5-65 parts of acrylonitrile-butadiene-styrene copolymer, 5-15 parts of compatilizer, 1-15 parts of flame retardant agent, 3-20 parts of filler, 1-10 parts of hardness modifier, 0.5-5 parts of anti-falling agent and 0-1 part of auxiliary agent. By adopting specific high-molecular polymers of polymethyl methacrylate (PMMA), ultrahigh-molecular polysiloxane and the like, the special PC / ABS alloy selects mineral fillers of specific-size mica, glass fiber and the like to carry out rematching therewith and generates synergistic effect, thus obviously improving the surface hardness and scraping resistance of the material and simultaneously having no influence on the other performances of the material. The PC / ABS alloy material has excellent impact resistance, surface scraping resistance and flame retardance, can meet the requirements of plastic for the notebook computer shell and has considerable promotion and application values.

Description

technical field [0001] The invention relates to a polymer alloy, in particular to a PC / ABS alloy specially used for the shell of a notebook computer. Background technique [0002] The shell of a notebook computer is not only the most direct way to protect the body, but also an important factor affecting its cooling effect, weight and aesthetics. Because notebook computers have the characteristics of compact structure, strong mobility and changeable use environment, the casing materials are required to have high mechanical strength, scratch resistance, excellent high and low temperature impact resistance, good heat resistance, combustion resistance, light weight, And it has the characteristics of excellent formability, electroplating and low cost. [0003] Existing commercial notebook computer plastic shells are mostly modified with polymers such as polycarbonate (PC) and acrylonitrile-butadiene-styrene copolymer (ABS), such as glass fiber modified PC, carbon fiber modified ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/00C08K3/34C08L83/04C08L67/02C08K7/14C08L33/12C08L25/12C08K13/04C08L55/02C08L69/00
Inventor 罗煜郭旭平郭长华
Owner 大河宝利材料科技(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap