Optical compensation film, polarizing plate and liquid crystal display device

An optical compensation film, liquid crystal display technology, applied in optics, nonlinear optics, instruments, etc., can solve the problems of changing optical compensation performance, changing the optical compensation performance of cellulose ester film, etc.

Active Publication Date: 2010-12-08
FUJIFILM CORP
View PDF63 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in recent years, liquid crystal displays have been increasingly used in various environments, and changing the optical compensation properties of cellulose ester films using the above-mentioned techniques in these environments has become a problem
More specifically, the problem is that these cellulose ester films are affected by environmental changes, especially humidity, especially when they are stacked on liquid crystal cells, so that their Re retardation value and Rth retardation value change, making the optical Compensation for performance changes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical compensation film, polarizing plate and liquid crystal display device
  • Optical compensation film, polarizing plate and liquid crystal display device
  • Optical compensation film, polarizing plate and liquid crystal display device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0576] 1. Formation of cellulose acylate film

[0577] (1) Cellulose acylate

[0578] Cellulose acylates with different acyl substitution degrees shown in Table 1-1 were prepared. More specifically, in addition to carboxylic acid, sulfuric acid was added as a catalyst (7.8 parts by mass / 100 parts by mass of cellulose), and the acylation reaction was performed at 40°C. Subsequently, by controlling the sulfuric acid catalyst content, water content and aging time, the total degree of substitution and the degree of substitution at the 6-position are adjusted. Maturation is carried out at 40°C. In addition, low molecular weight components in the obtained cellulose acylate were washed away with acetone.

[0579] (2) Preparation of concentrated solution

[0580] Under stirring, to the cellulose acylate shown in Table 1-1, a plasticizer (2:1 mixture of triphenyl phosphate and biphenyl diphenyl phosphate) was added, and the retardation having the structure shown below Expression agent and ...

Embodiment 2

[0643] 1. Formation of cellulose acylate film

[0644] (1) Cellulose acylate

[0645] Cellulose acylates with different degrees of acyl substitution shown in Table 2-1 were prepared. More specifically, in addition to carboxylic acid, sulfuric acid (7.8 parts by mass / 100 parts by mass of cellulose) was added as a catalyst, and the acylation reaction was carried out at 40°C. Subsequently, by controlling the sulfuric acid catalyst content, water content and aging time, the total degree of substitution and the degree of substitution at the 6-position are adjusted. Maturation is carried out at 40°C. In addition, low molecular weight components in the obtained cellulose acylate were washed away with acetone.

[0646] (2) Preparation of concentrated solution

[0647] Under stirring, to each of the cellulose acylates shown in Table 2-1, a plasticizer (2:1 mixture of triphenyl phosphate and biphenyl diphenyl phosphate), having the structure shown below, was added Delay expression agent and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

An optical compensation film is provided and has a cellulose acylate film coated with an optically anisotropic layer containing a liquid crystalline compound, cellulose having a glucose unit, a hydroxyl group of the glucose unit being substituted with an acyl group having at least two carbon atoms. The cellulose acylate film satisfies relationships specified in the specification.

Description

Technical field [0001] The invention relates to an optical compensation film, and a polarizer and a liquid crystal display each using the optical compensation film. Background technique [0002] Liquid crystal displays are widely used in a variety of applications including personal computers, mobile device monitors, and televisions due to their various advantages, such as the ability to operate at low voltage and low energy consumption, and the high possibility of reducing size and appearance. . Although for this type of liquid crystal display, various modes have been proposed according to how the liquid crystal molecules are aligned in the liquid crystal cell, the main mode so far is the TN mode, in which the orientation state of the liquid crystal molecules is twisted from the lower substrate to the upper substrate. About 90°. [0003] Generally, a liquid crystal display is composed of a liquid crystal cell, an optical compensation film, and a polarizer. The optical compensati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B5/30G02F1/13363C08J7/04
Inventor 伊藤洋士中村亮
Owner FUJIFILM CORP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com