Anti-static polyphenylacetylene combination and preparation method and sheet material

A polystyrene sheet, polystyrene technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of high humidity dependence, surface deterioration, and lack of long-term effect, and achieve humidity sensitivity The effect of small resistance, improvement of packaging grade, and improvement of advanced nature

Active Publication Date: 2008-04-09
浙江三和塑料有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although products with higher transparency can be prepared, such antistatic agents rely on absorbing moisture in the air to achieve antistatic effects, and are easy to precipitate to make the surface worse, and are easy to be thermally decomposed during processing, so the dependence on humidity is too large
This type of ant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Polyethylene glycol monomethyl ether methacrylate PEDMA 1 7.4%, hydroxyethyl methacrylate HEMA4.96%, coupling agent KH-570 1.4%, azobisisobutyronitrile AIBN 0.12%, sodium perchlorate Na + 3.02%, HIPS polystyrene 73%, other 0.10% (others are mainly antioxidants, anti-aging agents, reinforcing agents, toughening agents).

[0023] Polyethylene glycol monomethyl ether PEDMA methacrylate, hydroxyethyl methacrylate HEMA, azobisisobutyronitrile AIBN, sodium perchlorate Na + The material is reacted at 60-90°C for 2-6 hours, then poured out, and baked at 45-100°C for several hours to obtain an antistatic material.

[0024] Mix the antistatic material obtained from the above reaction with polystyrene, antioxidant 1010, antioxidant 168, silane coupling agent KH-570, reinforcing agent and toughening agent, knead at 60°C for 43 minutes, and feed to extrusion The extruder is extruded, the speed of the feeder is 520 rpm, the temperature of the extrusion is 180 ° C ~ 210 ° C, the spe...

Embodiment 2

[0028] The formulation of antistatic plastic is as follows:

[0029] Polyethylene glycol monomethyl ether methacrylate PEDMA 16.04%, hydroxyethyl methacrylate HEMA 4.57%, coupling agent KH-570 1.4%, azobisisobutyronitrile AIBN 0.11%, sodium perchlorate Na + 2.78%, HIPS polystyrene 75%, other 0.10% (others are mainly antioxidants, anti-aging agents, reinforcing agents, toughening agents).

[0030] The preparation method of the polymer antistatic polystyrene plastic sheet is the same as in Example 1.

Embodiment 3

[0032] The formulation of antistatic plastic is as follows:

[0033] Polyethylene glycol monomethyl ether methacrylate PEDMA 18.76%, hydroxyethyl methacrylate HEMA 5.35%, coupling agent KH-570 1.4%, azobisisobutyronitrile AIBN 0.13%, sodium perchlorate Na + 3.26%, HIPS polystyrene 71%, other 0.10% (the other 0.10% is antioxidant, antiaging agent, reinforcing agent, toughening agent). The coupling agent is silane coupling agent KH-570 produced by Nanjing Shuguang Chemical General Factory, and the reinforcing agent and toughening agent are commonly used plastic reinforcing agents and toughening agents.

[0034] The preparation method of the polymer antistatic polystyrene plastic sheet is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to an antistatic plastics sheet, in particular to an antistatic polystyrene combination, a preparation method thereof and the produced sheet prepared by the combination. The antistatic polystyrene combination is made through mixing the components of the following prescription according to weight proportion: 65.0 percent to 85.0 percent of HIPS polystyrene, 8.0 percent to 28.0 percent of methyl-acrylic acid polyethylene glycol single methyl ether ester, 3.14 percent to 6.87 percent of hydroxylethyl methacrylate, 1.72 percent to 3.97 percent of sodium perchlorate, 0.0963 percent to 0.145 percent of azobisisobutyronitrile and 0.92 percent to 2.4 percent of coupling agent. In addition, the invention discloses a sheet that is produced by three layers of materials compounded together, wherein, the materials of the upper layer and the lower layer are the antistatic polystyrene combination gained through mixing the components. The antistatic polystyrene sheet of the invention saves the consumption of the antistatic polystyrene combination, reduces cost, adopts three surface layers combination with the property of no drop-off, is characterized by lasting long effect and low humidity sensitivity and enhances level and advancement of electric products packaging.

Description

technical field [0001] The invention relates to an antistatic plastic sheet, in particular to an antistatic polystyrene composition, a preparation method thereof and a sheet prepared from the composition. Background technique [0002] At present, polystyrene plastic products are widely used in the packaging and transportation of electronic products, but the surface resistance of ordinary plastics is greater than 10 12 More than Ω / sq, the conductivity is extremely poor, and static electricity is easily generated during the packaging and transportation of electronic products and is not easy to conduct away, causing great harm to electronic products. Therefore, it is imperative to develop and produce modified antistatic plastics. The surface resistivity of ordinary antistatic polystyrene plastics produced at present is mostly in the range of 10 9 -10 11 Ω / sq, although it has a certain antistatic performance, it can meet the needs of low-end electronic products with low electr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L25/06C08K5/54C08J5/18C09K3/16C08K5/10C08K3/24C08K5/23
Inventor 吴中心张宝成王建康
Owner 浙江三和塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap