Tear-resistant fluororubber shunt umbrella and preparation thereof

A technology of fluororubber and shunting umbrella, which is applied in liquid bottling, packaging, liquid treatment, etc., can solve the problems of deterioration of tear performance, high cost of carbon fiber, short service life, etc., and achieve simple preparation process, low cost, good durability The effect of tear properties

Active Publication Date: 2008-06-25
GUANGZHOU MECHANICAL ENG RES INST
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat tear resistance of tetrapropylene fluororubber is poor, especially the tear performance at high temperature is worse. During the vulcanization process of thin products, since the vulcanization temperature is about 170 ° C, after the vulcanization is completed, the shunt umbrella will be removed from the When the mold come

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] Example 1

[0018] The raw material ratio and preparation method of tear-resistant fluorine rubber shunt umbrella are as follows:

[0019] (1) 100 parts by mass of tetrapropylene fluorine rubber (FE2701) from Sanaifu Company, 30 parts by mass of N990 carbon black, 1.0 parts by mass of sodium stearate, 3 parts by mass of dicumyl peroxide, triallyl iso 5 parts by mass of cyanurate, mixed uniformly on an open mill to obtain a tetrapropylene fluorine rubber compound;

[0020] (2) 100 parts by mass of Lanxess hydrogenated nitrile rubber (Therban A3406), 2 parts by mass of magnesium oxide, 1.5 parts by mass of antioxidant MB, 50 parts by mass of N550 carbon black, and 3 parts by mass of dicumyl peroxide, 5 parts of triallyl isocyanurate are mixed evenly on an open mill to obtain a hydrogenated nitrile rubber compound;

[0021] (3) Take 75 parts by mass of the tetrapropylene fluoride rubber compound and 25 parts by mass of the hydrogenated nitrile rubber compound prepared above, m...

Example Embodiment

[0022] Example 2:

[0023] The raw material ratio and preparation method of tear-resistant fluorine rubber shunt umbrella are as follows:

[0024] (1) 100 parts by mass of tetrapropylene fluorine rubber (FE2701) from Sanaifu Company, 30 parts by mass of N990 carbon black, 1.0 parts by mass of sodium stearate, 3 parts by mass of dicumyl peroxide, triallyl iso 5 parts by mass of cyanurate, mixed uniformly on an open mill to obtain a tetrapropylene fluorine rubber compound;

[0025] (2) 100 parts by mass of hydrogenated nitrile rubber (Zetpot 2000) of Zeon Company, 5 parts by mass of magnesium oxide, 1.5 parts by mass of antioxidant MB, 50 parts by mass of N550 carbon black, and 3 parts by mass of dicumyl peroxide , 5 parts by mass of triallyl isocyanurate, mixed uniformly on an open mill to obtain a hydrogenated nitrile rubber compound;

[0026] (3) Take 80 parts by mass of the tetrapropylene fluoride rubber compound and 20 parts by mass of the hydrogenated nitrile rubber compound p...

Example Embodiment

[0027] Example 3:

[0028] The raw material ratio and preparation method of tear-resistant fluorine rubber shunt umbrella are as follows:

[0029] (1) The tetrapropylene fluorine rubber (Aflas  FA 100S) 100 parts by mass, 30 parts by mass of N990 carbon black, 1.0 parts by mass of sodium stearate, 2 parts by mass of dicumyl peroxide, 4 parts by mass of triallyl isocyanurate, and mixed on an open mill Mix evenly to obtain tetrapropylene fluorine rubber compound;

[0030] (2) 100 parts by mass of hydrogenated nitrile rubber (Zetpot 2000) of Zeon Company, 5 parts by mass of magnesium oxide, 1.5 parts by mass of antioxidant MB, 50 parts by mass of N550 carbon black, and 3 parts by mass of dicumyl peroxide , 5 parts of triallyl isocyanurate, kneaded uniformly on an open mill to obtain a hydrogenated nitrile rubber compound;

[0031] (3) Take 70 parts by mass of the tetrapropylene fluoride rubber compound and 30 parts by mass of the hydrogenated nitrile rubber compound prepared above, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fluorubber shunt parachute with tearing resistance and the preparation method thereof. The invention is made of the following row materials with the percentage in weight: 70-80 shares of tetrapropyl fluoro elastomer gross rubber, 20-30 shares of hydrogenated nitrile-butadiene gross rubber. The shunt parachute is both with the chemical mediator of the resistance to the broad spectrum and the better tearing resistance. The invention has the advantages of low cost and simple preparation technology.

Description

technical field [0001] The invention relates to the field of rubber industrial products, in particular to a tear-resistant fluororubber shunting umbrella and a preparation method thereof. Background technique [0002] The rubber diverter umbrella is a thin-walled rubber product, and the wall thickness of the product usually gradually transitions from 0.5mm to 3mm. On the liquid filling production line, the filled liquid flows through the diverter umbrella along the outer edge of the exhaust pipe, and then discharges down the inner wall of the packaging bottle. Due to exposure to various chemical media in pharmaceutical, daily chemical, food, pesticide and special industries, the rubber shunt umbrella must have good chemical media resistance. Tetrapropane fluoro rubber has a broad spectrum of chemical resistance, so tetrapropane fluoro rubber is usually used to manufacture rubber shunt umbrellas. However, the heat tear resistance of tetrapropylene fluororubber is poor, espe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/12C08K5/29B67C3/28C08L9/02C08K3/04C08K5/09C08K5/14
Inventor 肖风亮黄兴彭兵王勇
Owner GUANGZHOU MECHANICAL ENG RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap