Steel glue and preparation method thereof

A technology of viscose glue and stainless steel, which is applied in adhesives, anti-corrosion coatings, paints containing biocide, etc., to achieve the effects of simple production process, high strength and low cost

Inactive Publication Date: 2013-04-10
谢铋年
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no material with high hardness, high strength, corrosion resistance and wide application that can be produced by mixing viscose, cyclohexanone peroxide, methyl ethyl ketone peroxide and other common materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] A: Basic formula --- waterproof coating, handicrafts

[0035] 1. Viscose glue (mucus) ----------------------------------- 100

[0036] 2. Cyclohexanone peroxide ---------------------------------0~4

[0037] 3. Methyl ethyl ketone peroxide (transparent liquid)---------0.5~2

[0038] Add "2" to "1" at room temperature (about 25 degrees C) and mix well, then add "3" and mix well, then inject into mold or paint, and set for about 1 hour.

[0039] B: Ingredient formula added on the basis of A --- waterproof coating, plugging and glue:

[0040] 1. Viscose ------------------------------------------ 100

[0041] 2. Cyclohexanone peroxide -----------------------------------0~4

[0042] 3. Quartz powder (or stone powder) --------------------------- 1~150

[0043] 4. Methyl ethyl ketone peroxide---------------------0.1~2

[0044] Mix "1" and "2" at room temperature (about 25 degrees C), add '3' and mix well, then add "4", injection molding or coating and scraping, and it wil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a steel glue and a preparation method thereof; the components of the steel glue comprise cellogel, cyclohexanone peroxide, and methyl ethyl ketone peroxide; the proportion (by weight) is the cellogel : the cyclohexanone peroxide : the methyl ethyl ketone peroxide equal to 100 : 0-4: 0.5-2; the preparation method includes adding the cyclohexanone peroxide into the cellogel according to the proportion under room temperature and stirring uniformly, then adding the methyl ethyl ketone peroxide and stirring uniformly before injection molding or brushing; after solidifying and hardening for 0.5 to 1.5 hours, solid products or solid coatings are formed. The steel glue has simple production technology, low cost, strength four to five times harder than concrete, lighter weight than cement, acid and alkali resistance, and the strength two times harder than concrete after mixing with yellow clayey.

Description

technical field [0001] The invention relates to a method for making hard materials, and mainly refers to a steel glue and a preparation method thereof. Background technique [0002] It is known that viscose glue, cyclohexanone peroxide, and methyl ethyl ketone peroxide are all general-purpose chemical raw materials. Among them, viscose glue has the characteristics of waterproof, strong tensile strength, and high viscosity, and is characterized by good rigidity and hardness. Large, good stiffness, small deformation, small expansion coefficient, low heat generation, etc.; cyclohexanone peroxide is a ketone peroxide initiator (or curing agent) widely used in unsaturated polyester resin curing at room temperature ), often with cobalt naphthenate, etc. to form an initiator system, which has the advantages of convenient use and moderate curing speed. Cyclohexanone peroxide paste is generally used as an initiator in the production of FRP products. Cyclohexanone peroxide can also be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L101/00C09D201/00C09D5/08C09D5/16C09J201/00
Inventor 谢铋年
Owner 谢铋年