Calcium silicon iron core-spun yarn core layer composition

A composition and iron-clad technology, applied in the field of silicon-calcium iron-clad core wire core layer composition, can solve the problems of deoxidation cost, waste of resources, etc., and achieve the effects of improving utilization rate, reducing the amount of splashing, and being beneficial to the purification of molten steel

Inactive Publication Date: 2008-08-06
马长慧
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The task of the present invention is to provide a silicon-calcium-iron cored wire core layer composition that uses a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Take 300Kg of calcium powder and 700Kg of refining slag, and mix the two materials evenly to form the core layer composition of silicon-calcium cored wire. The refining slag is pre-melted refining slag, and the pre-melting refining slag contains 350Kg of calcium oxide, 250Kg of aluminum oxide and 100Kg of silicon dioxide.

Embodiment 2

[0014] Take 400Kg of calcium powder and 600Kg of refining slag, and mix the two materials evenly to form the core layer composition of silicon-calcium cored wire. The refining slag is pre-melted refining slag, and the pre-melting refining slag contains 300Kg of calcium oxide, 260Kg of aluminum oxide and 40Kg of silicon dioxide.

Embodiment 3

[0016] Take 100Kg of calcium powder, 600Kg of refining slag, and 300Kg of iron powder, and mix the three materials evenly to form the core layer composition of silicon-calcium cored wire. The refining slag is pre-melted refining slag, and the pre-melting refining slag contains 300Kg of calcium oxide, 250Kg of aluminum oxide and 50Kg of silicon dioxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a Si-Ca-Fe cored-wire sandwich layer combination, the combination is composed of calcium powder whose percentage by weight is 10%-60%, refining slag 40%-90% and ferrous powder 0-30%, wherein the refining slag can lower the vapor tension which is produced by calcium in the reaction process, lower the spraying amount of molten steel, and increase the utilization ratio, the refining slag adopts a calcium oxide and aluminum oxide slag system, which can exist in the molten steel in molten state, the concentration is smaller than that of the molten steel, inclusions are absorbed along the refining slag floats upward, which is very beneficial for purifying the molten steel, the ferrous powder not only can enlarge the specific weight of the cored-wire, which is beneficial for sinking the cored-wire, but also can play the role which is same with that of the refining slag, and the availability ratio of the calcium is further increased.

Description

Technical field: [0001] The invention relates to a silicon-calcium-iron cored wire core layer composition for making a cored wire. Background technique: [0002] The cored wire is a wire-shaped material used in refining molten steel. It is composed of a core layer and a sheath made of strip steel sheets wrapped around the outer surface of the core layer. When in use, the cored wire is continuously fed into the ladle through the wire feeding machine. When the foreskin of the cored wire entering the ladle is melted, the core layer is exposed to directly contact with the molten steel for chemical reaction, and stirred by argon The kinetic effect makes it able to effectively achieve deoxidation, desulfurization, and removal of inclusions, so as to improve the quality and performance of steel. It can be seen that in order for the cored wire to effectively purify molten steel, the first condition is that the active components in the core layer must be able to immerse into the mol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/04
Inventor 马长慧
Owner 马长慧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap